Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (63)
- Vortrag (50)
- Zeitschriftenartikel (47)
- Posterpräsentation (9)
- Beitrag zu einem Sammelband (8)
- Buchkapitel (2)
- Dissertation (1)
Schlagworte
- Ageing (26)
- Seal (25)
- Compression set (23)
- Elastomer (19)
- Rubber (16)
- Degradation (11)
- Low temperature (11)
- Metal seal (11)
- Aging (10)
- Dichtung (8)
Organisationseinheit der BAM
- 3 Gefahrgutumschließungen; Energiespeicher (48)
- 3.4 Sicherheit von Lagerbehältern (48)
- 9 Komponentensicherheit (2)
- 5 Werkstofftechnik (1)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
- 7 Bauwerkssicherheit (1)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (1)
- 9.5 Tribologie und Verschleißschutz (1)
- 9.6 Additive Fertigung metallischer Komponenten (1)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (50)
Polymer Testing - Editorial
(2016)
The special properties of high molecular weight polyethylene (HMW-PE) and ultra high molecular
weight polyethylene (UHMW-PE) result basically from their extreme chain lengths and their high
degree of crystallinity. As high-performance polymers, they are used for a variety of applications.
UHMW-PE in particular is often utilized for endoprothesis (due to its excellent slip and wear
properties) and due to its high hydrogen content as a neutron moderator in casks for storage and
transport of radioactive materials.
To prepare the material for instance for its use as a total joint replacement, it is exposed to radiation
for several reasons, such as sterilization and crosslinking, leading to partial improvement of the
mechanical properties (e.g. fracture toughness, crack propagation resistance, wear resistance) and
better chemical stability.
To be applicable for long term radiation shielding purposes for instance over a period of 40 years,
PE has to withstand any type of degradation affecting safety relevant aspects.
The scope of our investigation comprises an estimation of the radiation impact on the molecular and
supra molecular structure of two types of PE and to what extent these changes are detectable by
thermo-analytical (TA) methods, such as Differential Scanning Calorimetry (DSC), Thermo
Mechanical Analysis (TMA), Dynamic Mechanical Analysis (DMA) and Thermo Gravimetric
Analysis (TGA). Additionally FT-IR spectroscopy as well as density and gas sorption
measurements were carried out.
Due to the poor solubility of HMW-PE and UHMW-PE, some classical analytical techniques are
not applicable. But TA-methods represent a feasible approach to detect structural and
morphological features of these materials as well as changes caused by external influences, such as
thermal treatment and/or irradiation. With the combination of the applied TA-techniques it is
possible to distinguish between crosslinking and degradation.
The temperature dependences of dielectric permittivity and elastic modulus of poly(vinylidene fluoride - hexafluoropropylene) (P(VDF-HFP)) are compared and explained by use of structural data obtained by differential scanning calorimetry and X-ray analysis. Special emphasis is put on the effect of uniaxial stretching which renders the polymer ferroelectric. It is shown that dielectric and mechanical relaxations at the glass transition (aa relaxation) are closely related and not significantly affected by stretching. It is further confirmed that stretching destroys the non-polar spherulitic crystalline structure and produces relatively small-sized polar crystallites. This manifests in the disappearence of the so-called ac relaxation which is associated to molecular motions within the spherulitic crystalline lamellae. However, there are discrepancies between dielectric and mechanical losses above the glass transition which point towards a still not described structural transition.
Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste and in some countries for spent fuel transportation casks. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with regard to mechanical, thermal and environmental conditions as well as irradiation during the entire operation period.
In Germany the low and intermediate level radioactive waste is planned to be disposed in the Konrad repository in standardized containers. Many of these containers use an elastomer seal between lid and container body. Depending on the radiactive inventory and a possible containment of the waste in inner barrels and/or concrete structures, such containers may require a specific leak tightness. In such cases, specified leakage rates are shall not be exceeded by the the seals to keep potential activity releases from the inventories well below defined limits.
Generally, all waste containers have to fulfill the waste acceptance criteria for the Konrad repository as defined by the reports BfS SE-IB-29/08 and SE-IB-30/08. From these criteria several requirements for seal performance are derived. The seals have to:
- ensure full functionality until final container disposal,
- maintain its function in case of a thermal or mechanical accident,
- ensure encapsulation also at -20 °C.
This combination of requirements is challenging especially as a seal exchange, which is typical for many other applications, is hardly possible and thus a sound understanding of how to perform safety evaluation of containers is required. Therefore BAM has initiated investigations on elastomer seal behaviour. This work focuses on low temperature behaviour and sealing performance concerning static conditions as well as partial loss of compression and ageing of elastomer seals. Concerning ageing, property changes caused by long-term thermooxidative conditions as well as gamma irradiation are investigated.
This contribution presents an overview and explanation of the aims of the ongoing research and gives an update of the most relevant results.
Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste and in some countries for spent fuel transportation casks. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with regard to mechanical, thermal and environmental conditions as well as irradiation during the entire operation period.
In Germany the low and intermediate level radioactive waste is planned to be disposed in the Konrad repository in standardized containers. Many of these containers use an elastomer seal between lid and container body. Depending on the radiactive inventory and a possible containment of the waste in inner barrels and/or concrete structures, such containers may require a specific leak tightness. In such cases, specified leakage rates are shall not be exceeded by the the seals to keep potential activity releases from the inventories well below defined limits.
Generally, all waste containers have to fulfill the waste acceptance criteria for the Konrad repository as defined by the reports BfS SE-IB-29/08 and SE-IB-30/08. From these criteria several requirements for seal performance are derived. The seals have to:
- ensure full functionality until final container disposal,
- maintain its function in case of a thermal or mechanical accident,
- ensure encapsulation also at -20 °C.
This combination of requirements is challenging especially as a seal exchange, which is typical for many other applications, is hardly possible and thus a sound understanding of how to perform safety evaluation of containers is required. Therefore BAM has initiated investigations on elastomer seal behaviour. This work focuses on low temperature behaviour and sealing performance concerning static conditions as well as partial loss of compression and ageing of elastomer seals. Concerning ageing, property changes caused by long-term thermooxidative conditions as well as gamma irradiation are investigated.
This contribution presents an overview and explanation of the aims of the ongoing research and gives an update of the most relevant results.
Safety of long term containment and storage of radioactive waste is an essential issue, which is increasingly gaining international attention. Extending interim storage beyond initial license periods is one of the major challenges worldwide.
BAM has been involved in all kinds of radioactive waste container safety evaluation for storage and transportation including their long term performance from the very beginning. Today, all work related to the safe management of radioactive waste is linked by the activity field “Nuclear Waste Management” within the Focus Area “Energy” at BAM and in conjunction with a research strategy and agenda. Most recently, the working group “Long Term Safety of Container Systems and Components” was established to launch and perform research projects related to safety issues concerning the extended interim storage of radioactive waste.
For example, within our project LaMEP, we investigate ageing effects of metal and elastomer seals as well as polymeric neutron shielding materials, which are container components that fulfil major safety functions. The results of the experiments help to understand the long term behaviour of these components. Likewise, our project BRUZL started at BAM in 2018 with the aim of developing a fracture mechanics approach to understand and describe a potential brittle failure mechanism of fuel cladding during long-term interim storage. BAM also contributes to the GRS project “Development of methods and models and international exchange for safety evaluation in the frame of interim storage of radioactive waste”. Additionally, BAM is involved in several international research programmes dealing with extended interim storage, such as the European Joint Programme on Radioactive Waste Management (EURAD), the Extended Storage Collaboration Program (ESCP) and IAEA Coordinated Research Projects.
The present contribution provides a comprehensive overview of BAM research activities contributing to national and international gap analyses and to filling knowledge gaps regarding the safe long term management of radioactive waste.
Both chain scission and crosslinking reactions occur during ageing of EPDM rubber. However, with many conventional polymer analysis methods such as hardness and DMA, it is hardly possible to obtain information about the contribution of each reaction type to the measured data. For example, hardness and Tg both increase during ageing of EPDM, indicating crosslinking during ageing, but it is not clear whether this is partly counterbalanced by chain scission reactions which would lower hardness and Tg. An indication that chain scission reactions probably counteract the hardness or Tg increase by crosslinking is given by Compression Set (CS) measurements. CS exhibits a higher change than hardness or Tg, as CS increases additively through both chain scission and crosslinking reactions. In order to elucidate the share of chain scission reactions in the total degradation, a method testing relaxation and recovery behaviour using DMA equipment was applied. The method revealed the strong influence of chain scissions, leading to more pronounced relaxation and higher residual strain after compression.
Elastomers are susceptible to chemical ageing, i.e., scission and cross-linking, at high temperatures. This thermally driven ageing process affects their mechanical properties and leads to limited operating time. Continuous and intermittent stress Relaxation measurements were conducted on ethylene propylene diene rubber (EPDM) and hydrogenated nitrile butadiene rubber (HNBR) samples for different ageing times and an ageing temperature of 125 °C. The contributions of chain scission and cross-linking were analysed for both materials at different ageing states, elucidating the respective ageing mechanisms. Furthermore, compression set experiments were performed under various test conditions. Adopting the two-network model, compression set values were calculated and compared to the measured data. The additional effect of physical processes to scission and cross-linking during a long-term thermal exposure is quantified through the compression set analysis. The characteristic times relative to the degradation processes are also determined.