Filtern
Erscheinungsjahr
Dokumenttyp
Sprache
- Englisch (32) (entfernen)
Schlagworte
- Adhesive strength (2)
- Bonding strength (2)
- Centrifuge technology (2)
- Coatings (2)
- Ellipsometrie (2)
- Flammability (2)
- High pressure airborne ultrasound (2)
- High pressure oxygen (2)
- Imaging ellipsometry (2)
- Kohlenstoffschichten (2)
Organisationseinheit der BAM
- 6 Materialchemie (9)
- 6.1 Oberflächen- und Dünnschichtanalyse (5)
- 6.7 Materialsynthese und Design (4)
- 7 Bauwerkssicherheit (2)
- 7.1 Baustoffe (2)
- 4 Material und Umwelt (1)
- 4.1 Biologische Materialschädigung und Referenzorganismen (1)
- 6.2 Material- und Oberflächentechnologien (1)
- 6.6 Physik und chemische Analytik der Polymere (1)
- 7.4 Baustofftechnologie (1)
Functionality of optical systems requires optical coatings of
high quality which have to be adapted to the application in
terms of the performance of optical parameters such as
reflectivity (AR, low, defined, high), the substrate material of
interest (polymers, ceramics, and glass), the environmental
conditions (such as temperature or humidity), and the service
conditions (such spectral range and power density). Moreover,
in many cases, additional non-optical requirements have
to be met, including mechanical features such as scratch
resistance, hardness and modulus.
Consequently, thickness and overall uniformity requirements
are steadily increasing. In general, these demands can usually
not be achieved by a single film or coating. Instead, films with
specific design features (such as gradients), layer stacks and
multilayers are a prerequisite for high quality layers and their
reliability. For the development of such layer systems, a
versatile cluster deposition system consisting of three clusters
and a cluster-to-cluster handler has been designed. Besides a
PECVD cluster for DLC coatings, two PVD clusters implement
ion assisted electron beam evaporation and plasmabased
sputter technology. In addition to metallic films, preparation
of oxide and nitride optical coatings (SiO2, TiO2, Ta2O5,
ITO, Al2O3, TiN, AlN) in various process modifications (nonreactive,
partially reactive, full-reactive; rf-, dc-, mf- mode;
PEM control) has been carried out.
Within this paper, the effect of several process parameters on
layer quality (optical constants, density, and uniformity) is
discussed for selected applications examples (AR- and HR
coatings, applications at elevated temperatures and applications
of enhanced mechanical performance).
It has been shown that specific features of ion and plasma
assisted PVD processes, including ion-beam and plasma preand
post-treatment of substrates and layer systems, may
widen the application range and improve functionality features
of given coating/substrate systems.
The new promoted ignition combustion test apparatus at BAM matches the requirements of ASTM test method G 124 [ASTM G 124, Standard Test Method for Determining the Combustion Behavior of Metallic Materials in Oxygen-Enriched Atmospheres, 2003] and of EIGA publication, IGC Doc 13/02/E [EIGA Gas Association Document IGC Doc 13/02/E, Oxygen Pipeline Systems, 2003]. The test apparatus is most likely the only one in Europe. The test chamber allows investigations with pure oxygen or oxygen mixtures at pressures up to 500 bar and at temperatures up to 400°C at static or flowing gas conditions. The ignition device consists of an electrical ignition wire and a promoter. IR-sensors, distributed over the whole length of the rod, measure and record the burning temperature and allow measurement of the burn rate. A video system records the experiment for visual characterization of the burning behavior. BAM test results are compared with published data. Results on investigations with coated rods are presented. Ceramic coatings seem to be a solution for the use of certain less compatible metallic materials at higher oxygen pressures.
Two different test apparatuses are used at BAM to evaluate the safety of oxygen components: First, the promoted ignition combustion test according to ASTM G 124 [1] and to EIGA IGC Doc 13/02/E [2], and second, the new metallic disk ignition test that has not been standardized yet. The standard test method ASTM G 124 allows a ranking of metallic materials for use at high pressure oxygen. However, the transfer of those test results to valves and fittings in real-life situations is rather complex. The metallic disk ignition test, developed at BAM, is more practice oriented and uses metallic disks of different thicknesses of the investigated material. A commonly used nonmetallic sealing ring is placed in front of this disk and serves as an igniter. This test array is then exposed to high pressure gaseous oxygen impacts in a standardized pneumatic impact tester according to DIN EN 1797 [3].
Hydrogen-Containing Amorphous Carbon Layers as Optical Materials in the Near-IR Spectral Range
(2007)
Hydrogenated amorphous carbon layers were deposited on various substrates by means of a plasma CVD process with a RF substrate bias as well as an ECR plasma source. The optical properties of the a-C:H layers were obtained via spectroscopic ellipsometry and correlated with their mechanical and chemical properties. The layers from pure RF plasma exhibit a higher absorption constant in the visible spectral range and a higher refractive index. All layers are nearly transparent in the NIR spectral range making them candidates for optical thin layer systems. The laser damage behaviour of the a-C:H layers was investigated with ultrashort pulses. The damage thresholds were consistent with the absorption constants of the layers. Interesting damage morphologies were observed indicating a sensitivity of this experiment to sub-structures in the layer.
Hydrogenated amorphous carbon layers were deposited on BK7 glass in a plasma-assisted chemical vapor deposition
process. Low and high refracting films with thicknesses d ranging from 11 nm to 5.8 µm were produced having refractive
indices n between 1.68 and 2.41 and linear absorption coefficients of α~100 cm-1 and α~20000 cm-1 at 800 nm wavelength as a result of different plasma modes. Laser ablation thresholds Fth in dependence on d were determined using 30-fs laser pulses. Low absorbing layers show a constant Fth while Fth increases with rising d up to the optical penetration depth of light α-1 for high absorbing films.
The synthesis of polymerlike amorphous carbon (a-C:H) thin-films by microwave excited collisional hydrocarbon plasma process is reported. Stable and highly aromatic a-C:H were obtained containing significant inclusions of poly(p-phenylene vinylene) (PPV). PPV confers universal optoelectronic properties to the synthesized material. That is a-C:H with tailor-made refractive index are capable of becoming absorption-free in visible (red)-near infrared wavelength range. Production of large aromatic hydrocarbon including phenyl clusters and/or particles is attributed to enhanced coagulation of elemental plasma species under collisional plasma conditions. Detailed structural and morphological changes that occur in a-C:H during the plasma synthesis are also described.
The extremely low acoustic impedance of polypropylene ferroelectret combined with its piezoelectric properties makes this material suitable for construction of aircoupled ultrasonic transducers for non-destructive testing. For the fabrication of transducers with a stable quality, the reproducibility of their key parameters is of interest.
The reproducibility was evaluated by means of (i) impedance spectroscopy and (ii) pulse-echo measurements. (i) Impedance spectroscopy was applied to identify the resonance frequency, the coupling factor and the acoustic impedance of several nominally identical transducers. (ii) Pulse-echo measurements yielded the signal form of these transducers.
The variation of the signal amplitude measured with pulseecho technique was about 10 dB. A part of this variation Comes from the deposition of transducer electrodes and another part from local variations of ferroelectret properties. The variation of the signal amplitude was caused by the observed variation of the coupling factor, which was also about 10 dB. The variation of the acoustic impedance was only about 1 dB, thus having no effect on the variation of the signal amplitude.
These results indicate that the variability can be reduced by improving the control of electrode deposition and by optimizing the production technology affecting the reproducibility of material properties.
Public, hidden, and forensic features either encoded or directly legible are used for authentication. Fabry-Perot layer stacks as information carriers in combination with imaging ellipsometry as optical read-out system provide all-in-one anti-counterfeiting capability that may establish the new security level 'encoded forensic'. Different layer designs are described with regard to all three security levels: public features (e.g. color and tilt effect) perceptible by the human eye, hidden features (e.g. spectroscopic response in the UV or IR), and forensic features (ellipsometric quantities Ψ and Δ as a function of wavelength λ and angle of incidence AOI). Physically uncloneable functions (PUF) could be realized as a result of a multi-material and a multi-parameter deposition approach as well as by means of specific design features of the Fabry-Perot layer stack. Hence, they are not subject to any reverse engineering strategies. Examples of stratified, micro-structured, and laser-modified Fabry-Perot layer systems are considered that may be used at all perception levels (e.g. human eye, bar code reader, and imaging ellipsometry) for authentication against product counterfeiting and related areas. --------------------------------------------------------------------------------------------------------------------
Zur Authentifizierung werden offene, versteckte und forensische Merkmale entweder codiert oder direkt auslesbar verwendet. Mit Fabry-Perot Schichtsystemen als Informationsträger in Kombination mit der abbildenden Ellipsometrie als optischem Auslesesystem steht ein 'all-in-one' Fälschungsschutz-System zur Verfügung, das ein neues Sicherheitsniveau 'kodiert-forensisch' darstellt. Es werden unterschiedliche Schichtdesigns beschrieben, mit denen alle drei Sicherheitsniveaus realisiert werden können: offene Merkmale (z.B. Farbe und Kippeffekt), die mit dem menschlichen Auge wahrnehmbar sind, versteckte Merkmale (z.B. die spektrale Antwort im Sichtbaren oder im IR) sowie forensische Merkmale (ellipsometrische Größen Ψ und Δ als Funktion der Wellenlänge λ und des Einfallswinkels AOI).
Physikalisch nicht klonbare Funktionen (PUF) können im Ergebnis einer Multi-Material- und Multi-Parameter Beschichtungsstrategie sowie durch spezifische Design-Merkmale des Fabry-Perot Schichtsystems realisiert werden. Folglich sind solche Schichtsysteme dem 'reverse engineering' nicht zugänglich. Es werden Beispiele für lateral ausgedehnte, mikrostrukturierte und Laser modifizierte Schichtsysteme auf verschiedenen Ausleseniveaus (menschliches Auge, Barcode-Lesegerät, abbildendes Ellipsometer) vorgestellt, die zur Authentifizierung von Produkten und verwandte Gebiete geeignet sind.