Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (34)
- Zeitschriftenartikel (20)
- Vortrag (8)
- Posterpräsentation (4)
- Beitrag zu einem Sammelband (1)
- Amtliche Bekanntmachung (1)
Sprache
- Englisch (68) (entfernen)
Schlagworte
- Radioactive material (15)
- Impact limiter (13)
- Transport (13)
- Wood (11)
- FEM (6)
- Package (6)
- Consequences (4)
- Drop test (4)
- Friction (4)
- Transport cask (4)
Organisationseinheit der BAM
- 3 Gefahrgutumschließungen; Energiespeicher (26)
- 3.3 Sicherheit von Transportbehältern (24)
- 2 Prozess- und Anlagensicherheit (4)
- 2.1 Sicherheit von Energieträgern (4)
- 8 Zerstörungsfreie Prüfung (4)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (4)
- 9 Komponentensicherheit (4)
- 9.5 Tribologie und Verschleißschutz (4)
- 2.2 Prozesssimulation (2)
- 3.0 Abteilungsleitung und andere (2)
Eingeladener Vortrag
- nein (8)
Modified Yoldas sols can be used to prepare crack-free well adherent layers on different substrate materials such as sodalime glass, corundum and metal (IN-718). These layers having thicknesses of 0.6 µm are strain tolerant and withstand thermal cycling between 810 °C and room temperature. Introducing alpha-Al2O3 filler particles into modified Yoldas sols allows the preparation of thicker layers of 1.6 µm, which as well can be thermally cycled without noticeable delaminations. Chemical bonding seems to be the predominant layer bonding mechanism.
Alumina coatings with differing phase compositions were deposited on Inconel-718 (IN-718) Ni-base
superalloy substrates using solgel processing. Mass gain measurements served for studying the oxidation
behavior of coated metal surfaces if exposed to 800°C and 900°C for up to 4000 h in static air. Itwas found, that
alumina coatings significantly reduce the oxidation related mass gain of IN-718 even after heating to 900°C
for 4000 h. Transmission electron microscopy (TEM) studies revealed diffusion of elements from the metal
substrate (IN-718) into the alumina coatings and to a much lower degree from the coating into the
substrate. These diffusion processes are greatly influenced by the phase composition of the coatings, especially
by the presence of alpha-alumina.
Simulation of the Crushing of Wood Filled Impact Limiters for Packages of Radioactive Material
(2008)
Mechanical and thermal safety assessment of packages for transport of radioactive material in Germany is carried out by the Federal Institute for Materials Research and Testing (BAM). Both experimental and computational (analytical, numerical) methods combined with material and/or component tests are the basis for the state of the art safety assessment concept at BAM. The required mechanical tests according to IAEA regulations include, among others, a 9-m-drop-test on an unyielding target. Impact limiting components, which are attached to the cask at both ends, limit forces applied on the cask body and lid system by absorbing a major part of the impact energy. In Germany, impact limiters of packages for transport of radioactive materials are typically of steel-wood-sandwich construction, combining a relatively stiff steel structure bolted to the cask body, outer steel plates and different types of wood. By crushing the wood-steel-sandwich-structure between an unyielding target and the cask, the kinetic energy of a 9-m-free-fall is absorbed. The main energy absorber is wood under a high level of deformation. Wood under large deformations exhibits destruction of the fibre matrix. By analysing compression of the impact limiter wood after the drop tests with prototype casks for radioactive material, underlying mechanisms of wood crushing and corresponding energy absorption under large deformations are identified. Softening occuring at compression of the wood is a function of the lateral strain restriction of wood. Against the background of continuum mechanics an analogous model for compression of the fibre bundle is presented. The model takes the lateral strain restriction as triaxiality of the stress state into account. Further modelling possibilities for wood with a continuum approach are described. Different material laws in the explicit finite element code LS-DYNA are analysed for possible application using the analogous model for the fibre bundle. Small scale compression tests with wooden specimens are modelled in order to evaluate the ability of different modelling techniques to simulate softening. Although modelling of the compression of wood under large deformations is possible, softening could not be simulated purposefully. A drop test of a cask with impact limiting devices similar to existing impact limiters is simulated with different material laws for wood. The behaviour of impact limiting devices could not be simulated universally including the influence of the lateral strain restriction; nevertheless loading of the cask by crushing of the impact limiter could be simulated purposefully. Verification with experimental results is essential.
The moisture content of wood is known to have a significant influence on the wood's mechanical properties. Using wood as an energy absorber in impact limiters of packages for the transport of radioactive material, it is of particular importance to ensure the moisture content and thus relevant mechanical properties to be in specified limits. The paper surveys the influence of wood moisture content on the mechanical properties of wood. Different measuring methods are discussed with respect to in situ applicability, accuracy and effort. The results of an experimental analysis of the accuracy of hand held moisture metres using the electrical resistance method are discussed. Conclusions are drawn regarding the measurement of moisture content of wood upon delivery as well as of complete impact limiter assemblies. Requirements for quality surveillance during manufacturing of wood filled impact limiters are derived and it is exemplified how to meet them. Construction, manufacturing and inspection of impact limiter encapsulation with regard to leak tightness are addressed.
Impact limiters of packages for transport of radioactive materials are in Germany typically steel-wood-sandwich-constructions, combining a relatively stiff steel structure bolted to the cask body, outer steel plates and different types of wood. By crushing the wood-steel-sandwich-structure between unyielding target and cask, kinetic energy of 9-m-free-fall is absorbed. Main energy absorber is wood under a high level of deformation. Wood under large deformations exhibits destruction of the fibre matrix. By analysing compression of impact limiter wood after drop tests with prototype casks for radioactive material, underlying mechanisms of wood crushing and corresponding energy absorption under large deformations are identified. Softening occurring at compression of wood is a function of lateral strain restriction of wood. Against the background of continuum mechanics an analogous model for compression of fibre bundle is presented. The model takes lateral strain restriction as triaxiality of stress state into account. Further modelling possibilities for wood with a continuum approach are described. Different material laws in the explicit Finite Element code LS-DYNA are analysed for possible application on the analogous model for the fibre bundle. Small scale compression tests with wooden specimens were modelled in order to evaluate the ability of different modelling techniques to simulate softening. Although modelling of compression of wood under large deformations is possible, softening could not be simulated purposefully. A drop test of a cask with impact limiting devices similar to existing impact limiters is simulated with different material laws for wood. Behaviour of impact limiting devices could not be simulated universally including influence of lateral strain restriction; nevertheless loading of the cask by crushing of impact limiter could be simulated purposefully. Verification with experimental results is compulsory.
Alumosols in combination with well dispersed corundum were successfully used to form up to 2.5 ìm thick coatings on the Ni-base alloy SC16. These coatings withstood heat treatments at 700 °C in a water vapour containing atmosphere. The heat treatment caused formation of delta-alumina in the coating and diffusion of chromium and titanium into the coating.