EVA is a widely used material for the encapsulation of photovoltaic modules. It melts at elevated temperatures, and seals the module before it is crosslinked at temperatures above 130 °C by a peroxide-initiated crosslinking reaction. EVA has good optical properties necessary for application in solar modules. For process optimization and quality management, a method for the quick and reliable characterization of EVA crosslinking behaviour is of great value. Here, the practicability of ultrasound for online crosslinking monitoring is demonstrated. A sound velocity increase of about 8 m/s during the crosslinking reaction is found. The ultrasound results are compared with rheometer measurements performed with a curemeter typically used for the investigation of rubber crosslinking.
Carbon fibre prepregs have found widespread application in lightweight constructions. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. DMA measurements under temperature conditions similar to an autoclave programme were carried out using commercially available prepreg material with a high glass transition temperature. The characteristic of the temperature programme was a dynamic heating segment at 1.5 K/min followed by a longer isothermal segment at 180 °C. The courses of the storage modulus E', loss modulus E'' and tanδ were recorded. The measuring frequency was varied between 1 Hz and 33.3 Hz. Gelation and vitrification are assigned. The influence of the measuring frequency on the time to vitrification and the correlation with DSC are discussed. The reaction does not end even after 10 h curing at 180 °C, which is interpreted as the slow cessation of the reaction caused by vitrification.
Thermoanalytische Charakterisierung von Ethylen-Vinylacetat-Copolymer (EVA) für Photovoltaikmodule
(2011)
Das Ziel der Untersuchungen war mit Hilfe von DSC und DMA EVA-Folien im Anlieferungszustand hinsichtlich der Lage der Glasübergangstemperatur, des Schmelzverhaltens und der Temperaturabhängigkeit der Vernetzungsreaktion zu charakterisieren. Auf dieser Basis sollte die Lieferstabilität im Sinne einer Wareneingangskontrolle auf eine messtechnische Basis gestellt werden. In einem 2. Schritt sollte die vernetzte Folie dahingehend charakterisiert werden, ob infolge der Vernetzung eine Änderung der
Carbon-fibre prepregs have found widespread use in lightweight applications. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. Prepreg materials are generally pre-cured so that they have a higher molecular weight than typical resins in order to reduce resin flow, which facilitates storage and later processing properties.
The measurements were carried out using commercially available materials and follow the published DMA investigations of the same material. TMDSC was used to find the correlation between curing conditions, the degree of cure and glass transition temperature. TMDSC has the advantage over standard DSC that it enables better determination of the glass transition temperature, which is often accompanied by an exothermic curing reaction, and thus overshadowed. The influence of the amplitude of temperature modulation was tested in preliminary experiments. For non-cured material a glass transition temperature of approximately 0 °C was determined; whereas for the totally cured material it was approximately 230 °C. The changes in degree of cure, temperature of actual glass transition and post-reaction are given as a function of curing time at 180 °C. The correlation between actual glass transition temperature and degree of cure is derived.
Two types of commercially applied Ethylene/Vinyl Acetate Copolymers (EVA) for encapsulation of photovoltaic modules were investigated by the thermal analysis methods of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) in the temperature range from -150 °C to 200 °C. Glass transition, crystal melting and cross-linking were analyzed. The aims of the investigations were to gain more information for incoming goods control and to get information about the whole temperature dependent material properties in the investigated temperature range, starting at very low temperatures up to the crosslinking temperature region.