Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (37)
- Beitrag zu einem Tagungsband (11)
- Buchkapitel (1)
Referierte Publikation
- ja (49) (entfernen)
Schlagworte
- Compression set (12)
- Elastomer (8)
- Ageing (7)
- Rubber (6)
- Low temperature behaviour (5)
- Sealing material (5)
- DMA (4)
- DSC (4)
- Glass transition (4)
- Leakage rate (4)
Organisationseinheit der BAM
Paper des Monats
- ja (1)
Monitoring the vulcanization of elastomers: Comparison of curemeter and ultrasonic online control
(2009)
The vulcanization of elastomeric materials has a high impact on the properties of the final product. Therefore, it is important to monitor and control this crosslinking process. A common technique to attain the necessary curing time is the use of a curemeter in accordance with ISO 6502 in order to determine the time for full cure of a sample with a standardized geometry. Based on this result and a lot of practical experience, the required curing time for a given product geometry is estimated. Within the scope of this work, a new analysis technique will be compared with the standard procedure. The ultrasonic online control employs ultrasound waves to measure the changes in material properties caused by vulcanization. For this study, a natural rubber compound with a conventional curing system was investigated by both techniques. It was found that the results of the ultrasonic technique show good agreement with the results of the curemeter.
In consideration of the influence of the curing reaction on the material properties of elastomers, it is very important to control the vulcanization process properly.
As shown previously [1], the effects of the vulcanization reaction of an elastomer can be monitored by use of ultrasonic sound waves. This technique has to a certain degree a high similarity to the standard curemeter test according to ISO 6502 but can be applied also inside a production tool.
So far, the method was only applied to the vulcanization of one compound at a given temperature and sample thickness. This is now complemented with measurements on another compound system at different temperatures and sample thicknesses.
The expected effects of temperature and thickness on the curing behaviour were found by use of the ultrasound online control.
Über die in der Technik weit verbreitete typisierte Harnstoffformmasse UF 131.5, ein Aminoplast, wird berichtet, dass sie im Zuge der thermisch aktivierten Vernetzungsreaktion wegen "Überhärtung" mangelhafte Eigenschaften annimmt. Zur Verifizierung dieses Effektes werden mithilfe der Ultraschall-Prozesskontrolle gezielt Proben unterschiedlicher Aushärtegrade hergestellt. Sie werden mit verschiedenen Methoden, wie der "Kochprobe" und der Thermoanalyse, charakterisiert und auf ihre Materialeigenschaften untersucht. Dabei zeigt sich ein deutlicher Einfluss der Härtezeit auf die Glasübergangstemperatur der Formmasse. In den mechanischen Eigenschaften ist eine Veränderung allerdings nur in der Schlagzähigkeit festzustellen, die sich mit steigender Härtezeit sogar wesentlich verbessert.
A new method for the evaluation of the low temperature properties of rubber materials is presented. The method emulates the standardized compression set measurement, which is frequently used for sealing materials, but can be performed within a considerably shorter time. The results are compared with the standard test and found to be qualitatively the same. Slight differences are discussed on the basis of the differences in the measurement procedures. Further data evaluation is done by fitting functions to describe the material behaviour.
Two types of commercially applied Ethylene/Vinyl Acetate Copolymers (EVA) for encapsulation of photovoltaic modules were investigated by the thermal analysis methods of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) in the temperature range from -150 °C to 200 °C. Glass transition, crystal melting and cross-linking were analyzed. The aims of the investigations were to gain more information for incoming goods control and to get information about the whole temperature dependent material properties in the investigated temperature range, starting at very low temperatures up to the crosslinking temperature region.
Rubber is widely used as sealing material in various applications. In many fields the sealing function at low temperatures is necessary. Therefore the understanding of failure mechanisms is of high importance. Rubbers are normally used above their glass-rubber transition region but the minimum working temperature limit is not defined precisely. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties. The results of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are combined with the results of the standardized compression set according to ISO 815 respectively a modified test using the DMA equipment.
EVA is a widely used material for the encapsulation of photovoltaic modules. It melts at elevated temperatures, and seals the module before it is crosslinked at temperatures above 130 °C by a peroxide-initiated crosslinking reaction. EVA has good optical properties necessary for application in solar modules. For process optimization and quality management, a method for the quick and reliable characterization of EVA crosslinking behaviour is of great value. Here, the practicability of ultrasound for online crosslinking monitoring is demonstrated. A sound velocity increase of about 8 m/s during the crosslinking reaction is found. The ultrasound results are compared with rheometer measurements performed with a curemeter typically used for the investigation of rubber crosslinking.
The method for the determination of compression set values with a Dynamic Mechanical Analysis (DMA) setup at low temperatures, which was presented previously, allows a much faster and readily automated procedure than the standardized compression set test according to ISO 815-2. This method is applied to a series of different elastomeric materials that are commonly used for sealing applications. The results of the compression set test are compared with results from thermal analysis to allow an in depth comparison of the material behaviour at low temperatures.
Furthermore, a comparison between two EPDM materials is presented. These materials show very similar properties determined by thermo analytical methods such as Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) but differ clearly in their compression set behaviour. This comparison shows the importance and value of information of the compression set test in addition to thermal analysis to judge the behaviour of sealing materials and confirms the relevance of the new compression set test method for the investigation of low temperature properties of elastomers.
Fracture mechanics approaches are increasingly applied for the characterization of epoxy resin and adhesive mechanical properties. Therefore, the fracture toughness and crack resistance under static load ISO 13586 [1] are often regarded as state of the art to analyse material improvements. However, experimental investigations on fatigue behaviour, thus the crack propagation according to ISO 15850 [2], seem to be much more sensitive to characterize the materials for in service loading conditions. Firstly, an efficient testing concept was developed at BAM. In this framework, the geometry for a modified single edge notched tensile specimen (SET) was developed in order to assure appropriate resolution in measuring the crack length via a CCD-camera [3]. In the next step, the influence of the cure temperature on the fracture-mechanical properties was investigated.
Partial discharges may cause damage to electrical insulation of high voltage equipment. They initiate elastic waves in the insulating material, e.g. in the stress cone of an outdoor termination. Localisation of the origin of such elastic waves can help to predict serious damaging processes in the electrical insulation. In order to measure and evaluate the wave propagation effects in typical multilayered elastomeric structures, knowledge of the material properties is required. The propagating velocity and the attenuation of longitudinal waves are important parameters. Values for these quantities found in the literature were not appropriate. Therefore, for cross-linked polyethylene (XLPE) and cured liquid silicone rubber (LSR), the longitudinal wave velocity and the attenuation were evaluated in the temperature interval from -20°C to 50°C and in the frequency range from 200 kHz to 600 kHz using a two-sample ultrasound technique. The loss factor was determined from these measured quantities. Additionally, low frequency Dynamic Mechanical Thermal Analysis (DMTA) was applied to investigate LSR and XLPE in a temperature interval between -100 and 50°C and to check qualitatively the ultrasound data.