Impulse and lock-in thermography have been applied to detect delaminations of prototype solder joints, similar to those to be produced between Cu shunts and Cu busbar stabilisers at the Large Hadron Collider (LHC) at CERN. Two infrared cameras with different detector materials and with different spectral ranges and two excitation techniques have been tested and compared for their ability to detect delaminations behind 2 and 3 mm thick Cu shunts. We have analyzed the signal to noise ratio (SNR) for each detected defect and are able to detect defects down to a nominal edge length of 4 mm behind 2 mm thick Cu shunts by using fast impulse thermography and a camera with a microbolometer array. For the 3 mm thick Cu shunt, on the other hand, the nominal 4 mm defect is only visible in the lock-in thermography phase images and the highest SNR has been achieved with a cooled InSb-based camera. In addition, numerical simulations show the influence of the minimum detectable defect size on the shunt thickness and that the developed on-site testing technique is sufficient to find all defects that are detectable theoretically.
We report on recent developments in the detection of surface breaking cracks using
flying laser spot thermography. Application of an infrared camera for mapping the
thermal radiation after excitation with a diode laser equipped with an optical scanner
allows us to examine a surface containing cracks in an entirely non-destructive,
contactless and fast way, without even moving the camera. We developed an efficient
and robust algorithm that can be applied directly to the recorded thermal sequences,
and that derives a single image containing all crack signatures. For this crack detection
technique, no specific synchronisation between laser and camera is required. Hence,
our approach is suitable for an upgrade of existing thermographic systems. The
feasibility of the proposed procedure is proven by testing an artificial test sample and a
piece of rail that comprises roll contact fatigue cracks and by comparing the results
with magnetic particle testing.
In dieser Arbeit wird ein kameragestütztes Verfahren zur Flying-
Spot-Thermografie vorgestellt. Die Anregung wird über einen Diodenlaser mit einem optischen Scanner realisiert. Bei der Auswertung kommt ein effizienter und robuster Algorithmus zum Einsatz, der direkt auf die mit der Kamera aufgenommene Thermografiesequenz angewendet werden kann, ohne auf eine
Synchronisation zwischen Kamera und Lasersystem angewiesen zu sein. Daher eignet sich diese Herangehensweise besonders zur Nachrüstung bestehender Thermografiesysteme.
Die prinzipielle Eignung dieser Methode wird anhand einer Messung an einem Schienenstück mit Rollkontaktermüdungsrissen gezeigt. Als Referenzverfahren werden die Magnetpulverprüfung und eine auf GMR (Giant Magnetoresistance)- Sensoren basierende Streufeldmessung herangezogen. Mit dem thermografischen Verfahren konnten sämtliche enthaltenen Fehler erkannt werden. Dabei wurden Risse im mm-Abstand getrennt nachgewiesen, was etwa der geometrischen Auflösung der eingesetzten Kamera entspricht.
Thermografische ZfP-Verfahren erlauben die Erkennung einer Vielzahl von Defekten in unterschiedlichsten Werkstoffen. Neue Ansätze unter Verwendung von Lasern ermöglichen darüber hinaus die Prüfung auf Oberflächenrisse. Wir stellen die neuesten Entwicklungen dieser vielversprechenden Technik vor und zeigen warum deren Einsatz potentiell die Standardprüfverfahren Magnetpulver- bzw. Eindringprüfung für eine Reihe von Prüfproblemen beerben könnte. Hierzu stellen wir die Prüfergebnisse zu unterschiedlichen metallischen Werkstoffen, Rissgrößen und -typen in Abhängigkeit der Prüfparameter vor. Die aktuelle Grenze der Nachweisempfindlichkeit für die mittels klassischer Thermografie schwer prüfbaren hochreflektierenden Metalloberflächen liegt mit Rissbreiten und -tiefen von weni-gen Mikrometern im Bereich der fluoreszierenden Magnetpulver- und Eindringprüfung. Dabei sind weder Verbrauchsmittel noch eine Oberflächenpräparation notwendig und eine Prüfung kann berührungslos und automatisiert über Entfernungen im Meter-Bereich erfolgen.
We present a systematic study on the performance of laser-thermography for the detection of surface cracks in metallic components. Scanning a metallic surface with laser causes local heating that is mapped simultaneously by an IR-camera and allows identifying cracks with sub-µm openings. The detectability, however, depends on a number of acquisition parameters (e.g. scanning speed, laser power, IR-camera resolution) that typically relate on each other. Most importantly, the detection-sensitivity of surface breaking cracks is given by a particular combination for the acquisition parameter values. As a result, this sensitivity is adaptable within wide ranges allowing the detection of cracks with openings ranging from 200 to 0.1 µm at testing speeds of 100 to 0.05 cm²/s. By examining artificial as well as fatigue cracks, we demonstrate that the method can be even applied to shiny surfaces with no need of pretreatments, which makes it an entirely contactless, remote and automatable NDT technique. A comparison with magnetic particle testing shows that laser-thermography has the potential to become a strong competitor to conventional surface inspection methods in the future.
We present an all-purpose crack detection algorithm for flying spot thermography which is directly applicable to a thermogram sequence without the need of any additional information about the experimental setup. A single image containing distinct crack signatures is derived in two steps. Firstly, the spatial derivative is calculated for each frame of the sequence and, secondly, the resulting data set is sorted pixel wise along the time axis. The feasibility of the proposed procedure is proven by testing a piece of rail that comprises roll contact fatigue cracks and by comparing the results with magnetic particle testing.
Sicherheitsrelevante und zyklisch hoch belastete Bauteile erfordern zur Vermeidung von kostenintensiven Ausfällen besonders stabile Prozessparameter. Bereits sehr kleine Randzonenfehler können unter zyklischer Bauteilbelastung zu Risswachstum und letztendlich zum Bauteilversagen führen. Die frühzeitige Erkennung von Randzonenfehler in Hochleistungsbauteilen wie z.B. Zahnräder, Ritzelwellen und Kurbelwellen erfordert daher eine leistungsfähige zerstörungsfreie Oberflächenrissprüfung, die es ermöglicht in den hochbeanspruchten Funktionsflächen auch Härterisse, Schleifrisse oder Zundereinschlüsse zu detektieren.
Hierzu sind in den letzten Jahren einige neue, innovative Oberflächenprüfverfahren wie die laserangeregte Thermografie und die Streuflussprüfung mit hochauflösenden GMR-Sensoren oder magnetooptischen Verfahren entwickelt worden. Zusätzlich zur hohen Empfindlichkeit zeichnen sich diese innovativen Verfahren durch einen schnellen und teils auch berührungslosen Einsatz aus. Da die noch relativ neu-en Verfahren naturgemäß noch nicht normativ verankert sind, wurden auch bereits erste Validierungen durchgeführt. Um die Leistungsfähigkeit der Verfahren eingehend zu untersuchen, erfolgten Testreihen an verschiedenen Testkörpern in Bezug auf Ortsauflösung, Empfindlichkeit, Automatisierung und Bewertung der Messsig-nale.
Neben den neuen Verfahren und ihren ersten Schritten hin zur Validierung kamen als Referenz auch die „klassischen“ Verfahren der Magnetpulver- und Wirbelstromprüfung zum Einsatz, deren Leistungsfähigkeit durch angepasste Sondenentwicklung auch für sehr kleine Oberflächendefekte nochmals unter Beweis gestellt wurde. Zusätzlich wurde an einigen Testkörpern eine hochauflösende CT durchgeführt. Die Ergebnisse dieses Vergleiches werden vorgestellt und Möglichkeiten sowie Grenzen der einzelnen Verfahren herausgearbeitet.