In the last years, new approaches for the evaluation of the corrosion resistance of martensitic stainless steels were developed, which allow nearly non-destructive as well as short-term corrosion testing. This work analyzes the sensitive influence of microstructure and surface treatment on the corrosion resistance. The effect of alloy composition and microstructure, which is always present in addition to the influence of various surface treatments will be evaluated and discussed. The corrosion behavior was investigated with conventional evaluation of the pitting potential, electrochemical potentiodynamic reactivation (EPR), electrochemical noise (EN), and the 'KorroPad' (KP) technique. EPR provided information about the passivation ability and the extent of chromium content reduction due to chromium carbide precipitation in the microstructure. The use of EN and KP aims to detect the influence of different surface treatment parameters on the corrosion resistance in a nearly non-destructive way. Furthermore the results shall demonstrate the functionality and convenience of the short-term corrosion test methods EN and KP in order to gain more acceptance within the scientific community. The results will allow the extraction of surface treatment effects on the corrosion behavior of the martensitic stainless steels 1.4116, 1.4034, and 1.4021.
Die Qualität von Schneidwaren aus martensitisch nichtrostenden Stählen (MNS) hängt neben ihrer härtebedingten Schneidleistung wesentlich von ihrer Korrosionsbeständigkeit ab, die dauerhaft das hochwertige optische Erscheinungsbild gewährleisten soll. Zur Prüfung der Korrosionsbeständigkeit hat sich bei Schneidwaren aus MNS die Anwendung des Wechseltauchversuchs etabliert, dessen Ausweitung aufwendig und dessen Ergebnisse oftmals fragwürdig sind. In den letzten Jahren wurden daher neue elektrochemische Methoden entwickelt, um das Korrosionsverhalten von MNS objektiver zu bewerten. Diese neuen Untersuchungsmethoden ermöglichen eine genauere Erfassung der teilweise stark schwankenden Korrosionsbeständigkeit von MNS und bilden damit die Grundlage zur Aufklärung der Ursachen dieser Schwankungen. Im Rahmen des IGF-Vorhabens 16636 BG wurden dazu das elektrochemische Rauschen (ECR), das KorroPad und die elektrochemisch potentiodynamische Reaktivierung (EPR) eingesetzt, um die werkstoffseitigen Einflüsse der Mikrostruktur und den Einfluss der Oberflächenbearbeitung auf die Korrosionsbeständigkeit zu untersuchen. Es wurden dazu an drei weit verbreiteten MNS (1.4116, 1.4034 und 1.4021) je acht verschiedene Oberflächenzustände hergestellt und das Korrosionsverhalten untersucht. Um die dabei aufgetretenen Unterschiede im Lochkorrosionsverhalten zwischen den drei Werkstoffen zu erklären, wurde der EPR-Test eingesetzt, der lokale ChromVerarmung im Gefüge als werkstoffbedingte Ursache von Lochkorrosionsanfälligkeit nachweist. Mit der Kombination der Ergebnisse aus EPR, ECR und KorroPad war es möglich, die unterschiedliche Lochkorrosionsanfälligkeit direkt der unterschiedlich stark ausgeprägten Chromverarmung der drei MNS zuzuordnen. Der Einfluss der Chromverarmung auf die Lochkorrosionsanfälligkeit ist dabei deutlich größer als der Effekt der Oberflächenbearbeitung, der nur bei gering ausgeprägter Chromverarmung ersichtlich ist. Damit wurde gezeigt, dass nur bei Betrachtung aller Einflussgrößen sichere Aussagen zur Korrosionsbeständigkeit und zu den Ursachen der Lochkorrosionsanfälligkeit von MNS möglich sind.
Martensitic stainless steels are commonly used in cutlery fabrication requiring high hardness and sufficient corrosion resistance. The heat treatment process affects the mechanical and electrochemical behavior of martensitic stainless steels due to the precipitation of chromium carbides. Depending on the heat treatment the corrosion resistance of these steels can vary strongly, and improper heat treatment parameters can lead to a weak pitting corrosion resistance. The aim of this work is to identify heat treatment parameters influencing the corrosion resistance of martensitic stainless steels by using three different electrochemical testing methods. To this purpose, five different heat treatments were applied to the alloys 1.4116 and 1.4034. In addition to the determination of the critical pitting potentials and the modified double-loop electrochemical potentiodynamic reactivation tests (DL-EPR) a new KorroPad indicator test was used assessing the pitting corrosion behavior. The results showed that all methods used were in good agreement for verifying the influence of the various heat treatment parameters on the corrosion behavior and to identify the effect of heat treatment conditions on the pitting corrosion resistance.
Bei der Qualitätsbewertung von Schneidwaren aus nichtrostenden martensitischen Chrom-Stählen stellt die Überprüfung der Korrosionsbeständigkeit ein wichtiges Kriterium dar. Allgemein üblich sind Wechseltauchversuche mit relativ hohem zeitlichem und auswertungsbedingtem Aufwand, die noch dazu zerstörend sind und teilweise fragwürdige Ergebnisse liefern. In den letzten Jahren wurden neue Ansatze der Prüfung geschaffen, die eine nahezu zerstörungsfreie Kurzzeit-Korrosionsprüfung erlauben. Es wird gezeigt, dass mit dem elektrochemischen Rauschen sehr empfindlich Einflüsse des Härtens und der Oberflächenbehandlung auf die Korrosionsbeständigkeit nachgewiesen werden können, wodurch eine schnelle und objektive Qualitätsbewertung innerhalb des Fertigungsprozesses und der Endkontrolle von Produkten möglich ist. Das für die Prüfmethodik ausgenutzte Phänomen des elektrochemischen Rauschens zielt darauf ab, den Beginn der Korrosion empfindlich und schnell zu detektieren, ohne die Prüfbedingungen maßlos zu verschärfen und Produkte damit zu zerstören. Neben der Funktionalität der Prüfung stehen aber auch die Anwenderfreundlichkeit und somit die Akzeptanz bei den Herstellern im Vordergrund. Aus diesem Grund wurde zusätzlich ein Indikatortest (KorroPad) als praxistaugliche Alternative zum elektrochemischen Rauschen angewendet. Die Ergebnisse zeigen eine gute Übereinstimmung beider Methoden und ermöglichen eine effektive betriebliche Qualitätsüberwachung von Schneidwaren.
Mit Hilfe des KorroPad-Prüfverfahrens konnten verschiedene umgebungs- sowie prozessbedingte Einflüsse in Parameterstudien gezielt untersucht werden. So konnte der negative Einfluss von korundbasierten Schleifmitteln auf die Passivschichtausbildung nachgewiesen werden. Weiterhin konnte mittels KorroPad die Wirksamkeit verschiedener Oberflächenbearbeitungsverfahren bei der Schweißnahtnachbearbeitung untersucht und daraus Erkenntnisse für die Prozessoptimierung gewonnen werden. In den hier gezeigten Untersuchungen hat sich das KorroPad-Prüfverfahren für die Beschreibung der Passivschichtstabilität als hervorragend geeignet erwiesen.
The corrosion resistance of aluminium surfaces is closely linked to the surfacecstate after a grinding process. For years, iron‐containing abrasive materials were suspected to lead to increased corrosion susceptibility after processing of aluminium surfaces. To prove a possible correlation between the iron content of an abrasive and the corrosion behaviour of aluminium components, scientific investigations and experimentally practical corrosion tests are necessary.
For the current investigation, specimens of a technical Al‐Si alloy from the same batch were used. The test specimens were mechanically ground with various resin‐bonded model abrasives containing different iron contents. The performed corrosion tests did not reveal a negative influence of the different iron‐containing abrasives on the corrosion behaviour of the Al–Si alloy.
However, the most sensitive measuring method (electrochemical noise)
showed differences in the surface activity depending on the type of abrasive.