Filtern
Erscheinungsjahr
- 2012 (15) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (4)
- Beitrag zu einem Tagungsband (4)
- Vortrag (4)
- Beitrag zu einem Sammelband (1)
- Dissertation (1)
- Posterpräsentation (1)
Schlagworte
- Crack propagation (2)
- Crack resistance (2)
- Elastomer (2)
- Fracture mechanics (2)
- Fracture toughness (2)
- Plastics (2)
- (U)HMW-PE (1)
- Acoustic propagation (1)
- Cask for storage and transport of radioactive materials (1)
- Compression set (1)
Eingeladener Vortrag
- nein (4)
Partial discharges may cause damage to electrical insulation of high voltage equipment. They initiate elastic waves in the insulating material, e.g. in the stress cone of an outdoor termination. Localisation of the origin of such elastic waves can help to predict serious damaging processes in the electrical insulation. In order to measure and evaluate the wave propagation effects in typical multilayered elastomeric structures, knowledge of the material properties is required. The propagating velocity and the attenuation of longitudinal waves are important parameters. Values for these quantities found in the literature were not appropriate. Therefore, for cross-linked polyethylene (XLPE) and cured liquid silicone rubber (LSR), the longitudinal wave velocity and the attenuation were evaluated in the temperature interval from -20°C to 50°C and in the frequency range from 200 kHz to 600 kHz using a two-sample ultrasound technique. The loss factor was determined from these measured quantities. Additionally, low frequency Dynamic Mechanical Thermal Analysis (DMTA) was applied to investigate LSR and XLPE in a temperature interval between -100 and 50°C and to check qualitatively the ultrasound data.
The method for the determination of compression set values with a Dynamic Mechanical Analysis (DMA) setup at low temperatures, which was presented previously, allows a much faster and readily automated procedure than the standardized compression set test according to ISO 815-2. This method is applied to a series of different elastomeric materials that are commonly used for sealing applications. The results of the compression set test are compared with results from thermal analysis to allow an in depth comparison of the material behaviour at low temperatures.
Furthermore, a comparison between two EPDM materials is presented. These materials show very similar properties determined by thermo analytical methods such as Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) but differ clearly in their compression set behaviour. This comparison shows the importance and value of information of the compression set test in addition to thermal analysis to judge the behaviour of sealing materials and confirms the relevance of the new compression set test method for the investigation of low temperature properties of elastomers.
Fracture mechanics approaches are increasingly applied for the characterization of epoxy resin and adhesive mechanical properties. Therefore, the fracture toughness and crack resistance under static load ISO 13586 [1] are often regarded as state of the art to analyse material improvements. However, experimental investigations on fatigue behaviour, thus the crack propagation according to ISO 15850 [2], seem to be much more sensitive to characterize the materials for in service loading conditions. Firstly, an efficient testing concept was developed at BAM. In this framework, the geometry for a modified single edge notched tensile specimen (SET) was developed in order to assure appropriate resolution in measuring the crack length via a CCD-camera [3]. In the next step, the influence of the cure temperature on the fracture-mechanical properties was investigated.
EVA is a widely used material for the encapsulation of photovoltaic modules. It melts at elevated temperatures, and seals the module before it is crosslinked at temperatures above 130 °C by a peroxide-initiated crosslinking reaction. EVA has good optical properties necessary for application in solar modules. For process optimization and quality management, a method for the quick and reliable characterization of EVA crosslinking behaviour is of great value. Here, the practicability of ultrasound for online crosslinking monitoring is demonstrated. A sound velocity increase of about 8 m/s during the crosslinking reaction is found. The ultrasound results are compared with rheometer measurements performed with a curemeter typically used for the investigation of rubber crosslinking.