Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (52)
- Vortrag (51)
- Zeitschriftenartikel (10)
- Posterpräsentation (9)
- Beitrag zu einem Sammelband (8)
- Buchkapitel (1)
- Dissertation (1)
Referierte Publikation
- nein (132) (entfernen)
Schlagworte
- Ageing (21)
- Seal (21)
- Compression set (11)
- Elastomer (11)
- Rubber (10)
- Metal seal (9)
- Degradation (8)
- Dichtung (8)
- Low temperature (8)
- Aging (7)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (51)
Elastomerdichtungen finden als Bauteil oder Maschinenelement vielseitige Verwendung. Jedoch war trotz ihrer zentralen Bedeutung die untere Temperaturgrenze, bis zu der solche Dichtungen eingesetzt werden können, bisher nicht tiefgehend verstanden. Dieser Umstand erschwert die entsprechende notwendige sicherheitsrelevante Beurteilung. Mit der vorliegenden Arbeit ist deshalb das Ziel verfolgt worden, dass Materialverhalten repräsentativer Elastomerwerkstoffe in Abhängigkeit von der Temperatur zu verstehen und daraus dann abzuleiten, bis zu welcher Temperatur eine daraus hergestellte Dichtung unter Berücksichtigung der jeweiligen Einsatzbedingungen ihre Funktion noch sicher erfüllen kann. Ausgehend von der in der Literatur beschriebenen Aussage, dass eine Dichtung auch unterhalb der „Glasübergangstemperatur“ funktionsfähig ist, wurde der Einfluss des Glas-Gummi-Übergangs auf das Dichtungsversagen untersucht. Zunächst wurden dazu die Glasübergangstemperaturen an einer Vielzahl von Elastomeren mit gebräuchlichen Verfahren bestimmt, um diese mit dem Verhalten der Dichtung vergleichen zu können. Weiterhin wurde im Rahmen der Arbeit eine neue Charakterisierungsmethode des Tieftemperaturverhaltens von Elastomeren entwickelt, die die bisher für Dichtungen eingesetzte Normprüfung des Druckverformungsrests nachstellt. Mit dieser Methode ist im Vergleich zur Normprüfung jedoch eine deutlich schnellere und automatisierbare Untersuchung des Materialverhaltens gegeben. Darüber hinaus ist durch eine modellgestützte Auswertung eine Extrapolation der Messdaten auf zusätzliche Temperaturen möglich, wodurch der experimentelle Aufwand weiter reduziert wird. Zur temperaturabhängigen Charakterisierung des Versagensvorgangs an realen Bauteilen wurde deren Dichtverhalten mittels eines dafür entwickelten Versuchsstandes untersucht. Die festgestellte Abhängigkeit der Versagenstemperatur vom Verpressgrad konnte unter Verwendung der Ergebnisse aller angewandten Charakterisierungsmethoden für die hier untersuchten statisch beanspruchten Dichtungen erklärt werden. Zudem lassen sich aus dem mit Hilfe des Zeit-Temperatur- Superpositionsprinzips gewonnenen Informationen zur Zeitabhängigkeit der Materialeigenschaften auch Aussagen zum Verhalten von dynamisch beanspruchten Dichtungen ableiten. Mit dem Ergebnis der Arbeit zum Verständnis des Verhaltens von Elastomerdichtungen bei tiefen Temperaturen wird die gezielte Beurteilung und Auswahl von sicherheitsrelevanten Dichtsystemen in Zukunft vereinfacht.
Die Messung des dynamischen Speichermoduls mit der Dynamisch-Mechanischen-Analyse ermöglicht einen schnellen Überblick über das temperaturabhängige Verhalten von elastomeren Dichtungsmaterialien. Ein direkter Rückschluss von der so ermittelten Glasübergangstemperatur Tg auf die Versagenstemperatur einer Dichtung ist aber ohne zusätzliche Messungen bisher nicht möglich.
Mit den Ergebnissen des Druckverformungsrestes DVR und des DVRDMA ist eine ge-nauere Beschreibung der Tieftemperatureigenschaften und dadurch der Funktion von elastomeren Dichtungsmaterialien möglich. Messungen ergeben beispielsweise, dass sich das EPDM bei einer Temperatur von -40 °C laut der Dynamisch Mechanischen Analyse noch im gummielastischen Bereich befindet. Die DVRDMA-Werte zeigen eine Rückstellung um mehr als 40 % der Ausgangsdeformation in wenigen Minuten.
Mit derart detailliert bestimmten Eigenschaften lassen sich Rückschlüsse auf einsatzspezifische Anforderungen wie z. B. die Dichtwirkung in Abhängigkeit von Betriebstemperatur und mechanischer Belastungsgeschwindigkeit ziehen, so dass je nach Einsatzbedingungen für die Dichtungen eine geeignete Materialauswahl getrof-fen werden kann.
Rubbers are widely used as main sealing materials for containers for low and intermediate level radioactive waste and as additional component to metal seals in spent fuel and high active waste containers. The save encapsulation of the radioactive container inventory has to be guaranteed according to legislation and appropriate guidelines for long term storage periods as well as down to temperatures of -40 °C during transport.
Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance.
It is known that the material properties of rubbers are strongly temperature dependent. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling the material changes from rubber-like entropy-elastic to stiff energy-elastic behaviour, that allows nearly no strain or retraction, due to the glass transition. Hence rubbers are normally used above their glass transition but the minimum working temperature limit is not defined precisely, what can cause problems during application. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties.
The results of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are combined with the results of standardized measurements as the compression set according to ISO 815. To reduce the test time of the standard tests a faster technique was developed.
Additionally, the breakdown temperature of the sealing function of complete O-ring seals is measured in a component test setup to compare it with the results of the other tests. The experimental setup is capable of measuring the leakage rate at low temperatures by the pressure rise method.
A fluorocarbon rubber (FKM) was selected for this investigation as it is often used for radioactive waste containers. Some materials (seals and test sheets) were purchased from a commercial seal producer and some materials were compounded and cured at BAM in form of rubber sheets.
At BAM Federal Institute for Materials Research and Testing in Germany, it is our responsibility to audit the safety of casks designed for transport and/or storage of radioactive material. With regard to the requirements on long-term safety of the containers, it is necessary to evaluate the service lifetime of the elastomeric seals used in the containers. With ageing, the elastomers will gradually lose their elasticity and their ability for recovery, which might result in a leakage above the allowed level or in a release of radioactivity during an incident. It is important to know the rate of degradation and which property can be used as an practical and easily measurable end-of-lifetime criterion. For this reason, we devised ageing experiments on different kinds of elastomers, namely FKM, EPDM and HNBR. The former two are actually used in containers for radioactive wastes – either as auxiliary seal in casks containing high activity waste, or as main seal in casks for medium or low activity waste. The latter is an often used seal material that is tested for comparative reasons. In our ageing program, these three materials are aged at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) in order to extrapolate the data to service temperature using a suitable model. They are examined at logarithmic time intervals of several days up to 5 years. The samples are aged in their undeformed O-ring state as well as compressed between flanges with a deformation corresponding to the actual compression during service. Thus we can compare the ageing between relaxed and stressed sample. Additionally, we are ageing samples in flanges that allow leakage rate measurements. Other measurements include monitoring of the recovery force of the seal and the compression set. Furthermore, the samples are examined by thermal and dynamic-mechanical analysis for detecting changes in the glass transition temperature due to crosslinking or chain scission in the material. Besides, hardness is measured as a practical macroscopic indicator. Until now, we have analyzed samples aged up to 100 days. At the highest ageing temperature of 150 °C, the compressed EPDM has already reached a compression set of 95 %, while HNBR and FKM have reached 80 % and 30 %, respectively. Furthermore, HNBR has reached a Shore D hardness of 85, which is an immense increase after the initial value of 80 Shore A. However, when looking at the cross-section of the sample, it was obvious that only a layer of about 1 mm thickness has become so hard, while the inner part remained rubbery. This shows that there has been intense crosslinking mostly near the surface of the HNBR which forms a kind of oxygen diffusion barrier, inhibiting the thermooxidation of the inner part of sample which can retain elastic properties. In EPDM, the oxygen permeability is much greater, which leads to a more homogeneous degradation across the whole sample and thus resulted in a higher compression set. The low compression set of FKM shows the outstanding high-temperature properties of this material.
For many sealing applications rubbers are applied due to their special material properties and easy use. In many applications, e.g. in aviation, traffic or process technology the material can be exposed to low temperatures during Operation. Therefore it is important to know the material behaviour at those low temperatures to determine the temperature range that allows a safe Operation of the seal. As rubbers are used as main sealing materials for Containers for low and intermediate level radioactive waste and as additional component to metal seals in spent fuel and high active waste Containers, a comprehensive elastomer investigation program is run at BAM. This program comprises investigations of elastomer overall performance, durability, influence of gamma irradiation and low temperature behaviour.
In this paper we focus on the behaviour of elastomer seals at low temperatures with regard to potential decrease of leak-tightness as material properties of rubbers are strongly temperature dependent. But additionally to the investigation presented in the past which considered the material properties of new materials and the seal behaviour under purely static conditions [1, 2] we now focus on irradiated materials and on the sealing performance after a fast partial release of the compressed seal.
For the investigations different materials were used, e.g. fluorocarbon (FKM) and ethylenepropylene-diene (EPDM) rubber. To determine the effect of gamma irradiation some samples were irradiated and studied by several thermo-analytical methods and compression set. For the investigation of the seal performance under non static conditions we decided to design a new measurement setup which allows for a small flange deflection and simultaneous leakage rate measurement at low temperatures.
Fourier-Spektroskopische Untersuchungen von hochmolekularem Polyethylen (HMW-PE) und ultrahochmolekularem Polyethylen (UHMW-PE) im Mittleren - und Fernen Infrarotbereich können Veränderungen der molekularen Strukturen nachweisen, die durch Co60 γ-Strahlung und Rekristallisationsprozesse initiiert werden. UHMW-PE und HMW-PE sind im gewählten IR-Bereich unterscheidbar. Die integrale Absorption der B1u – Gitterschwingungen im Fernen Infrarotbereich (THz-Bereich) ermöglichen die quantitative Beschreibung des Kristallinitätsgrades und dessen Abbau. Die Bildung ungesättigter Vinylengruppen und der Abbau ungesättigter Methylengruppen können im Mittleren Infrarotbereich nachgewiesen werden.
According to the relevant guidelines and regulations, the safe enclosure of radioactive Container contents has to be guaranteed for long storage periods as well as down to temperatures of -40 °C during transportation. As rubbers are widely used as the main sealing materials for Containers for low- and intermediate-level radioactive waste and as additional component to metal seals in spent fuel and high active waste Containers, a comprehensive eiastomer investigation Programme is in place at BAM. This Programme comprises investigations of overall eiastomer performance, durability, influence of gamma irradiation and low temperature behaviour.
In this paper we focus on the behaviour of eiastomer seals at low temperatures with regard to the potential increase in leakage as material properties of rubbers are strongly temperature-dependent. During continuous cooling, the material behaviour of elastomers changes in the rubber-glass transition temperature ränge from rubberlike entropy-elasticity to stiff energy-elasticity, allowing for almost no strain or retraction. Hence rubbers are normally used above their rubber-glass transition but the minimum limit at which they work has not been defined precisely. For the investigations, fluorocarbon (FKM) and ethylene-propylene-diene (EPDM) rubbers were selected, as they are often used in radioactive waste Containers. The elastomers were studied using several thermoanalytical methods and compression set. The results were compared with component tests to determine the temperature at which the sealing function of O-rings made of eiastomer breaks down. In addition to these results, under static conditions we designed a new measurement set-up which allows for a small deflection of the flange and simultaneous leakage rate measurement at low temperatures.
Elastomeric seals are used in many containers, including casks for radioactive waste. However, like all polymers, elastomers are prone to aging, which leads to a loss of sealing force and the ability for recovery which can ultimately result in leakage. Therefore it is important to be able to define an end-of-lifetime criterion and to judge the lifetime of elastomeric seals. For this reason, we started an aging program on three kinds of rubbers (HNBR, EPDM, FKM), monitoring the change of properties at four different aging temperatures over extended periods up to five years. The measured data is used for lifetime prediction by applying a suitable model.
Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste and for spent fuel transportation casks. In addition, they are also used for spent fuel storage and transportation casks (dual purpose casks (DPC)) as auxiliary seals to allow leakage rate measurements of metal barrier seals for demonstration of their proper assembling conditions. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with regard to mechanical, thermal, and environmental conditions as well as irradiation during the entire operation period. Concerning DPC, degradation effects should be limited in a way that, for example, effects from potentially released decomposition elements may not harm e.g. metal barrier seals. Leakage rate measurements should be possible also after long interim storage periods prior to subsequent transportation.
Because of the complex requirements resulting from the various applications of containers for radioactive waste and spent nuclear fuel, BAM has initiated several test programmes for investigating the behaviour of elastomer seals. In this contribution the current status is described and first results are discussed.
The long time-frame of the necessary safe enclosure of radioactive waste in containers gains interna-tionally an increasing attention. As well extended storage periods as a usually necessary subsequent transportation after storage have to be evaluated.
In Germany, the concept of dry interim storage in dual purpose metal casks before disposal is being pursued for spent nuclear fuel (SNF) and high level waste (HLW) management. The initially planned and established dry interim storage license duration of up to 40 years will be too short and its exten-sion will become necessary since there is no repository available in due time.
The main safety relevant components are the thick-walled dual purpose metal casks. These casks consist e.g. of a monolithic cask body with integrated neutron shielding components (polymers, e.g. polyethylene) and a monitored double lid barrier system equipped with metal and elastomer seals. The metal seals of this bolted closure system guarantee the required leak-tightness whereas the elastomer seals allow for leakage rate measurement of the metal seals.
At BAM we focus on the long-term performance of the sealing system and neutron shielding materials as their application conditions have to be concerned as rather demanding.
Therefore, BAM began to investigate the overall function and long-term behavior of elastomer and metal seals and also the irradiation influence on neutron shielding materials.
Recently a new project was initiated to expand our investigations to get more and in some context better applicable data.
This paper describes the approach of our new research project with the aim of further closure of existing knowledge gaps and presents an overview of investigations concerning the low temperature behavior of elastomer seals, of running long-term tests on elastomer seals at different temperatures under static conditions and the influence of gamma irradiation on neutron shielding materials.
BAM is the federal institute for materials research and testing in Germany. One of our tasks is to evaluate the safety of casks designed for transport and/or storage of radioactive waste. As elastomeric seals are used in the containers as safety-relevant parts, it is our goal to be able to evaluate the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. For this reason, an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) was started. Ageing was performed at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) for up to 2 years. For assessing properties related to the sealability, O-rings were aged in compression by 25 % (corresponding to the compression during service) between plates. For comparison, uncompressed O-rings were aged as well. The aged materials were characterized with conventional polymer analysis methods such as hardness and tensile tests, but also with more seal-specific methods such as compression stress relaxation (CSR, reflecting the loss of sealing force of a compressed seal over time), and compression set (CS, representing the recovery behaviour of a seal after release from compression). CS is chosen as the property for lifetime prediction as it is both sensitive to degradation and related to the seal performance. CS data is extrapolated to 60 °C, which yields lifetimes of approximately 5 years for HNBR and 64 years for EPDM for a criterion of 85 % CS respectively, and approx. 40 years for FKM for a criterion of 65 % CS (the highest value measured so far).
Rubber is widely used as sealing material in various applications. In many fields the function of seal materials at low temperatures is necessary.
Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance.
It is known that the material properties of rubbers are strongly temperature dependent. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling the material changes from rubber-like entropy-elastic behaviour to stiff energy-elastic behaviour, that allows nearly no strain or retraction, due to the glass transition. Hence rubbers are normally used above their glass transition but the minimum working temperature limit is not defined precisely, what can cause problems during application. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties.
In the past we investigated the material properties and sealing behaviour of elastomeric seals at low temperatures. Additionally we started to study the effect of a small partial release of elastomer seals at low temperatures. To study the influence of dynamic events on seal performance and to enhance the understanding of occurring seal failure, a setup for a fast partial seal release was designed.
In this contribution we focus on the correlation of material properties and component behaviour under different application conditions. It is desired to widen the understanding of the process of seal failure at low temperature.
Rubber is widely used as sealing material in various applications. In many fields the function of seal materials at low temperatures is necessary. Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance. It is known that the material properties of rubbers are strongly temperature dependent. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling the material changes from rubber-like entropy-elastic behaviour to stiff energy-elastic behaviour, that allows nearly no strain or retraction, due to the glass transition. Hence rubbers are normally used above their glass transition but the minimum working temperature limit is not defined precisely, what can cause problems during application. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties. In the past we investigated the material properties and sealing behaviour of elastomeric seals at low temperatures. Additionally we started to study the effect of a small partial release of elastomer seals at low temperatures. To study the influence of dynamic events on seal performance and to enhance the understanding of occurring seal failure, a setup for a fast partial seal release was designed. In this contribution we focus on the correlation of material properties and component behaviour under different application conditions. It is desired to widen the understanding of the process of seal failure at low temperature.
At BAM, which is the federal institute for materials research and testing in Germany, it is one of our tasks to evaluate the safety of casks designed for transport and/or storage of radioactive material. This includes assessment of elastomeric seals applied in the containers. Besides examining the low-temperature behaviour and irradiation effects of elastomeric seals, it is our goal to evaluate the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. Therefore, we started an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) which are aged at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) up to 1 year. In order to assess sealability, O-rings are aged in compression by 25 % (corresponding to the compression during service) between plates as well as in flanges that allow leakage rate measurements. For comparison, uncompressed O-rings are aged as well. Further methods characterising seal performance are compression stress relaxation (CSR) reflecting the loss of sealing force of a compressed seal over time, and compression set (CS) which represents the recovery behaviour of a seal after release from compression. Additionally, hardness is measured for information about the change of mechanical properties. The experimental results indicate that while hardness, CSR and CS show considerable degradation effects, the leakage rate stays constant or even decreases until shrinkage and the loss of resilience of the aged seal leads to the formation of a leakage path. This indicates that static leakage rate, which is the only available direct seal performance criterion, has only limited sensitivity for the degradation of the seal material.
Elastomers are widely used as the main sealing materials in Containers for low- and intermediate-level radioactive waste and as an additional component fo metal seals in spent-fuel and high-level waste containers. According to appropriate guidelines and regulations, safe enclosure of the radioactive container contents has to be guaranteed for lengthy storage periods of at least 40 years. Therefore, the understanding of seal ageing behaviour is of high importance and has to be considered with regard to possible dynamic events taking place during transport after storage. An accelerated ageing approach for compressed seals is presented, as well as some first results.
For many sealing applications rubbers are applied due to their special material properties and easy use. In many applications as e.g. in aviation, traffic or process technology the material can be exposed to low temperatures during operation. Therefore, it is important to know the material behaviour at those low temperatures to determine the temperature range that allows a safe operation of the seal.
In this work, we focus on the behaviour of elastomer seals at low temperatures with regard to potential decrease of leak-tightness or catastrophic seal failure of O-ring rubber seals. This is required as material properties of rubbers are strongly temperature dependent but their temperature application range is not always clearly defined.
Based on previous investigations which considered the physical material properties and the seal behaviour under purely static conditions we widen the focus on the sealing performance after a fast partial relief of compressed seals and additional materials.
For the investigations, different typical rubber seal materials were used as e.g. fluorocarbon (FKM), ethylene propylene diene (EPDM) and hydrogenated acrylonitrile-butadiene (HNBR) rubber.
The correlation of the physical material properties with seal performance is studied. This includes as well purely static sealing applications as the Performance during/after fast partial relief of seals at low temperatures.
Einfluss der Alterung auf dichtungsrelevante Eigenschaften von FKM-, VMQ- und EPDM-Elastomeren
(2017)
Da Elastomere in vielfältigen Dichtungsanwendungen eingesetzt werden und dabei teilweise großen Einfluss auf die Funktionsfähigkeit und Sicherheit haben, ist der Einfluss der Alterung auf dichtungsrelevante Eigenschaften relevant. Eine strukturierte Untersuchung des Einflusses von verschiedenen Mischungsrezepturen auf die Bauteileigenschaften, das Alterungsverhalten und die Funktion wird vorgestellt.
For many sealing applications low temperature performance is required. The overall understanding of the relevant influences on low temperature performance of rubber seals are summarized and the currently running investigations described.
The correlation of the physical material properties with seal performance is studied. This includes as well purely static sealing applications as the performance during/after fast partial relief of seals at low temperatures.
Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste. In addition, they are also used in waste fuel storage and transportation casks as auxiliary seals. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with respect to mechanical, thermal and environmental conditions as well as irradiation during the entire operation period. A fundamental understanding of the structure property relationship and their changes during aging can help to evaluate the long-term sealing performance.
In the present study, specific materials are investigated to study the structure-property and seal performance-correlation. Fluoro-elastomer (FKM), silicone rubber (VMQ) and ethylene propylene diene rubber (EPDM) were chosen as base rubbers. Comparable mechanical properties for these seals, especially in terms of a comparable compression behavior were achieved by careful control of base rubber formulation, i.e., by opting for the right filler and its concentration, amount of crosslinking chemicals, and with the assistance of process oils. Moreover, with the same rubber, similar mechanical properties were achieved by varying the filler concentration and crosslinking degree, which shall enable to correlate the particular influence on the structure property dependency of the seals in detail. The materials are investigated under pristine and aged conditions to evaluate the influence of aging, e.g. on the stress relaxation or recovery behavior. These values appear to be suitable parameters to judge the expected sealing performance.
Due to the electrically conducting nature of some fillers used to reinforce rubbers (such as carbon blacks, carbon nanotubes (CNTs), Graphene, etc.) it is possible to obtain current information about mechanical and visco-elastic properties by monitoring the electrical conductivity or resistivity. A simple relation that relates electrical resistance with mechanical stress was derived and the stress values were theoretically predicted from the electrical resistance values, which showed good correlation with experimental results.
In Germany, for the transport and storage of spent nuclear fuel, casks with double closure lid systems are used, which are equipped with Helicoflex® metal seals. The original interim storage period for these casks was planned to be 40 years. However, recent political developments indicate that a storage time of more than 80 years might be necessary. Therefore, the current storage licenses have to be renewed in due course, which requires extended knowledge of the long-term behaviour of all cask components.
At the Bundesanstalt für Materialforschung und -prüfung (BAM), metal seals have been investigated after ageing at temperatures between room temperature and 150 °C for up to 7 years. At regular intervals the seals have been tested for leakage rate as well as for their mechanical behaviour. From these tests pronounced influence of ageing could be shown which results in the decrease of the seal force and the useable resilience. The main reason attributed to these performance changes is the increasing permanent deformation of the outer layer of the seal due to creep. So far, an explicit analytical description of the long-term behaviour that could be used for predictions exceeding the tested ageing times and temperatures was not suitable.
In addition to the component tests that were already conducted, a comprehensive investigation programme has been started to describe the mechanical behaviour of the individual seal components.
The individual seal components are tested regarding different material characteristics including creep, deformation and microstructural properties. The comparability of the material characterization is ensured by comparing the basic raw material of the specimen with the actual component material.
Furthermore, detailed investigations of the time and temperature dependent deformation behaviour are realized by ageing seal segments at multiple temperatures for different periods of time and employing standardized tests.
By analysing the acquired data in combination with the ongoing long-term component tests a dataset for analytical prediction of the long-term behaviour of the seals is intended for an extended period of time under a certain temperature regime.
For many sealing applications rubbers are applied due to their special material properties and easy use. In many applications as e.g. in aviation, traffic or process technology the material can be exposed to low temperatures during operation. Therefore, it is important to know the material behaviour at those low temperatures to determine the temperature range that allows a safe operation of the seal.
In this work, we focus on the behaviour of elastomer seals at low temperatures with regard to potential decrease of leak-tightness or catastrophic seal failure of O-ring rubber seals. This is required as material properties of rubbers are strongly temperature dependent but their temperature application range is not always clearly defined.
Based on previous investigations which considered the physical material properties and the seal behaviour under purely static conditions we widen the focus on the sealing performance after a fast partial relief of compressed seals and additional materials.
For the investigations, different typical rubber seal materials were used as e.g. fluorocarbon (FKM), ethylene propylene diene (EPDM) and hydrogenated acrylonitrile-butadiene (HNBR) rubber.
The correlation of the physical material properties with seal performance is studied. This includes as well purely static sealing applications as the performance during/after fast partial relief of seals at low temperatures.
Aufgrund ihrer einfachen und zuverlässigen Anwendung werden Elastomere für viele Dichtungsaufgaben eingesetzt. In vielen Anwendungsbereichen, wie z.B. Verkehr, Luftfahrt und Verfahrenstechnik, können während des Einsatzes tiefe Temperaturen auftreten, bei denen die Funktionsfähigkeit der Dichtung erhalten bleiben muss. Daher ist die Untersuchung des Verhaltens von Elastomerdichtungen bei tiefen Temperaturen wichtig, um ihren Temperatureinsatzbereich nach unten abzugrenzen und dadurch einen verlässlichen Betrieb zu sichern. Ziel dieser Arbeit ist es, den sicheren Einschluss von gefährlichen Gütern unter verschiedenen Umgebungsbedingungen und über lange Zeiten zu ermöglichen bzw. die Materialauswahl entsprechend zu steuern.
To achieve the required tightness levels of Containers for low and intermediate level radioactive wastes rubbers are widely applied as main sealing materials. The save encapsulation of the radioactive Container contents has to be guaranteed according to legislation and appropriate guidelines for long storage periods as well as down to temperatures of-40 °C during transportation.
Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance.
It is known that the material properties of rubbers are strongly influenced by temperature. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling the material changes from rubber-like entropy-elastic to stiff energy-elastic behaviour, that allows nearly no strain or retraction. Therefore, rubbers are normally used above their glass transition but the minimum working temperature limit is not defrned precisely, what can cause problems during application. The temperature ränge where full functionality is possible is strongly dependent on the application conditions and the material.
For this investigation mainly ethylene propylene diene (EPDM) and fluorocarbon rubbers (FKM) were selected as they are often used for radioactive waste Containers.
Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are typically used for the determination of the temperature ränge of the glass transition process. The standardized compression set measurement according to ISO 815 is common for investigation of rubber sealing materials as the test simulates the seal behaviour after release. To reduce the test time of the Standard tests a faster technique giving the same information was developed.
Additionally, the breakdown temperature of the sealing function of complete O-ring seals is measured in a component test Setup to compare it with the results of the other tests. The experimental Setup is capable of measuring the leakage rate at low temperatures by the pressure rise method.
A model was developed that allows calculating the minimum working temperature limit of a seal by combining the results of the applied methods.
Langzeituntersuchungen an Metalldichtungen mit innen liegendem Federkern und doppelter Ummantelung
(2013)
In Deutschland werden in Transport- und Lagerbehältern (TLB) wärmeentwickelnde radioaktive Abfälle gegenwärtig über einen Zeitraum von bis zu 40 Jahren zwischengelagert. Aufgrund der Situation der noch nicht abgeschlossenen Endlagersuche werden hier möglicherweise Verlängerungen in Betracht zu ziehen sein. Im Deckeldichtsystem der TLB werden in der Regel Metalldichtungen vom Typ Helicoflex® eines französischen Herstellers verwendet, die aus einem innen liegenden Spiralfederkern und zwei Ummantelungen bestehen. Die Ermittlung der Fliess- und Relaxationseigenschaften der Dichtungskomponenten über den vorgesehenen langen Betriebseitraum sind vor dem Hintergrund des Erhalte eines geforderten hohen Dichtniveaus ein wichtiger Untersuchungsgegenstand.