Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (15) (entfernen)
Schlagworte
- Corrosion (6)
- Corrosion testing (3)
- Gel-type electrolytes (3)
- Heat treatment (3)
- KorroPad (3)
- Martensitic stainless steel (3)
- Zinc coatings (3)
- Electrochemical noise (2)
- Electrochemical potentiodynamic reactivation (2)
- Gel electrolytes (2)
Organisationseinheit der BAM
In the last years, new approaches for the evaluation of the corrosion resistance of martensitic stainless steels were developed, which allow nearly non-destructive as well as short-term corrosion testing. This work analyzes the sensitive influence of microstructure and surface treatment on the corrosion resistance. The effect of alloy composition and microstructure, which is always present in addition to the influence of various surface treatments will be evaluated and discussed. The corrosion behavior was investigated with conventional evaluation of the pitting potential, electrochemical potentiodynamic reactivation (EPR), electrochemical noise (EN), and the 'KorroPad' (KP) technique. EPR provided information about the passivation ability and the extent of chromium content reduction due to chromium carbide precipitation in the microstructure. The use of EN and KP aims to detect the influence of different surface treatment parameters on the corrosion resistance in a nearly non-destructive way. Furthermore the results shall demonstrate the functionality and convenience of the short-term corrosion test methods EN and KP in order to gain more acceptance within the scientific community. The results will allow the extraction of surface treatment effects on the corrosion behavior of the martensitic stainless steels 1.4116, 1.4034, and 1.4021.
Martensitic stainless steels are commonly used in cutlery fabrication requiring high hardness and sufficient corrosion resistance. The heat treatment process affects the mechanical and electrochemical behavior of martensitic stainless steels due to the precipitation of chromium carbides. Depending on the heat treatment the corrosion resistance of these steels can vary strongly, and improper heat treatment parameters can lead to a weak pitting corrosion resistance. The aim of this work is to identify heat treatment parameters influencing the corrosion resistance of martensitic stainless steels by using three different electrochemical testing methods. To this purpose, five different heat treatments were applied to the alloys 1.4116 and 1.4034. In addition to the determination of the critical pitting potentials and the modified double-loop electrochemical potentiodynamic reactivation tests (DL-EPR) a new KorroPad indicator test was used assessing the pitting corrosion behavior. The results showed that all methods used were in good agreement for verifying the influence of the various heat treatment parameters on the corrosion behavior and to identify the effect of heat treatment conditions on the pitting corrosion resistance.
The development of organic coatings for corrosion protection is an elaborate process with a multitude of often interminable investigations and tests of protection properties. Electrochemical methods support the processes of development to a great extent and help to understand mechanisms of action and failure. They are usually carried out on applied coating systems with a completed formulation. An examination possibility is presented in this publication that enables the characterization of waterbased coatings with different formulation variations in the liquid (aqueous) state with the aid of electrochemical noise technique. Thus, selection of binders, pigments, and other additives is supported essentially and made more efficient in a very early Phase of formulation development. The paper shows that a unique insight into the dynamic processes of a metal in contact with an aqueous coating dispersion is possible using the example of the development of zinc-free corrosion-inhibiting pigments for waterbased coatings. In addition, it is presented in which way the results correlate with the performance of applied coatings.
Bei der Qualitätsbewertung von Schneidwaren aus nichtrostenden martensitischen Chrom-Stählen stellt die Überprüfung der Korrosionsbeständigkeit ein wichtiges Kriterium dar. Allgemein üblich sind Wechseltauchversuche mit relativ hohem zeitlichem und auswertungsbedingtem Aufwand, die noch dazu zerstörend sind und teilweise fragwürdige Ergebnisse liefern. In den letzten Jahren wurden neue Ansatze der Prüfung geschaffen, die eine nahezu zerstörungsfreie Kurzzeit-Korrosionsprüfung erlauben. Es wird gezeigt, dass mit dem elektrochemischen Rauschen sehr empfindlich Einflüsse des Härtens und der Oberflächenbehandlung auf die Korrosionsbeständigkeit nachgewiesen werden können, wodurch eine schnelle und objektive Qualitätsbewertung innerhalb des Fertigungsprozesses und der Endkontrolle von Produkten möglich ist. Das für die Prüfmethodik ausgenutzte Phänomen des elektrochemischen Rauschens zielt darauf ab, den Beginn der Korrosion empfindlich und schnell zu detektieren, ohne die Prüfbedingungen maßlos zu verschärfen und Produkte damit zu zerstören. Neben der Funktionalität der Prüfung stehen aber auch die Anwenderfreundlichkeit und somit die Akzeptanz bei den Herstellern im Vordergrund. Aus diesem Grund wurde zusätzlich ein Indikatortest (KorroPad) als praxistaugliche Alternative zum elektrochemischen Rauschen angewendet. Die Ergebnisse zeigen eine gute Übereinstimmung beider Methoden und ermöglichen eine effektive betriebliche Qualitätsüberwachung von Schneidwaren.
Electrochemical tests, hardness measurements, and microstructure analysis are performed to study the influence of austenitizing, quenching, and tempering parameters on the corrosion resistance of the martensitic stainless steel grade X50CrMoV15 (1.4116). Different heat treatment states were studied using an adapted EPR-Test to evaluate the chromium distribution and depletion caused by the formation and dissolution of chromium rich carbides. The EPR results were correlated with pitting corrosion behavior, demonstrating the strong effect of heat treatment parameters on the susceptibility of martensitic stainless steels to corrosion phenomena.
The salinization and contamination of metal surfaces by chloride-containing aerosols is of great importance with regard to corrosion phenomena of damaged coated metal surfaces and stainless steels in the maritime sector and in offshore applications. Detailed questions have to be answered to clarify whether and to what extent salinization of the surface has an influence on the adhesion and durability of coatings in repairing applications and on pitting occurrence on stainless steels under atmospheric conditions. The questions arise which degree of salinization is reached after which period of time and how a defined and reproducible salinization can be simulated in the laboratory for further systematic investigations. The article is dedicated to these questions. Results of a field trial on the Island of Heligoland are presented and a simple procedure for a defined loading of metal surfaces with chlorides at a laboratory scale using a design of experiments (DoE) approach is introduced.
The present work describes the combination of electrochemical investigations by using a gel‐type electrolyte with Fourier‐transformed infrared spectroscopy to investigate partially extremely thin corrosion product films on titanium‐zinc. The gel pad method enables the determination of corrosion relevant parameters such as the potential and the linear polarization resistance without altering the corrosion product layers, which are extremely prone to re‐dissolution when freshly formed. Complementary infrared spectroscopy enables the determination of main compounds of even very thin surface layers of few tenth of nanometers with a certain lateral resolution. It was found that zinc forms mostly zinc carboxy‐hydroxides such as hydrozincite, under various exposure conditions. The protective properties of these hydrozincite layers depend on the structure of the corrosion product film rather than on its thickness. In mid‐term exposure tests, shallow corrosion pits were found even in the absence of corrosive agents such as chloride.
Samples of the austenitic stainless steel grade X5CrNi18‐10 (1.4301, AISI 304) were ground industrially with various grinding parameters to study their influence on corrosion resistance. The ability of the mechanically ground surfaces to form a stable passive layer was evaluated by KorroPad test and a modified electrochemical potentiodynamic reactivation test based on a single loop (EPR‐SL). Furthermore, the surfaces were characterized by surface analytical methods. The main influence was determined regarding abrasive belt type. Surfaces mechanically ground with granulate abrasive belts constantly had a lower corrosion resistance than surfaces ground with single‐coated grain. The granulate abrasive belts generated more sensitized surface areas and left formations of welded sample material on the mechanically ground surfaces. A post‐treatment with a nonwoven abrasive proved to be an effective finishing process by which the surface defects and sensitized material got removed and the surfaces regained the expected corrosion resistance.
The paper presents a new method for the determination and evaluation of tafel factors using gel-type electrolytes and electrochemical frequency modulation technique (EFM). This relatively new electrochemical method offers the possibility to determine both polarization resistances and tafel factors within one measurement and in short measuring intervals. Starting from a comprehensive parameter study it is shown that a direct relationship between the two values exists that can be described mathematically. This contribution presents the determined tafel factors for the system gel-type electrolyte/zinc and discusses their applicability and their limits.
Ergebnisse auf einen Blick
Elektrochemische Messungen in wässrigen Lackdispersionen konnten erfolgreich durchgeführt werden und bieten vielversprechende Ergebnisse.
Es können zeitnah Aussagen zum Auflösungsverhalten des Substrates in Abhängigkeit von verschiedenen Korrosionsschutzpigmenten, dispergiert im wässrigen Bindemittel, getroffen werden.
Somit ist eine Vorauswahl/Screening verschiedener Korrosionsschutzpigmente in Kombination mit dem wässrigen Bindemittel möglich, welche mit konventioneller Korrosionsprüfung bestätigt werden konnte.
Das Erkennen und Nutzen synergetischer Wechselwirkungen hilft bei der Entwicklung neuartiger zinkfreier Pigmente.