Impulse and lock-in thermography have been applied to detect delaminations of prototype solder joints, similar to those to be produced between Cu shunts and Cu busbar stabilisers at the Large Hadron Collider (LHC) at CERN. Two infrared cameras with different detector materials and with different spectral ranges and two excitation techniques have been tested and compared for their ability to detect delaminations behind 2 and 3 mm thick Cu shunts. We have analyzed the signal to noise ratio (SNR) for each detected defect and are able to detect defects down to a nominal edge length of 4 mm behind 2 mm thick Cu shunts by using fast impulse thermography and a camera with a microbolometer array. For the 3 mm thick Cu shunt, on the other hand, the nominal 4 mm defect is only visible in the lock-in thermography phase images and the highest SNR has been achieved with a cooled InSb-based camera. In addition, numerical simulations show the influence of the minimum detectable defect size on the shunt thickness and that the developed on-site testing technique is sufficient to find all defects that are detectable theoretically.
Für die optische Erwärmung von Prüfteiloberflächen sind Blitz- und Halogenlampen Stand der Technik. Der Vorteil dieser Wärmequellen liegt in ihren relativ geringen Anschaffungskosten bei gleichzeitig hohen Leistungsdichten am Prüfobjekt. Nachteilig ist bei den Halogenlampen die Limitierung der möglichen Modulationsffequenz auf ca. 1 Hz für die Anwendung dieser Quelle in der Lockin-Thermografie. Blitzlampen bieten für gewöhnlich nur eine feste Blitzdauer bei einer geringen Taktrate. Beide Anregungsquellen müssen in Reflexionsanordnung mit Filtern betrieben werden um die entstehende thermische Eigenstrahlung als Störquelle zu eliminieren. Wir stellen Untersuchungen an Hochleistungs-LEDs für den Einsatz in der aktiven Thermografie vor. Diese Lichtquellen werden durch die rasante Entwicklung der möglichen Leistungsdichten nun auch für die thermografische ZfP interessant. Sie zeigen ähnlich dem Laser eine schmale und auf den Werkstoff abstimmbare spektrale Verteilung der Strahlungsleistung bei moderaten Kosten. Die zugrunde liegende Elektrolumineszenz generiert kaum Wärmestrahlung und ermöglicht dadurch die Prüfung während des Erwärmungsvorganges ohne größeren Aufwand. Modulationsfrequenzen über 100 Hz mit thermischen Eindringtiefen < 1 mm sind möglich. Dadurch qualifizieren sich die LEDs zur Anwendung in der Lockin-Thermografie von Metallen und zur oberflächennahen Prüfung von Schichtsystemen. Durch die fast verzögerungsffeie Reaktion der LED auf das steuernde Signal sind nahezu beliebige zeitliche Anregungsformen möglich. Mit solch flexiblen Anregungsformen ließen sich bereits bei den photothermischen Verfahren erfolgreich höhere Tiefenreichweiten und -auflösungen gegenüber den klassischen Methoden der monofrequenten Lockin - und energiereichen Kurzimpuls-Anregung erzielen. Untersuchungen dieser Möglichkeiten im praktischen Einsatz der HochleistungsLEDs werden vorgestellt und mit herkömmlichen Lichtquellen verglichen.
In diesem Beitrag werden die Möglichkeiten der Ortung von Fehlstellen in Cu Lötverbindungen unterhalb verschiedener Cu Blechdicken mit aktiver Thermografie demonstriert. Dabei wurden die Anregung mit Blitzlicht und die periodische Anregung mit der Lock-In Technik miteinander verglichen. Die Vor- und Nachteile der Anwendung unterschiedlicher IR-Kamerasysteme, einer gekühlten InSb-Quantendetektor IR-Kamera und einer Mikrobolometer IR-Kamera, werden dargestellt. Als objektives Kriterium wurde das SNR für unterschiedliche Fehlstellengrößen herangezogen.
Carbon fiber reinforced polymer (CFRP) specimens with artificial delaminations and with impact damage have been characterized using active thermography with flash excitation. Systematic investigations have been performed in four different experimental configurations of flash lamps and infrared (IR) camera in transmission as well as in reflection alignment. It is shown here that the diffusivities determined for the sound and for the damaged areas give a good measure for damage characterization. Although reflection measurements also give information about defect depth, reflection measurements from only one side are not sufficient for assessing the whole cross section of the specimens. Thus, depending on sample thickness the lateral size of damage could only be determined from reflections measurements from both sides or from transmission measurements. In this paper, measurement accuracy and limits of flash thermography for the investigation of CFRP specimens are presented in detail together with quantitative data concerning the defects.
Eine Arbeitsgruppe der BAM in der Abteilung für Zerstörungsfreie Prüfung forscht seit 2011 an verschiedenen technischen Fragestellungen, die sich aus dem thermografischen Lösungsansatz ergeben. Zum Beispiel werden spezielle Prüfkörper aus GFK im Labor unter dem Gesichtspunkt untersucht, inwieweit (materielle) innere Strukturen und äußerlich nicht sichtbare Schäden mit Thermografie offenbart werden können. Hierbei werden verschiedene Anregungs- und Auswertungstechniken auf ihre Eignung für diese Problemstellung untersucht. Der folgende Beitrag erläutert einige technische Schwierigkeiten bei der praktischen Anwendung der geplanten Inspektionsmethode und stellt einen erfolgversprechenden Lösungsansatz vor.
Lockin thermography as well as flash thermography are very well suited for non-destructive testing and characterisation of inhomogeneities and damage in CFRP structures. Both methods are applied more and more in research and industry, but until know it is not clear which are the advantages of one method against the other. In
this paper, results of two research projects concerning the validation and standardisation of both methods are presented. Three different types of CFRP test specimens consisting of well-defined flat bottom holes, of artificial delaminations made of PTFE plates embedded in CFRP and of real impact damage have been investigated systematically with flash and lockin excitation. Here, the phase images of both methods are compared qualitatively as well as quantitatively.
Standards for the application of flash thermography as well as of lock-in thermography are urgently required.
Both methods are applied more and more often in research and industry, but still extensive validation procedures are required for each individual application. In this paper, the results of two research projects concerning the validation and standardisation of both methods are presented. This includes results of a detailed study of the influence of measurements parameters on flash thermography, of the comparison of the lateral resolution obtained with flash and lock-in thermography and the description of a draft standard for flash thermography.
Weltweit errichtet man zunehmend Offshore-Windkraftanlagen (WKA). Diese auf hoher See errichteten WKA benötigen geeignete Wartungs- und Instandhaltungskonzepte. Bestehende Konzepte aus dem Landbereich geraten unter Offshore-Bedingungen an ihre Grenzen oder lassen sich überhaupt nicht anwenden, daher müssen neue Ansätze erprobt werden. Im Rahmen des BMBF geförderten Forschungsprojektes "IKARUS" ist das Potential der (berührungslosen) thermografischen Fernerkundung zur Zustandsüberwachung der Rotorblätter von WKA zu untersuchen.
Veränderungen der Umgebungsbedingungen wie z.B. solare Einstrahlung oder der Tagestemperaturgang führen zu veränderlichen Energieeinträgen in ein Objekt, die beim Vorhandensein von Inhomogenitäten im Material oder Strukturmerkmalen thermische Signaturen hervorrufen können. Ebenso können Veränderungen der Witterungsbedingungen dazu führen, dass bereits vorhandene thermische Signaturen wieder ausgelöscht werden. Daher ist es unbedingt notwendig, systematische Langzeitmessungen bei verschiedenen Umgebungsbedingungen durchzuführen, um Fehlinterpretationen zu vermeiden.
In diesem Beitrag wird anhand von Laborversuchen und Simulationen zunächst die grundsätzliche Eignung des thermografischen Ansatzes für glasfaserverstärkte Kunststoffe (GFK), aus denen die Außenhüllen der Rotorblätter gefertigt sind, demonstriert. Hierbei werden unterschiedliche Arten von Defekten an GFK vorgestellt, die zu thermischen Signaturen an Rotorblättern führen können. Anschließend werden Zwischenergebnisse aus einem laufenden Langzeitversuch zu einem demontierten Rotorblattsegment vorgestellt, welches unter verschiedenen Witterungsbedingungen und zu verschiedenen Tages- und Jahreszeiten thermografisch beobachtet wurde.