Eingeladener Vortrag
- nein (11)
NbC has a relatively high hardness (19.6 GPa) and melting temperature (3600 °C) and is usually applied as a grain growth inhibitor in WC–Co hardmetals. The current study reports on the influence of the sintering technology and overall chemical composition on the microstructure and mechanical properties of NbC-based hardmetals, using Co as a binder. The partial replacement of NbC by 5 wt.% WC, Mo2C, VC or TiC allows one to significantly improve the hardness and toughness of the NbC–Co materials. The influence of different binders, i.e., Co, 316L stainless steel and Fe3Al on the microstructure and mechanical properties of NbC-based hardmetals was also investigated. The powder mixtures were sintered in the solid state by PECS and liquid state by conventional vacuum sintering. Detailed microstructural analysis was conducted by EPMA elemental mapping and WDS point analysis. Mechanical properties, including Vickers hardness and indentation toughness were assessed.
The tribological behavior under dry sliding of a Fe3Al-NbC composite prepared by pyro-metallurgical synthesis is compared to different SPS sintered NbC-based hardmetals bonded by cobalt or Fe3AI. The dry sliding wear resistance (0. 1-7 /10 m/s) of the present Fe3Al-NbC with -60 % NbC was close to those known ofNbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks of the Fe3Al-NbC composite, as a metallurgical interphase was formed between matrix and NbC grains. The physical prope1ties of melt grown NbC match those known from powder metallurgically sintered NbC using powders converted from Nb205.
In this present study, the mechanical properties (strength, hardness, moduli) and the dry sliding properties of stoichiometric and sub-stoichiometric NbC were compared. Microhardness and elastic properties of NbC depend from the C/Nb ratio, because the binary phase diagram Nb-C shows a region of homogeneity of NbCx of 0,72≤ x ≤1.0. At RT, hard metals of stoichiometric NbC have an elastic modulus E of ~440 GPa, those of substochiometric NbC0,88 an E of 405 GPa. The hot hardness of sub-stoichiometric NbC is above 600°C higher than of WC. The dry sliding wear resistance (0,1-7/10 m/s) of the present Fe3Al-NbC0,94 with ~61 vol.-% NbC as hard phase was close to those known of NbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks of the Fe3Al-NbC composite (MMC), as a metallurgical interphase was formed between matrix and NbC grains. Stoichiometric and sub-stoichiometric niobium carbides have at RT and 400°C under dry sliding a prone intrinsic wear resistance more or less independent from sliding speed, either as hardmetal or as hard phase in metal matrix composite, associated with an exceptional high load carrying capacity.
Thc tribological behavior under dry sliding of a Fe3Al-NbC composite prepared by pyrometallurgical synthesis is compared to NbC-based hard metals bonded by cobalt or Fe3Al. The dry sliding wear resistance (0,1-7/10 m/s) of the present Fe3Al-NbC with 60% NbC was close to those known of NbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks, as a metallurgical interphase was formed between matrix and NbC grains.
The tribological profile of alumina (99.7%) mated against rotating disks made in binder-less niobium carbide (NbC) and cobalt-bonded NbC were determined under unidirectional sliding tests (0.1 m/s to 8.0 m/s; 22 °C and 400 °C) as well as in oscillation tests (f = 20 Hz, Δx = 0.2 mm, 2/50/98% rel. humidity, n = 105/106 cycles) under unlubricated (dry) conditions. In addition, the microstructure and mechanical properties of binderless NbC and NbC bonded with 8% cobalt were determined as well. The reason for testing hot-pressed NbC was to avoid side effects generated by sintering additives and/or second phases. The tribological data obtained were benchmarked with different ceramics, cermets and thermally sprayed coatings. NbC and cobalt-bonded NbC exhibited low wear rates under dry sliding associated with high load carrying capacity. The tribological profile established revealed a strong position of NbC bearing materials under tribological considerations and for closed tribo-systems against traditional references, such as WC, Cr3C2 and (Ti,Mo)(C,N).