- Ageing (28)
- Seal (24)
- Compression set (23)
- Rubber (16)
- Elastomer (14)
- Low temperature (11)
- Metal seal (11)
- Aging (9)
- Degradation (9)
- Leakage rate (9)
Organisationseinheit der BAM
- 3 Gefahrgutumschließungen; Energiespeicher (45)
- 3.4 Sicherheit von Lagerbehältern (45)
- 9 Komponentensicherheit (2)
- 5 Werkstofftechnik (1)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
- 7 Bauwerkssicherheit (1)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (1)
- 9.5 Tribologie und Verschleißschutz (1)
- 9.6 Additive Fertigung metallischer Komponenten (1)
Paper des Monats
- ja (3)
Eingeladener Vortrag
- nein (20)
In consideration of the influence of the curing reaction on the material properties of elastomers, it is very important to control the vulcanization process properly.
As shown previously [1], the effects of the vulcanization reaction of an elastomer can be monitored by use of ultrasonic sound waves. This technique has to a certain degree a high similarity to the standard curemeter test according to ISO 6502 but can be applied also inside a production tool.
So far, the method was only applied to the vulcanization of one compound at a given temperature and sample thickness. This is now complemented with measurements on another compound system at different temperatures and sample thicknesses.
The expected effects of temperature and thickness on the curing behaviour were found by use of the ultrasound online control.
Monitoring the vulcanization of elastomers: Comparison of curemeter and ultrasonic online control
(2009)
The vulcanization of elastomeric materials has a high impact on the properties of the final product. Therefore, it is important to monitor and control this crosslinking process. A common technique to attain the necessary curing time is the use of a curemeter in accordance with ISO 6502 in order to determine the time for full cure of a sample with a standardized geometry. Based on this result and a lot of practical experience, the required curing time for a given product geometry is estimated. Within the scope of this work, a new analysis technique will be compared with the standard procedure. The ultrasonic online control employs ultrasound waves to measure the changes in material properties caused by vulcanization. For this study, a natural rubber compound with a conventional curing system was investigated by both techniques. It was found that the results of the ultrasonic technique show good agreement with the results of the curemeter.
Today rubber is due to its unique property profile one of the most important materials for the production of bearings, dampers or also tires and tubes. In the production of rubber goods a chemical cross-linking reaction (vulcanisation) generates the final material properties. This process takes place during the shape giving of the rubber compound in the mould and can proceed for several minutes. The cross-linking process is influenced by the mixture of the basic polymer, the cross-linking agent, the influence of catalysts and inhibitors and especially the processing conditions. The quality of every ingredient, the reproducibility of the mixing ratio, the homogeneity of the mixture and the accurateness in temperature control can have a direct influence on the cross linking reaction. To control the quality of a rubber compound and verify the processing conditions in industry moving die rheometers, named curemeter, are involved in the production process. Starting from our experience in cure monitoring of thermosetting materials by measuring ultrasound velocity in the mould we extended the measuring principle to rubber vulcanisation monitoring. After first investigations using a compression mould we dealt here with on-line monitoring of vulcanisation in an injection moulding process which is one of the most used techniques in rubber industry.
A new method for the evaluation of the low temperature properties of rubber materials is presented. The method emulates the standardized compression set measurement, which is frequently used for sealing materials, but can be performed within a considerably shorter time. The results are compared with the standard test and found to be qualitatively the same. Slight differences are discussed on the basis of the differences in the measurement procedures. Further data evaluation is done by fitting functions to describe the material behaviour.
Rubbers are widely used as main sealing materials for containers for low and intermediate level radioactive waste and as additional component to metal seals in spent fuel and high active waste containers. The save encapsulation of the radioactive container inventory has to be guaranteed according to legislation and appropriate guidelines for long term storage periods as well as down to temperatures of -40 °C during transport.
Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance.
It is known that the material properties of rubbers are strongly temperature dependent. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling the material changes from rubber-like entropy-elastic to stiff energy-elastic behaviour, that allows nearly no strain or retraction, due to the glass transition. Hence rubbers are normally used above their glass transition but the minimum working temperature limit is not defined precisely, what can cause problems during application. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties.
The results of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are combined with the results of standardized measurements as the compression set according to ISO 815. To reduce the test time of the standard tests a faster technique was developed.
Additionally, the breakdown temperature of the sealing function of complete O-ring seals is measured in a component test setup to compare it with the results of the other tests. The experimental setup is capable of measuring the leakage rate at low temperatures by the pressure rise method.
A fluorocarbon rubber (FKM) was selected for this investigation as it is often used for radioactive waste containers. Some materials (seals and test sheets) were purchased from a commercial seal producer and some materials were compounded and cured at BAM in form of rubber sheets.
The special properties of high molecular weight polyethylene (HMW-PE) and ultra high molecular
weight polyethylene (UHMW-PE) result basically from their extreme chain lengths and their high
degree of crystallinity. As high-performance polymers, they are used for a variety of applications.
UHMW-PE in particular is often utilized for endoprothesis (due to its excellent slip and wear
properties) and due to its high hydrogen content as a neutron moderator in casks for storage and
transport of radioactive materials.
To prepare the material for instance for its use as a total joint replacement, it is exposed to radiation
for several reasons, such as sterilization and crosslinking, leading to partial improvement of the
mechanical properties (e.g. fracture toughness, crack propagation resistance, wear resistance) and
better chemical stability.
To be applicable for long term radiation shielding purposes for instance over a period of 40 years,
PE has to withstand any type of degradation affecting safety relevant aspects.
The scope of our investigation comprises an estimation of the radiation impact on the molecular and
supra molecular structure of two types of PE and to what extent these changes are detectable by
thermo-analytical (TA) methods, such as Differential Scanning Calorimetry (DSC), Thermo
Mechanical Analysis (TMA), Dynamic Mechanical Analysis (DMA) and Thermo Gravimetric
Analysis (TGA). Additionally FT-IR spectroscopy as well as density and gas sorption
measurements were carried out.
Due to the poor solubility of HMW-PE and UHMW-PE, some classical analytical techniques are
not applicable. But TA-methods represent a feasible approach to detect structural and
morphological features of these materials as well as changes caused by external influences, such as
thermal treatment and/or irradiation. With the combination of the applied TA-techniques it is
possible to distinguish between crosslinking and degradation.
The temperature dependences of dielectric permittivity and elastic modulus of poly(vinylidene fluoride - hexafluoropropylene) (P(VDF-HFP)) are compared and explained by use of structural data obtained by differential scanning calorimetry and X-ray analysis. Special emphasis is put on the effect of uniaxial stretching which renders the polymer ferroelectric. It is shown that dielectric and mechanical relaxations at the glass transition (aa relaxation) are closely related and not significantly affected by stretching. It is further confirmed that stretching destroys the non-polar spherulitic crystalline structure and produces relatively small-sized polar crystallites. This manifests in the disappearence of the so-called ac relaxation which is associated to molecular motions within the spherulitic crystalline lamellae. However, there are discrepancies between dielectric and mechanical losses above the glass transition which point towards a still not described structural transition.
Ultra high molecular weight polyethylene (UHMW-PE) - due to its high hydrogen content - is used as neutron shielding material in casks for storage and transport of radioactive materials. Besides this, UHMW-PE - as a high-performance polymer - has been used for several years in medical technology due to its excellent slip and wear properties. Due to the special properties of UHMW-PE which result basically from its extreme chain lengths and its high degree of crystallinity, it is predestinated for the aforementioned applications.
In both cases, irradiation and its impact on the molecular structure of polyethylene play an important role. In the first case, irradiation exists as a by-product of inserting the radioactive material in the cask. Hence PE has to withstand any type of degradation affecting safety relevant aspects to be applicable for long term radiation shielding purposes for instance over a period of 40 years. In the second case irradiation is applied deliberately for purposes such as sterilization and crosslinking, leading to partial improvement of the mechanical properties (e.g. fracture toughness, crack propagation resistance, wear resistance) and better Chemical stability.
Specifically concerning their use in the field of medical technology, different types of UHMW-PE have been objects of numerous publications. It is generally accepted that two parallel and competitive processes, based on chain scission and reactions of Ccentered radicals and molecular fragments, occur in PE as a consequence of radiation: radical recombination accounts for crosslinking, together with some disproportionation, formation of low molecular weight fragments, and recrystallization. Furthermore, formation of oxygenated structures in the presence of traces of oxygen is an antagonist of the C-centered radicals. Radiation induced scission preferentially takes place in the amorphous phase and noncrystalline surface of the crystals. It is followed by folding of molecular fragments, crystallinity growth and increased perfection in the crystal lamellae [4, 5]. Chain scission results in shorter polymer molecules, fewer entanglements, and consequently, increased molecular mobility.
The scope of our investigation comprises an estimation of the radiation and thermal impact on the molecular and supra molecular structure of the two types of PE used for neutron shielding cask components. A further point which is worth to explore is to what extent these changes are detectable by thermo-analytical (TA) methods, such as Differential Scanning Calorimetry (DSC), Thermo Mechanical Analysis (TMA), Dynamic Mechanical Analysis (DMA) and Thermogravimetry (TG). Additionally FT-IR and solubility measurements have been performed.
In our studies we focused on the UHMW-PE material GUR 4120 which was y irradiated at RT and compared to the untreated material.
Rubbers are often used for seal applications due to their special material properties and easy use. In many applications the material is exposed to low temperatures during Operation. Therefore it is important to know the material behavior at low temperatures to determine the temperature ränge that allows a Safe Operation of the seal, e.g. in storage and transport Containers for radioactive materials.
The seal function of an elastomer is limited in temperature by the rubber-glass transition during which the material properties change from rubber-like to stiff and glass-like. For a given application this correlation is not trivial and therefore needs an in-depth investigation under consideration of the physical properties and the
application conditions.
In this work different analytical methods are used to characterize the material behavior at low temperature in the ränge of the glass-rubber-transition and are compared with the quality of Operation of a component which is here defined by the detected leakage rate.
Elastomers are widely used as the main sealing materials for containers for low and intermediate level radioactive waste and as an additional component to metal seals in spent fuel and high active waste containers. The safe encapsulation of the radioactive container inventory has to be guaranteed according to regulation and appropriate guidelines for long term storage periods as well as for temperatures as low as -40°C during transport. Therefore, the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance. It is known that the material properties of elastomers are strongly temperature dependent. At low temperatures, this is caused by the rubber-glass transition (abbreviated: glass transition). During continuous cooling, the material changes from a rubber-like entropy elastic to a stiff energy elastic behaviour, which allows nearly no strain or retraction. Hence, rubbers are normally used above their glass transition, but the minimum working temperature limit is not defined precisely; this can cause problems during the above noted applications. Therefore, the lower operation temperature limit of elastomer seals must be determined in dependence of the material properties. Differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) are combined with standardised measurements to determine the compression set according to ISO 815. To reduce the test time of the standard tests, a faster technique than normally used was developed. Additionally, the breakdown temperature of the sealing function of complete O ring seals was measured in a component test set-up to compare it with the results of the other tests. The experimental set-up is capable of measuring the leakage rate at low temperatures by the pressure rise method. A fluorocarbon rubber (FKM) was selected for this investigation as it is often used for radioactive waste containers. The materials (seals and test sheets) were purchased from a commercial seal producer.
Two types of commercially applied Ethylene/Vinyl Acetate Copolymers (EVA) for encapsulation of photovoltaic modules were investigated by the thermal analysis methods of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) in the temperature range from -150 °C to 200 °C. Glass transition, crystal melting and cross-linking were analyzed. The aims of the investigations were to gain more information for incoming goods control and to get information about the whole temperature dependent material properties in the investigated temperature range, starting at very low temperatures up to the crosslinking temperature region.
Rubber is widely used as sealing material in various applications. In many fields the sealing function at low temperatures is necessary. Therefore the understanding of failure mechanisms is of high importance. Rubbers are normally used above their glass-rubber transition region but the minimum working temperature limit is not defined precisely. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties. The results of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are combined with the results of the standardized compression set according to ISO 815 respectively a modified test using the DMA equipment.
EVA is a widely used material for the encapsulation of photovoltaic modules. It melts at elevated temperatures, and seals the module before it is crosslinked at temperatures above 130 °C by a peroxide-initiated crosslinking reaction. EVA has good optical properties necessary for application in solar modules. For process optimization and quality management, a method for the quick and reliable characterization of EVA crosslinking behaviour is of great value. Here, the practicability of ultrasound for online crosslinking monitoring is demonstrated. A sound velocity increase of about 8 m/s during the crosslinking reaction is found. The ultrasound results are compared with rheometer measurements performed with a curemeter typically used for the investigation of rubber crosslinking.
Fracture mechanics approaches are increasingly applied for the characterization of epoxy resin and adhesive mechanical properties. Therefore, the fracture toughness and crack resistance under static load ISO 13586 [1] are often regarded as state of the art to analyse material improvements. However, experimental investigations on fatigue behaviour, thus the crack propagation according to ISO 15850 [2], seem to be much more sensitive to characterize the materials for in service loading conditions. Firstly, an efficient testing concept was developed at BAM. In this framework, the geometry for a modified single edge notched tensile specimen (SET) was developed in order to assure appropriate resolution in measuring the crack length via a CCD-camera [3]. In the next step, the influence of the cure temperature on the fracture-mechanical properties was investigated.