- Compression set (5)
- Elastomer (5)
- DSC (4)
- Glass transition (4)
- Curemeter (3)
- Dynamic mechanical analysis (3)
- Low temperature behaviour (3)
- Prepreg (3)
- Sealing material (3)
- Ultrasound (3)
Epoxy carbon-fibre prepreg, Hexcel Type 6376 HTS, was investigated using Dynamic Mechanical Analysis (DMA). The DMA characteristic parameters are storage modulus E', loss modulus E' and loss factor tanδ. These parameters are ideally suited to observe the vitrification, referred to as glass transition, resulting from the cross-linking reaction. Detection of the cure state may also be achieved by determining the momentary glass transition temperature of partially cured samples. The consequent use of a multi-frequency measuring regime was used to derive the apparent activation energy for the glass transition process. Different temperature programs were also applied to monitor the curing process directly, as well as to investigate the different states of incomplete cure reached in preceding curing steps. The intention was to provide better understanding of the consequences of an interrupted autoclave curing process and to use DMA to detect the cure state achieved. With DMA, the continuation of an incomplete curing process also can be monitored. DMA measurements up to 300 °C showed, furthermore, that the final glass transition temperature was reduced by thermal degradation at high temperatures.
Rubbers are widely used as main sealing materials for Containers for low and intermediate level radioactive waste and as additional component to metal seals in spent fuel and high active waste containers. The save enclosure of the radioactive container inventory has to be guaranteed according to legislation and appropriate guidelines for long term storage periods as well as down to temperatures of -40 °C for transportation. Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is necessary to ensure a proper material choice which is certainly also influenced by additional factors as e.g. the aging behavior.
Carbon-fibre prepregs have found widespread use in lightweight applications. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. Prepreg materials are generally pre-cured so that they have a higher molecular weight than typical resins in order to reduce resin flow, which facilitates storage and later processing properties.
The measurements were carried out using commercially available materials and follow the published DMA investigations of the same material. TMDSC was used to find the correlation between curing conditions, the degree of cure and glass transition temperature. TMDSC has the advantage over standard DSC that it enables better determination of the glass transition temperature, which is often accompanied by an exothermic curing reaction, and thus overshadowed. The influence of the amplitude of temperature modulation was tested in preliminary experiments. For non-cured material a glass transition temperature of approximately 0 °C was determined; whereas for the totally cured material it was approximately 230 °C. The changes in degree of cure, temperature of actual glass transition and post-reaction are given as a function of curing time at 180 °C. The correlation between actual glass transition temperature and degree of cure is derived.
Rubbers are widely used as sealing material in various applications. In many fieldsthefunction of seal materials at lowtemperatures is required. Therefore the understanding of faiiure mechanisms that lead to leakage at low temperatures is of high importance. Therefore the lower Operation temperature limit of rubber seals should be determined in dependence of the material properties.
The results of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are combined with results of standardized measurements as the compression set according to ISO 815. To reduce the test time of the Standard tests a faster and more efficient technique was developed and applied. In addition the breakdown temperature of the sealing function of O-ring seals at lowtemperatures is measured in a component test Setup in dependence of the material and the degree of compression.
Carbon fibre prepregs have found widespread application in lightweight constructions. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. DMA measurements under temperature conditions similar to an autoclave programme were carried out using commercially available prepreg material with a high glass transition temperature. The characteristic of the temperature programme was a dynamic heating segment at 1.5 K/min followed by a longer isothermal segment at 180 °C. The courses of the storage modulus E', loss modulus E'' and tanδ were recorded. The measuring frequency was varied between 1 Hz and 33.3 Hz. Gelation and vitrification are assigned. The influence of the measuring frequency on the time to vitrification and the correlation with DSC are discussed. The reaction does not end even after 10 h curing at 180 °C, which is interpreted as the slow cessation of the reaction caused by vitrification.
EVA is a widely used material for the encapsulation of photovoltaic modules. It melts at elevated temperatures, and seals the module before it is crosslinked at temperatures above 130 °C by a peroxide-initiated crosslinking reaction. EVA has good optical properties necessary for application in solar modules. For process optimization and quality management, a method for the quick and reliable characterization of EVA crosslinking behaviour is of great value. Here, the practicability of ultrasound for online crosslinking monitoring is demonstrated. A sound velocity increase of about 8 m/s during the crosslinking reaction is found. The ultrasound results are compared with rheometer measurements performed with a curemeter typically used for the investigation of rubber crosslinking.
The method for the determination of compression set values with a Dynamic Mechanical Analysis (DMA) setup at low temperatures, which was presented previously, allows a much faster and readily automated procedure than the standardized compression set test according to ISO 815-2. This method is applied to a series of different elastomeric materials that are commonly used for sealing applications. The results of the compression set test are compared with results from thermal analysis to allow an in depth comparison of the material behaviour at low temperatures.
Furthermore, a comparison between two EPDM materials is presented. These materials show very similar properties determined by thermo analytical methods such as Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) but differ clearly in their compression set behaviour. This comparison shows the importance and value of information of the compression set test in addition to thermal analysis to judge the behaviour of sealing materials and confirms the relevance of the new compression set test method for the investigation of low temperature properties of elastomers.
Partial discharges may cause damage to electrical insulation of high voltage equipment. They initiate elastic waves in the insulating material, e.g. in the stress cone of an outdoor termination. Localisation of the origin of such elastic waves can help to predict serious damaging processes in the electrical insulation. In order to measure and evaluate the wave propagation effects in typical multilayered elastomeric structures, knowledge of the material properties is required. The propagating velocity and the attenuation of longitudinal waves are important parameters. Values for these quantities found in the literature were not appropriate. Therefore, for cross-linked polyethylene (XLPE) and cured liquid silicone rubber (LSR), the longitudinal wave velocity and the attenuation were evaluated in the temperature interval from -20°C to 50°C and in the frequency range from 200 kHz to 600 kHz using a two-sample ultrasound technique. The loss factor was determined from these measured quantities. Additionally, low frequency Dynamic Mechanical Thermal Analysis (DMTA) was applied to investigate LSR and XLPE in a temperature interval between -100 and 50°C and to check qualitatively the ultrasound data.
Two types of commercially applied Ethylene/Vinyl Acetate Copolymers (EVA) for encapsulation of photovoltaic modules were investigated by the thermal analysis methods of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) in the temperature range from -150 °C to 200 °C. Glass transition, crystal melting and cross-linking were analyzed. The aims of the investigations were to gain more information for incoming goods control and to get information about the whole temperature dependent material properties in the investigated temperature range, starting at very low temperatures up to the crosslinking temperature region.
Rubber is widely used as sealing material in various applications. In many fields the sealing function at low temperatures is necessary. Therefore the understanding of failure mechanisms is of high importance. Rubbers are normally used above their glass-rubber transition region but the minimum working temperature limit is not defined precisely. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties. The results of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are combined with the results of the standardized compression set according to ISO 815 respectively a modified test using the DMA equipment.
A new method for the evaluation of the low temperature properties of rubber materials is presented. The method emulates the standardized compression set measurement, which is frequently used for sealing materials, but can be performed within a considerably shorter time. The results are compared with the standard test and found to be qualitatively the same. Slight differences are discussed on the basis of the differences in the measurement procedures. Further data evaluation is done by fitting functions to describe the material behaviour.
Monitoring the vulcanization of elastomers: Comparison of curemeter and ultrasonic online control
(2009)
The vulcanization of elastomeric materials has a high impact on the properties of the final product. Therefore, it is important to monitor and control this crosslinking process. A common technique to attain the necessary curing time is the use of a curemeter in accordance with ISO 6502 in order to determine the time for full cure of a sample with a standardized geometry. Based on this result and a lot of practical experience, the required curing time for a given product geometry is estimated. Within the scope of this work, a new analysis technique will be compared with the standard procedure. The ultrasonic online control employs ultrasound waves to measure the changes in material properties caused by vulcanization. For this study, a natural rubber compound with a conventional curing system was investigated by both techniques. It was found that the results of the ultrasonic technique show good agreement with the results of the curemeter.
In consideration of the influence of the curing reaction on the material properties of elastomers, it is very important to control the vulcanization process properly.
As shown previously [1], the effects of the vulcanization reaction of an elastomer can be monitored by use of ultrasonic sound waves. This technique has to a certain degree a high similarity to the standard curemeter test according to ISO 6502 but can be applied also inside a production tool.
So far, the method was only applied to the vulcanization of one compound at a given temperature and sample thickness. This is now complemented with measurements on another compound system at different temperatures and sample thicknesses.
The expected effects of temperature and thickness on the curing behaviour were found by use of the ultrasound online control.
Über die in der Technik weit verbreitete typisierte Harnstoffformmasse UF 131.5, ein Aminoplast, wird berichtet, dass sie im Zuge der thermisch aktivierten Vernetzungsreaktion wegen "Überhärtung" mangelhafte Eigenschaften annimmt. Zur Verifizierung dieses Effektes werden mithilfe der Ultraschall-Prozesskontrolle gezielt Proben unterschiedlicher Aushärtegrade hergestellt. Sie werden mit verschiedenen Methoden, wie der "Kochprobe" und der Thermoanalyse, charakterisiert und auf ihre Materialeigenschaften untersucht. Dabei zeigt sich ein deutlicher Einfluss der Härtezeit auf die Glasübergangstemperatur der Formmasse. In den mechanischen Eigenschaften ist eine Veränderung allerdings nur in der Schlagzähigkeit festzustellen, die sich mit steigender Härtezeit sogar wesentlich verbessert.