Filtern
Erscheinungsjahr
- 2016 (17) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (7)
- Beitrag zu einem Tagungsband (5)
- Vortrag (5)
Schlagworte
- Degradation (4)
- Aging (3)
- Compression set (3)
- Leakage rate (3)
- Low temperature (3)
- Rubber (3)
- Ageing (2)
- Compression (2)
- Extrapolation (2)
- Neutron shielding (2)
Eingeladener Vortrag
- nein (5)
Rubber is widely used as sealing material in various applications. In many fields the function of seal materials at low temperatures is necessary. Therefore, the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance.
It is known that the material properties of rubbers are strongly temperature dependent. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling, due to the glass transition the material changes from rubber-like entropy-elastic behaviour to stiff energy-elastic behaviour, that allows nearly no strain or retraction. Hence, rubbers are normally used above their glass transition. But as the minimum working temperature limit of elastomers cannot be defined globally and precisely, the lower operation temperature limit of rubber seals should be determined in dependence of the application conditions and the most relevant material properties.
In this paper, wesummarize results of our temperature dependent investigation of seal material properties by classical thermal analysis as Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA), combined with measurements of standardized tests as compression set and the seal performance determined in component tests. To reduce the test time of compression set tests a faster technique was developed and applied.
To study the influence of dynamic events on the seal performance and to enhance the understanding of occurring seal failure, a setup for a fast partial seal release was designed.
Ein wesentliches sicherheitstechnisches Kriterium für Transport und Lagerbehälter ist das Langzeitverhalten von verschraubten Deckel-Dichtsystemen unter Verwendung von Metall- und Elastomerdichtungen sowie von im Behälterkörper integrierten Polyethylenen zur Neutronen¬abschirmung.
Die ordnungsgemäße Funktion der Metalldichtungen ist Voraussetzung für die Einhaltung der geforderten Dichtheit des Deckelsystems, während die Elastomerdichtungen für die Messung der Leckagerate an den Metalldichtungen benötigt werden. Darüber hinaus kommen Elastomer-dichtungen als Primärdichtungen in Behältern für radioaktive Abfälle mit vernachlässigbarer Wärmeentwicklung zum Einsatz.
Zur Bewertung des Dichtungsverhaltens sind die alterungsabhängige verbleibende Rückstellkraft für die Metall- und Elastomerdichtungen sowie die sog. nutzbare Rückfederung bei Metalldichtungen von entscheidender Bedeutung. Für Elastomerdichtungen ist zusätzlich eine radiologisch bedingte Materialdegradation zu bewerten.
In Bezug auf das Alterungsverhalten von Polyethylen zur Neutronenabschirmung sind neben zeit- und temperaturabhängigen Materialveränderungen insbesondere auch durch Gammastrahlung induzierte Degradationseffekte wie Wasserstoffabspaltung, Vernetzung und Abbau der Polymer¬moleküle zu berücksichtigen. Über die eigentliche Bewertung der Abschirmeigenschaften hinaus sind somit zusätzlich Auswirkungen von Degradationsprodukten auf andere Behälterkomponenten zu diskutieren.
Die an der BAM im Fachbereich 3.4 Sicherheit von Lagerbahältern durchgeführten und aktuell laufenden Untersuchungen werden vorgestellt und diskutiert.
Testing and numerical simulation of elastomeric seals under consideration of time dependent effects
(2016)
Due to delays in the siting procedure to establish a deep geological repository for spent nuclear fuel and high level waste and in construction of the already licensed Konrad repository for low and intermediate level waste, extended periods of interim storage will become more relevant in Germany. BAM is involved in most of the cask licensing procedures and is responsible for the evaluation of cask-related long-term safety issues. Elastomeric seals are widely used as barrier seals for containers for low and intermediate level radioactive waste. In addition they are also used as auxiliary seals in spent fuel storage and transportation casks (dual purpose casks (DPC)).
To address the complex requirements resulting from the described applications, BAM has initiated several test programs for investigating the behavior of elastomeric seals. These include experiments concerning the hyperelastic and viscoelastic behavior at different temperatures and strain rates, the low temperature performance down to -40°C, the influence of gamma irradiation and the aging behavior.
The first part of the paper gives an overview of these tests, their relevant results and their possible impact on BAM’s work as a consultant in the framework of approval and licensing procedures.
The second part presents an approach of the development of a finite element model using the finite element code ABAQUS®. The long-term goal is to simulate the complex elastomeric behavior in a complete lid closure system under specific operation and accident conditions.
Both chain scission and crosslinking reactions occur during ageing of EPDM rubber. However, with many conventional polymer analysis methods such as hardness and DMA, it is hardly possible to obtain information about the contribution of each reaction type to the measured data. For example, hardness and Tg both increase during ageing of EPDM, indicating crosslinking during ageing, but it is not clear whether this is partly counterbalanced by chain scission reactions which would lower hardness and Tg. An indication that chain scission reactions probably counteract the hardness or Tg increase by crosslinking is given by Compression Set (CS) measurements. CS exhibits a higher change than hardness or Tg, as CS increases additively through both chain scission and crosslinking reactions. In order to elucidate the share of chain scission reactions in the total degradation, a method testing relaxation and recovery behaviour using DMA equipment was applied. The method revealed the strong influence of chain scissions, leading to more pronounced relaxation and higher residual strain after compression.
Polymer Testing - Editorial
(2016)
Polymer Testing - Editorial
(2016)
Rubber is widely used as sealing material in various applications. In many fields the function of seal materials at low temperatures is necessary.
Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance.
It is known that the material properties of rubbers are strongly temperature dependent. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling the material changes from rubber-like entropy-elastic behaviour to stiff energy-elastic behaviour, that allows nearly no strain or retraction, due to the glass transition. Hence rubbers are normally used above their glass transition but the minimum working temperature limit is not defined precisely, what can cause problems during application. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties.
In the past we investigated the material properties and sealing behaviour of elastomeric seals at low temperatures. Additionally we started to study the effect of a small partial release of elastomer seals at low temperatures. To study the influence of dynamic events on seal performance and to enhance the understanding of occurring seal failure, a setup for a fast partial seal release was designed.
In this contribution we focus on the correlation of material properties and component behaviour under different application conditions. It is desired to widen the understanding of the process of seal failure at low temperature.
Rubber is widely used as sealing material in various applications. In many fields the function of seal materials at low temperatures is necessary. Therefore the understanding of failure mechanisms that lead to leakage at low temperatures is of high importance. It is known that the material properties of rubbers are strongly temperature dependent. At low temperatures this is caused by the rubber-glass transition (abbr. glass transition). During continuous cooling the material changes from rubber-like entropy-elastic behaviour to stiff energy-elastic behaviour, that allows nearly no strain or retraction, due to the glass transition. Hence rubbers are normally used above their glass transition but the minimum working temperature limit is not defined precisely, what can cause problems during application. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties. In the past we investigated the material properties and sealing behaviour of elastomeric seals at low temperatures. Additionally we started to study the effect of a small partial release of elastomer seals at low temperatures. To study the influence of dynamic events on seal performance and to enhance the understanding of occurring seal failure, a setup for a fast partial seal release was designed. In this contribution we focus on the correlation of material properties and component behaviour under different application conditions. It is desired to widen the understanding of the process of seal failure at low temperature.
The long time-frame of the necessary safe enclosure of radioactive waste in containers gains interna-tionally an increasing attention. As well extended storage periods as a usually necessary subsequent transportation after storage have to be evaluated.
In Germany, the concept of dry interim storage in dual purpose metal casks before disposal is being pursued for spent nuclear fuel (SNF) and high level waste (HLW) management. The initially planned and established dry interim storage license duration of up to 40 years will be too short and its exten-sion will become necessary since there is no repository available in due time.
The main safety relevant components are the thick-walled dual purpose metal casks. These casks consist e.g. of a monolithic cask body with integrated neutron shielding components (polymers, e.g. polyethylene) and a monitored double lid barrier system equipped with metal and elastomer seals. The metal seals of this bolted closure system guarantee the required leak-tightness whereas the elastomer seals allow for leakage rate measurement of the metal seals.
At BAM we focus on the long-term performance of the sealing system and neutron shielding materials as their application conditions have to be concerned as rather demanding.
Therefore, BAM began to investigate the overall function and long-term behavior of elastomer and metal seals and also the irradiation influence on neutron shielding materials.
Recently a new project was initiated to expand our investigations to get more and in some context better applicable data.
This paper describes the approach of our new research project with the aim of further closure of existing knowledge gaps and presents an overview of investigations concerning the low temperature behavior of elastomer seals, of running long-term tests on elastomer seals at different temperatures under static conditions and the influence of gamma irradiation on neutron shielding materials.
As a Federal institute for materials research and testing it is part of our tasks to evaluate the safety of casks designed for transport and/or storage of radioactive material. This includes the investigation of elastomeric seals and polymeric neutron shielding materials used in the containers.
In this contribution we would like to present our research focused on the long term performance and associated changes of material properties of elastomeric seals (e.g. EPDM, FKM) and neutron shielding materials ((Ultra) High Molecular Weight Polyethylene) employed in storage casks. Our approach comprises accelerated ageing investigations at elevated temperatures and to some extent investigations of irradiated materials.
As the requirements for the extended use of cables in nuclear power plants and for the long term use of cask components are to a certain extent similar, our work might be of interest for the workshop on “Cables ageing in nuclear power plants; R&D current status and forecast”.
The cure behaviour of a specific ethylene vinyl acetate material as used for encapsulation of photovoltaic modules was analysed by rheometer, differential scanning calorimetry and Fourier transform infrared spectroscopy to test for a suitable replacement for the laborious determination of gel content. The results show that all applied methods are capable of describing the effects of the cross-linking process. Some provide results very similar to those yielded by analysis of the insoluble content, but the question remains as to whether indirect methods should be preferred over the direct measurement of physical properties, e.g. as performed by the curemeter. A material stored for one year was also tested to demonstrate the effect of extended storage on cure behaviour and how this is detected by different methods. This complements the other methods, which were clearly able to detect the different cure behaviour of the aged EVA, whereas determination of the gel content could not.
At BAM, which is the federal institute for materials research and testing in Germany, it is one of our tasks to evaluate the safety of casks designed for transport and/or storage of radioactive material. This includes assessment of elastomeric seals applied in the containers. Besides examining the low-temperature behaviour and irradiation effects of elastomeric seals, it is our goal to evaluate the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. Therefore, we started an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) which are aged at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) up to 1 year. In order to assess sealability, O-rings are aged in compression by 25 % (corresponding to the compression during service) between plates as well as in flanges that allow leakage rate measurements. For comparison, uncompressed O-rings are aged as well. Further methods characterising seal performance are compression stress relaxation (CSR) reflecting the loss of sealing force of a compressed seal over time, and compression set (CS) which represents the recovery behaviour of a seal after release from compression. Additionally, hardness is measured for information about the change of mechanical properties. The experimental results indicate that while hardness, CSR and CS show considerable degradation effects, the leakage rate stays constant or even decreases until shrinkage and the loss of resilience of the aged seal leads to the formation of a leakage path. This indicates that static leakage rate, which is the only available direct seal performance criterion, has only limited sensitivity for the degradation of the seal material.
Seals used in containers for dangerous goods need to maintain leak tightness for several decades. For investigating the change in seal material properties during aging, a comprehensive aging program on both uncompressed and compressed EPDM and HNBR seals was started. In order to obtain results closely related to practical conditions, O-rings with a full-scale cord diameter of 10 mm were aged. However, this set-up can lead to heterogeneous aging caused by diffusion-limited oxidation (DLO) effects. These effects depend on material, dimensions, time and temperature. Heterogeneous aging results in distorted bulk properties such as compression stress relaxation and compression set (CS) suggesting that HNBR has better performance than EPDM at 150 °C but which is not the case at 100 °C. The presence of heterogeneous material properties was shown by hardness measurements across the seal cross-section. If DLO-affected data is excluded, extrapolations of CS data are possible using time-temperature shifts and Arrhenius graphs. Exemplary CS values of 50 % and 80 % would be reached after approx. 10 years and 29 years, respectively for HNBR and after approx. 400 years and 1100 years, respectively for EPDM.
The properties of the encapsulant are critical to the long-term performance of photovoltaic (PV) modules under the influence of sunlight including UV, elevated temperature, humidity and diffusion of oxygen. Encapsulation process represents a bout 40% of the whole PV module cost. The introduction of new non-EVA encapsulant material type "Low-Cost, High-Performance" should provide a solution to outdoor yellowing degradation problems. The emerging encapsulant materials exhibit a good compatibility with emerging PV solar cells for long term durability. This new generation of encapsulant materials has the advantage to improve e the PV module performances and long term durability for specific climate like desert regions. This scientific contribution presents an overview of the different encapsulant materials currently on the market, the general requirements of the emerging encapsulant materials and characterizations techniques for degradation, diagnostic and reliability lifetime estimation in the framework of Algerian renewable energy strategy.
The properties of the encapsulant are critical to the long-term performance of photovoltaic (PV) modules under the influence of sunlight including UV, elevated temperature, humidity and diffusion of oxygen. Encapsulation process represents about 40% of the whole PV module cost. The introduction of new non-EVA encapsulant material type “Low-Cost, High-Performance” should provide a solution to outdoor yellowing degradation problems. The emerging encapsulant materials exhibit a good compatibility with emerging PV solar cells for long term durability. This new generation of encapsulant materials has the advantage to improve the PV module performances and long term durability for specific climate like desert regions. This scientific contribution presents an overview of the different encapsulant materials currently on the market, the general requirements of the emerging encapsulant materials and characterizations techniques for degradation, diagnostic and reliability lifetime estimation in the framework of Algerian renewable energy strategy.
HNBR, EPDM and FKM O-rings were aged uncompressed and compressed at 75 °C, 100 °C, 125 °C and 150 °C for up to 1 year. HNBR exhibited the strongest ageing effects with high increases of hardness and glass transition temperature. Furthermore, heterogeneous ageing caused by diffusion-limited oxidation effects had a significant influence for HNBR at ageing temperatures of 125 °C and 150 °C. EPDM showed similar property changes as HNBR, but less pronounced. FKM displayed only minor ageing effects. O-rings aged in compression exhibited considerable compression set (CS). CS data was used for a time-temperature shift and resulting master curve construction. Leakage rate measurements showed that O-rings can remain leak tight under static conditions even if material properties have already deteriorated strongly.
BAM is the federal institute for materials research and testing in Germany. One of our tasks is to evaluate the safety of casks designed for transport and/or storage of radioactive waste. As elastomeric seals are used in the containers as safety-relevant parts, it is our goal to be able to evaluate the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. For this reason, an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) was started. Ageing was performed at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) for up to 2 years. For assessing properties related to the sealability, O-rings were aged in compression by 25 % (corresponding to the compression during service) between plates. For comparison, uncompressed O-rings were aged as well. The aged materials were characterized with conventional polymer analysis methods such as hardness and tensile tests, but also with more seal-specific methods such as compression stress relaxation (CSR, reflecting the loss of sealing force of a compressed seal over time), and compression set (CS, representing the recovery behaviour of a seal after release from compression). CS is chosen as the property for lifetime prediction as it is both sensitive to degradation and related to the seal performance. CS data is extrapolated to 60 °C, which yields lifetimes of approximately 5 years for HNBR and 64 years for EPDM for a criterion of 85 % CS respectively, and approx. 40 years for FKM for a criterion of 65 % CS (the highest value measured so far).