Rubber is widely used as sealing material in various applications. In many fields the function of seal materials at low temperatures is necessary. Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance. It is known that the material properties of rubbers are strongly temperature dependent. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling the material changes from rubber-like entropy-elastic behaviour to stiff energy-elastic behaviour, that allows nearly no strain or retraction, due to the glass transition. Hence rubbers are normally used above their glass transition but the minimum working temperature limit is not defined precisely, what can cause problems during application. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties. In the past we investigated the material properties and sealing behaviour of elastomeric seals at low temperatures. Additionally we started to study the effect of a small partial release of elastomer seals at low temperatures. To study the influence of dynamic events on seal performance and to enhance the understanding of occurring seal failure, a setup for a fast partial seal release was designed. In this contribution we focus on the correlation of material properties and component behaviour under different application conditions. It is desired to widen the understanding of the process of seal failure at low temperature.
In technical applications, static seals are sometimes also subjected to dynamic loadings. Therefore, the leakage behaviour under dynamic conditions has to be evaluated as well. For this purpose, FKM elastomer seals have been tested by using newly designed equipment that allows for rapid partial release of the seal and simultaneous leakage rate measurement at a wide range of test temperatures. Furthermore, material characterisation was done by using Dynamic Mechanical Analysis, Differential Scanning Calorimetry and Compression Set. It was shown that, under static conditions, the leakage rate increased significantly during cooling at temperatures around 18 K lower than the glass transition range. On reheating, the seal’s functionality was restored in the high temperature region of the glass rubber transition. In the subsequent dynamic release tests, that comprised a reduction of the seal compression within 1 s from 25 % to 23 %, increased leakage rates were observed in the high temperature region of the glass transition range. It was shown that the temperature that is critical for increased leakage is significantly lower under static conditions compared to dynamic conditions. The obtained leakage rates for static tests and dynamic release tests at different temperatures were analysed with reference to results of the material characterisation.
For many sealing applications rubbers are applied due to their special material properties and easy use. In many applications as e.g. in aviation, traffic or process technology the material can be exposed to low temperatures during operation. Therefore it is important to know the material behaviour at those low temperatures to determine the temperature range that allows a safe operation of the seal. As rubbers are used as main sealing materials for containers for low and intermediate level radioactive waste and as additional component to metal seals in spent fuel and high acitve waste containers, a comprehensive elastomer investigation program is run at BAM. This program comprises investigations of elastomer overall performance, durability, influence of gamma irradiation and low temperature behaviour.
In this paper we focus on the behaviour of elastomer seals below ambient temperatures after a fast partial release. Despite the primarily static application conditions of many seals their behaviour after partial compression release is of interest with regard to potential decrease of leak-tightness.
For this investigation a special setup was designed which allows the partial release of compressed seal systems at different temperatures accompanied by leakage rate measurements.
The results for FKM seals are presented and discussed.