Due to the diffusive nature of heat propagation in solids, the detection and resolution of internal defects with active thermography based non-destructive testing is commonly limited to a defect-depth-to-defect-size ratio greater than or equal to one. In the more recent past, we have already demonstrated that this limitation can be overcome by using a spatially modulated illumination source and photothermal super resolution-based reconstruction. Furthermore, by relying on compressed sensing and computational imaging methods we were able to significantly reduce the experimental complexity to make the method viable for investigating larger regions of interest. In this work we share our progress on improving the defect/inhomogeneity characterization using fully 2D spatially structured illumination patterns instead of scanning with a single laser spot. The experimental approach is based on the repeated blind pseudo-random illumination using modern projector technology and a high-power laser. In the subsequent post-processing, several measurements are then combined by taking advantage of the joint sparsity of the defects within the sample applying 2D-photothermal super resolution reconstruction. Here, enhanced nonlinear convex optimization techniques are utilized for solving the underlying ill-determined inverse problem for typical simple defect geometries. As a result, a higher resolution defect/inhomogeneity map can be obtained at a fraction of the measurement time previously needed.
Among the photothermal methods, full-field thermal imaging is used to characterize materials, to determine thicknesses of layers, or to find inhomogeneities such as voids or cracks. The use of classical light sources such as flash lamps (impulse heating) or halogen lamps (modulated heating) led to a variety of nondestructive testing methods, in particular, lock-in and flash-thermography. In vertical-cavity surface-emitting lasers (VCSELs), laser light is emitted perpendicularly to the surface with a symmetrical beam profile. Due to the vertical structure, they can be arranged in large arrays of many thousands of individual lasers, which allows power scaling into the kilowatt range. Recently, a high-power yet very compact version of such a VCSEL-array became available that offers both the fast timing behavior of a laser as well as the large illumination area of a lamp. Moreover, it allows a spatial and temporal control of the heating because individual parts of the array can be controlled arbitrarily in frequency, amplitude, and phase. In conjunction with a fast infrared camera, such structured heating opens up a field of novel thermal imaging and testing methods. As a first demonstration of this approach, we chose a testing problem very challenging to conventional thermal infrared testing: The detection of very thin subsurface defects perpendicularly oriented to the surface of metallic samples. First, we generate destructively interfering thermal wave fields, which are then affected by the presence of defects within their reach. It turned out that this technique allows highly sensitive detection of subsurface defects down to depths in excess of the usual thermographic rule of thumb, with no need for a reference or surface preparation.
Active thermography as a nondestructive testing modality suffers greatly from the limitations imposed by the diffusive nature of heat conduction in solids. As a rule of thumb, the detection and resolution of internal defects/inhomogeneities is limited to a defect depth to defect size ratio greater than or equal to one. Earlier, we demonstrated that this classical limit can be overcome for 1D and 2D defect geometries by using photothermal laser-scanning super resolution. In this work we report a new experimental approach using 2D spatially structured illumination patterns in conjunction with compressed sensing and computational imaging methods to significantly decrease the experimental complexity and make the method viable for investigating larger regions of interest.
We present a systematic study on the performance of laser-thermography for the detection of surface cracks in metallic components. Scanning a metallic surface with laser causes local heating that is mapped simultaneously by an IR-camera and allows identifying cracks with sub-µm openings. The detectability, however, depends on a number of acquisition parameters (e.g. scanning speed, laser power, IR-camera resolution) that typically relate on each other. Most importantly, the detection-sensitivity of surface breaking cracks is given by a particular combination for the acquisition parameter values. As a result, this sensitivity is adaptable within wide ranges allowing the detection of cracks with openings ranging from 200 to 0.1 µm at testing speeds of 100 to 0.05 cm²/s. By examining artificial as well as fatigue cracks, we demonstrate that the method can be even applied to shiny surfaces with no need of pretreatments, which makes it an entirely contactless, remote and automatable NDT technique. A comparison with magnetic particle testing shows that laser-thermography has the potential to become a strong competitor to conventional surface inspection methods in the future.
In-line laser thermography for crack detection at elevated temperature: A Numerical modeling study
(2016)
The detection and characterization of cracks prior to damage is a technologically and economically highly significant task and is of very importance when it comes to safety-relevant structures. The evaluation of a components life is closely related to the presence of cracks in it. Laser thermography has already high capability for the detection of surface cracks and for the characterization of the geometry of artificial surface flaws in metallic samples. Crack detection in metallic samples at high temperature is highly significant in present manufacturing scenario. During the casting process of billets, surface cracks form, due to the suboptimal cooling rates. These cracks reduce value of the billet and must be removed using machining process after cooling. This secondary process increases cost of manufacturing. In this work we developed a heat transfer model for laser thermography to study the thermal contrast variation with increase in surface temperature using finite element method (FEM). Here we are mainly concentrating the capability of the scanning laser thermography in crack detection which are in elevated temperature and numerical modeling study of thermal contrast variation of crack with respect increase in metal surface temperature. This study is important to prove the capability of laser thermography for crack detection in elevated temperature. Since we are using High power CW Laser to local heating of the metal surface which can give relatively high thermal contrast even at elevated temperature compare to other heating source. Here we are modeled and simulated 2D laser scanning across a surface breaking crack and developed an algorithm to produce the vicinity of crack. The algorithm we developed applied for various surface temperature data. And validated the credibility of the algorithm with experimental data.
Thermographic super-resolution techniques allow the resolution of defects/inhomogeneities beyond the classical limit, which is governed by the diffusion properties of thermal wave propagation. Photothermal super-resolution is based on a combination of an experimental scanning strategy and a numerical optimization which has been proven to be superior to standard thermographic methods in the case of 1D linear defects. In this contribution, we report on the extension of this approach towards a full frame 2D photothermal super-resolution technique. The experimental approach is based on a repeated spatially structured heating using high power lasers. In a second post-processing step, several measurements are coherently combined using mathematical optimization and taking advantage of the (joint) sparsity of the defects in the sample. In our work we extend the possibilities of the method to efficiently detect and resolve defect cross sections with a fully 2D-structured blind illumination.
Using an infrared camera for radiometric imaging allows the contactless temperature measurement of multiple surface pixels simultaneously. From the measured surface data, a sub-surface structure, embedded inside a sample or tissue, can be reconstructed and imaged when heated by an excitation light pulse. The main drawback in radiometric imaging is the degradation of the spatial resolution with increasing depth, which results in blurred images for deeper lying structures. We circumvent this degradation with blind structured illumination, combined with a non-linear joint sparsity reconstruction algorithm. The ground-breaking concept of super-resolution can be transferred from optics to thermographic imaging.