- Colour center (1)
- EVA (1)
- Incoming goods control (1)
- Insoluble content (1)
- Irradiation (1)
- Photovoltaic cell encapsulation (1)
- Rheometer (1)
- UHMWPE (1)
- Yellowness index (1)
The cure behaviour of a specific ethylene vinyl acetate material as used for encapsulation of photovoltaic modules was analysed by rheometer, differential scanning calorimetry and Fourier transform infrared spectroscopy to test for a suitable replacement for the laborious determination of gel content. The results show that all applied methods are capable of describing the effects of the cross-linking process. Some provide results very similar to those yielded by analysis of the insoluble content, but the question remains as to whether indirect methods should be preferred over the direct measurement of physical properties, e.g. as performed by the curemeter. A material stored for one year was also tested to demonstrate the effect of extended storage on cure behaviour and how this is detected by different methods. This complements the other methods, which were clearly able to detect the different cure behaviour of the aged EVA, whereas determination of the gel content could not.
Discoloration Effects of High-Dose gamma-Irradiation and Long-Term Thermal Aging of (U) HMW-PE
(2017)
Two polyethylene types with ultra-high (UHMWPE) and high molecular weight (HMW-PE) used as neutron radiation shielding materials in casks for radioactive waste were irradiated with doses up to 600 kGy using a 60Co gammasource. Subsequently, thermal aging at 125∘C was applied for up to one year. Degradation effects in the materials were characterized using colorimetry, UV-Visspectroscopy, IR spectroscopy, and DSC. Both materials exhibited a yellowing upon irradiation.The discoloration of UHMW-PE disappeared again after thermal aging.Therefore, the yellowing is assumed to originate fromannealable color centers in the formof free radicals that are trapped in the crystalline regions of the polymer and recombine at elevated temperatures. For the antioxidantcontaining HMWPE, yellowing was observed after both irradiation and thermal aging. The color change was correlated mainly to decomposition products of the antioxidant in addition to trapped radicals as in UHMW-PE. Additionally, black spots appeared after thermal aging of HMW-PE.