Schlagworte
- Active thermography (4)
- DMD (3)
- Thermal waves (2)
- Automotive industry (1)
- Crack detection (1)
- Cracks (1)
- DMD coupled laser (1)
- Elevated temperatures (1)
- FEM (1)
- FEM simulation (1)
The detection and characterization of surface cracks in steel specimens prior to damage is a technologically and economically highly significant task and is of utmost importance when it comes to safety-relevant structures. In steel production where steel billets at high temperatures have to be inspected while moving a number of well-established NDT methods cannot be applied. Laser thermography however is a promising candidate to serve as a fast, non-contact and remote tool in this case. We present a study that shows that the crack detection capabilities of laser thermography can be extended also to specimens at high temperature. A combination of inductive and laser heating allows to systematically study the contrast formation as well as the optimization of the important measurement parameters. The experiments are accompanied by FEM simulations that provide a better insight of the physical correlations and support the experimental developments. The aim of these studies is to develop a system with high inspection speed and detection performance to be in-line operated under the hostile environment of steel production lines.
In-line laser thermography for crack detection at elevated temperature: A Numerical modeling study
(2016)
The detection and characterization of cracks prior to damage is a technologically and economically highly significant task and is of very importance when it comes to safety-relevant structures. The evaluation of a components life is closely related to the presence of cracks in it. Laser thermography has already high capability for the detection of surface cracks and for the characterization of the geometry of artificial surface flaws in metallic samples. Crack detection in metallic samples at high temperature is highly significant in present manufacturing scenario. During the casting process of billets, surface cracks form, due to the suboptimal cooling rates. These cracks reduce value of the billet and must be removed using machining process after cooling. This secondary process increases cost of manufacturing. In this work we developed a heat transfer model for laser thermography to study the thermal contrast variation with increase in surface temperature using finite element method (FEM). Here we are mainly concentrating the capability of the scanning laser thermography in crack detection which are in elevated temperature and numerical modeling study of thermal contrast variation of crack with respect increase in metal surface temperature. This study is important to prove the capability of laser thermography for crack detection in elevated temperature. Since we are using High power CW Laser to local heating of the metal surface which can give relatively high thermal contrast even at elevated temperature compare to other heating source. Here we are modeled and simulated 2D laser scanning across a surface breaking crack and developed an algorithm to produce the vicinity of crack. The algorithm we developed applied for various surface temperature data. And validated the credibility of the algorithm with experimental data.
Spatial and temporal control of thermal waves by using DMDs for interference based crack detection
(2016)
Active Thermography is a well-established non-destructive testing method and used to detect cracks, voids or material inhomogeneities. It is based on applying thermal energy to a samples’ surface whereas inner defects alter the nonstationary heat flow. Conventional excitation of a sample is hereby done spatially, either planar (e.g. using a lamp) or local (e.g. using a focused laser) and temporally, either pulsed or periodical. In this work we combine a high power laser with a Digital Micromirror Device (DMD) allowing us to merge all degrees of freedom to a spatially and temporally controlled heat source. This enables us to exploit the possibilities of coherent thermal wave shaping. Exciting periodically while controlling at the same time phase and amplitude of the illumination source induces – via Absorption at the sample’s surface - a defined thermal wave propagation through a sample. That means thermal waves can be controlled almost like acoustical or optical waves. However, in contrast to optical or acoustical waves, thermal waves are highly damped due to the diffusive character of the thermal heat flow and therefore limited in penetration depth in relation to the achievable resolution. Nevertheless, the coherence length of thermal waves can be chosen in the mmrange for modulation frequencies below 10 Hz which is perfectly met by DMD technology. This approach gives us the opportunity to transfer known technologies from wave shaping techniques to thermography methods. We will present experiments on spatial and temporal wave shaping, demonstrating interference based crack detection.
Spot welding is one of the most important joining technologies, especially in the automotive industry. Hitherto,the quality of spot welded joints is tested mainly by random destructive tests. A nondestructive testing technique offers the benefit of cost reduction of the testing procedure and optimization of the fabrication process, because every joint could be examined. This would lead to a reduced number of spot welded joints, as redundancies could be avoided. In the procedure described here, the spot welded joint between two zinc-coated steel sheets (HX340LAD+Z100MB or HC340LA+ZE 50/50) is heated optically on one side. Laser radiation and flash light are used as heat sources. The melted zone, the so called “weld nugget” provides the mechanical stability of the connection, but also constitutes a thermal bridge between the sheets. Due to the better thermal contact, the spot welded joint reveals a thermal behavior different from the surrounding material, where the heat transfer between the two sheets is much lower. The difference in the transient thermal behavior is measured with time resolved thermography. Hence, the size of the thermal contact between the two sheets is determined, which is directly correlated to the size of the weld nugget, indicating the quality of the spot weld. The method performs well in transmission with laser radiation and flash light. With laser radiation, it works even in reflection geometry, thus offering the possibility of testing with just one-sided accessibility. By using heating with collimated laser radiation, not only contactfree, but also remote testing is feasible. A further convenience compared to similar thermographic approaches is the applicability on bare steel sheets without any optical coating for emissivity correction. For this purpose, a proper way of emissivity correction was established.
The coherent superposition of two anti-phased thermal wave fields creates a zone of destructive interference which is extremely sensitive to the presence of defects without any reference measurements.
Combining a high power laser with a spatial light modulator allows modulating phase and amplitude of an illuminated surface that induces spatially and temporally controlled thermal wave fields. The position and depth of defects are reconstructed from analysis of the Amplitude and Phase of the resulting photothermal signal. The proposed concept is experimentally validated and supported by numerical modeling.
For the last 20 years active thermography has developed into a standard method in non-destructive material testing. It has become possible to detect defects such as cracks, voids, or even material inhomogeneities. Until now, it is still difficult to quantify subsurface or hidden defects in size due to the diffusive nature of heat flow within a solid. Facing this issue, lockin thermography and other photothermal techniques have been established. They are based on exciting a sample periodically (e.g. with a halogen lamp), causing a controlled periodical heat flow and thereby representing strongly damped thermal waves. These techniques make use of interference and reflection of thermal waves which allow enhancing depth resolution.
So far, only the temporal component of the light source was modified to achieve a defined vertical heat flow – In contrast, we propose a novel technique in which we are able to control both: time and space. This technique enables us to exploit the possibilities of coherent thermal wave shaping. We achieve that by combining a spatial light modulator (SLM) with a high power laser. This approach allows us to launch a set of individually controlled and fully coherent high energy thermal waves into the sample volume. That means, we intentionally use wave propagation throughout the sample’s material in both - vertical and lateral direction. As one possible application, we use a thermal waves’ interference effect of two phase shifted wave patterns to detect the position of hidden defects. The wave patterns are positioned with a certain distance and a 180° phase shift to each other creating an amplitude depletion zone right in the middle of the two patterns. When a defect is brought unsymmetrically into the depletion zone, the lateral heat flow is disturbed. If the sample is now moved through the depletion zone, a defect can be easily characterized. Exciting periodically while controlling simultaneously phase and amplitude enables us to have a defined thermal wave propagation throughout the sample which means thermal waves can be controlled almost like acoustical or optical waves. This offers the opportunity to transfer known technologies from wave shaping techniques to thermography methods.
The method described here allows to determine the size of the thermal contact between two metal sheets joined by spot welding. This size is a measure for the size of the weld nugget, i.e. the zone melted during the welding process, and thus the quality of the welded joint. The method applies active thermography in transmission or reflection setup. Especially the reflection setup offers an attractive possibility for non-destructive testing when components can be accessed from one side only. The spot weld region is optically heated by laser or flash light radiation. The weld nugget provides the mechanical joint, but also constitutes a thermal bridge between the two welded sheets. The latter will be exploited in this method. The better thermal contact at the weld Nugget contrasts with the surrounding material, where the heat transfer between the two sheets is comparatively low. A major advantage of the described method is the applicability on sheets without any surface treatment. This is achieved by a proper normalization of the data, allowing for a correction of the varying surface emissivity.