Rubbers are widely used as main sealing materials for containers for low and intermediate level radioactive waste and as additional component to metal seals in spent fuel and high active waste containers. The save encapsulation of the radioactive container inventory has to be guaranteed according to legislation and appropriate guidelines for long term storage periods as well as down to temperatures of -40 °C during transport.
Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance.
It is known that the material properties of rubbers are strongly temperature dependent. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling the material changes from rubber-like entropy-elastic to stiff energy-elastic behaviour, that allows nearly no strain or retraction, due to the glass transition. Hence rubbers are normally used above their glass transition but the minimum working temperature limit is not defined precisely, what can cause problems during application. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties.
The results of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are combined with the results of standardized measurements as the compression set according to ISO 815. To reduce the test time of the standard tests a faster technique was developed.
Additionally, the breakdown temperature of the sealing function of complete O-ring seals is measured in a component test setup to compare it with the results of the other tests. The experimental setup is capable of measuring the leakage rate at low temperatures by the pressure rise method.
A fluorocarbon rubber (FKM) was selected for this investigation as it is often used for radioactive waste containers. Some materials (seals and test sheets) were purchased from a commercial seal producer and some materials were compounded and cured at BAM in form of rubber sheets.
THz and Mid IR Fourier transform spectroscopy on polyethylene irradiated with Gamma- Co60 radiation
(2014)
THz and mid IR spectroscopy of high molecular PE (HMW) and ultra high molecular PE (UHMW) reveals modifications of the molecular structure induced by γ-Co60 radiation. UHMW-PE and HMW-PE can be distinguished. The integral absorption in the B1u THz-region can quantitatively describe the amorphization of crystallinity. The formation of trans vinylene unsaturations and the decay of vinyl can be followed by mid IR spectroscopy
Fourier-Spektroskopische Untersuchungen von hochmolekularem Polyethylen (HMW-PE) und ultrahochmolekularem Polyethylen (UHMW-PE) im Mittleren - und Fernen Infrarotbereich können Veränderungen der molekularen Strukturen nachweisen, die durch Co60 γ-Strahlung und Rekristallisationsprozesse initiiert werden. UHMW-PE und HMW-PE sind im gewählten IR-Bereich unterscheidbar. Die integrale Absorption der B1u – Gitterschwingungen im Fernen Infrarotbereich (THz-Bereich) ermöglichen die quantitative Beschreibung des Kristallinitätsgrades und dessen Abbau. Die Bildung ungesättigter Vinylengruppen und der Abbau ungesättigter Methylengruppen können im Mittleren Infrarotbereich nachgewiesen werden.
The special properties of high molecular weight polyethylene (HMW-PE) and ultra high molecular
weight polyethylene (UHMW-PE) result basically from their extreme chain lengths and their high
degree of crystallinity. As high-performance polymers, they are used for a variety of applications.
UHMW-PE in particular is often utilized for endoprothesis (due to its excellent slip and wear
properties) and due to its high hydrogen content as a neutron moderator in casks for storage and
transport of radioactive materials.
To prepare the material for instance for its use as a total joint replacement, it is exposed to radiation
for several reasons, such as sterilization and crosslinking, leading to partial improvement of the
mechanical properties (e.g. fracture toughness, crack propagation resistance, wear resistance) and
better chemical stability.
To be applicable for long term radiation shielding purposes for instance over a period of 40 years,
PE has to withstand any type of degradation affecting safety relevant aspects.
The scope of our investigation comprises an estimation of the radiation impact on the molecular and
supra molecular structure of two types of PE and to what extent these changes are detectable by
thermo-analytical (TA) methods, such as Differential Scanning Calorimetry (DSC), Thermo
Mechanical Analysis (TMA), Dynamic Mechanical Analysis (DMA) and Thermo Gravimetric
Analysis (TGA). Additionally FT-IR spectroscopy as well as density and gas sorption
measurements were carried out.
Due to the poor solubility of HMW-PE and UHMW-PE, some classical analytical techniques are
not applicable. But TA-methods represent a feasible approach to detect structural and
morphological features of these materials as well as changes caused by external influences, such as
thermal treatment and/or irradiation. With the combination of the applied TA-techniques it is
possible to distinguish between crosslinking and degradation.
Ultra high molecular weight polyethylene (UHMW-PE) - due to its high hydrogen content - is used as neutron shielding material in casks for storage and transport of radioactive materials. Besides this, UHMW-PE - as a high-performance polymer - has been used for several years in medical technology due to its excellent slip and wear properties. Due to the special properties of UHMW-PE which result basically from its extreme chain lengths and its high degree of crystallinity, it is predestinated for the aforementioned applications.
In both cases, irradiation and its impact on the molecular structure of polyethylene play an important role. In the first case, irradiation exists as a by-product of inserting the radioactive material in the cask. Hence PE has to withstand any type of degradation affecting safety relevant aspects to be applicable for long term radiation shielding purposes for instance over a period of 40 years. In the second case irradiation is applied deliberately for purposes such as sterilization and crosslinking, leading to partial improvement of the mechanical properties (e.g. fracture toughness, crack propagation resistance, wear resistance) and better Chemical stability.
Specifically concerning their use in the field of medical technology, different types of UHMW-PE have been objects of numerous publications. It is generally accepted that two parallel and competitive processes, based on chain scission and reactions of Ccentered radicals and molecular fragments, occur in PE as a consequence of radiation: radical recombination accounts for crosslinking, together with some disproportionation, formation of low molecular weight fragments, and recrystallization. Furthermore, formation of oxygenated structures in the presence of traces of oxygen is an antagonist of the C-centered radicals. Radiation induced scission preferentially takes place in the amorphous phase and noncrystalline surface of the crystals. It is followed by folding of molecular fragments, crystallinity growth and increased perfection in the crystal lamellae [4, 5]. Chain scission results in shorter polymer molecules, fewer entanglements, and consequently, increased molecular mobility.
The scope of our investigation comprises an estimation of the radiation and thermal impact on the molecular and supra molecular structure of the two types of PE used for neutron shielding cask components. A further point which is worth to explore is to what extent these changes are detectable by thermo-analytical (TA) methods, such as Differential Scanning Calorimetry (DSC), Thermo Mechanical Analysis (TMA), Dynamic Mechanical Analysis (DMA) and Thermogravimetry (TG). Additionally FT-IR and solubility measurements have been performed.
In our studies we focused on the UHMW-PE material GUR 4120 which was y irradiated at RT and compared to the untreated material.