A series of Cp(C5H5)ZrCl2 and Cp2ZrCl2 pre-catalysts (Cp = C5HMe4, C4Me4P, C5Me5, C5H4tBu, C5H3-1,3-tBu2, C5H2-1,2,4-tBu3) together with (C5H5)2ZrCl2 was used for the directed oligomerization of propene and 1-hexene in comparative experiments. Oligomer characterization was carried out by 1H NMR, SEC (GPC), MALDI-TOF MS, cryoscopy and Raman spectroscopy. From 1H NMR the nature and relative ratio of the double-bond end group is determined together with n if every oligomer molecule contains such a double-bond end group. Normally vinylidene double bonds (from -hydrogen elimination) are found. From 1H NMR and MALDI-TOF MS also vinyl end groups (from -methyl elimination) are observed in the case of oligopropenes with (C4Me4P)- (C5H5)ZrCl2 and with the symmetrical methyl containing Cp2ZrCl2 pre-catalysts. The vinylidene/vinyl ratio depends on the ligand and increases from C5HMe4 (65/35) over C4Me4P (61/39) to C5Me5 (9/91). A comparison of n from 1H NMR and SEC together with MALDI-TOF MS shows that the phospholyl-zirconocenes and (C5HMe4)2ZrCl2 also exhibit chain transfer to aluminium, thereby giving saturated oligomers.
In vielen Umgebungen, besonders bei hohen Temperaturen, korrosiven Umgebungen oder auf bewegten oder schlecht zugänglichen Flächen, kann die Temperatur nicht oder nur mit nicht akzeptablem Aufwand mit Berührungsthermometern gemessen werden. Diese Umgebungsbedingungen sind unter anderem in der chemischen Industrie, der Lebensmittel-, Metall-, Glas-, Kunststoff- und Papierherstellung sowie bei der Lacktrocknung anzutreffen. In diesen Bereichen kommen Strahlungsthermometer zum Einsatz. Der VDI-Statusreport zeigt typische Anwendungsfelder von nicht radiometrisch kalibrierten Wärmebildkameras und von radiometrisch kalibrierten Thermografiekameras. Um verlässlich mit spezifizierten Messunsicherheiten berührungslos Temperaturen zu messen, müssen die Strahlungsthermometer und Thermografiekameras nicht nur kalibriert, sondern radiometrisch und strahlungsthermometrisch umfassend charakterisiert werden. Auch die optische Materialeigenschaft, der spektrale Emissionsgrad und die Gesamtstrahlungsbilanz (Strahlung des Messobjekts und der Umgebung) sind bei der industriellen Temperaturmessung von großer Bedeutung. In den letzten Jahrzehnten ist dazu ein umfassendes technisches Regelwerk entstanden, das wir Ihnen mit diesem VDI-Statusreport vorstellen. Manche in den Richtlinien beschriebenen Kennwerte mögen abstrakt wirken. In diesem Statusreport zeigen wir an konkreten Beispielen, was diese Kenngrößen für die berührungslose Temperaturmessung bedeuten. Beispiele von Anwendungen zeigen, wo temperaturmessende Thermografiekameras und ausschließlich bildgebende Wärmebildkameras in der Praxis eingesetzt werden. Mit einer Analyse, welche Themen und Anwendungen derzeit besonders intensiv diskutiert werden, versuchen wir Trends für zukünftige Entwicklungen herauszuarbeiten.
The large-scale mechanochemical reduction of binary sulfides chalcocite (Cu2S) and covellite (CuS) by elemental iron was investigated in this work. The reduction of Cu2S was almost complete after 360 min of milling, whereas in the case of CuS, a significant amount of non-reacted elemental iron could still be identified after 480 min. Upon application of more effective laboratory-scale planetary ball milling, it was possible to reach almost complete reduction of CuS. Longer milling leads to the formation of ternary sulfides and oxidation product, namely cuprospinel CuFe2O4. The rate constant calculated from the magnetometry measurements using a diffusion model for Cu2S and CuS reduction by iron in a large-scale mill is 0.056 min−0.5 and 0.037 min−0.5, respectively, whereas for the CuS reduction in a laboratory-scale mill, it is 0.1477 min−1. The nanocrystalline character of the samples was confirmed by TEM and XRD, as the produced Cu exhibited sizes up to 16 nm in all cases. The process can be easily scaled up and thus copper can be obtained much easier from refractory minerals than in traditional metallurgical approaches.
Control over the bottom up synthesis of metal nanoparticles (NP) depends on many experimental factors, including the choice of stabilising and reducing agents. By selectively manipulating these species, it is possible to control NP characteristics through solution-phase synthesis strategies. It is not known, however, whether NPs produced from mechanochemical syntheses are governed by the same rules. Using the Au NPs mechanosynthesis as a model system, we investigate how a series of common reducing agents affect both the reduction kinetics and size of Au NPs. It is shown that the relative effects of reducing agents on mechanochemical NP synthesis differ significantly from their role in analogous solution-phase reactions. Hence, strategies developed for control over NP growth in solution are not directly transferrable to environmentally benign mechanochemical approaches. This work demonstrates a clear need for dedicated, systematic studies on NP mechanosynthesis.