Filtern
Erscheinungsjahr
Dokumenttyp
- Posterpräsentation (13)
- Zeitschriftenartikel (10)
- Beitrag zu einem Tagungsband (3)
- Vortrag (2)
- Buchkapitel (1)
- Dissertation (1)
Schlagworte
- LTCC (6)
- Coefficient of thermal expansion CTE (2)
- Design (2)
- Glass ceramic composites (2)
- Particle size distribution (2)
- Partikelgröße (2)
- Partikelgrößenverteilung (2)
- Strain gauge (2)
- Thin-film substrate (2)
- Accuracy experiment (1)
Eingeladener Vortrag
- nein (2)
Alumina sols were prepared using a modified
Yoldas procedure, thus resulting in sols with high solids
content, excellent long term stability and small particle size.
PH-value ranged between 3.7 and 0.6. Sols were characterised
using rheological, UV-vis transmission and particle
size measurements. Depending on NO3-/Al molar ratio as
well as solids content, sols vary. Analysis of reduced viscosities
indicate the formation of chainlike polymeric species
above a critical solids fraction.
Presented are results of an inter-laboratory study (ILS) for measurements of the particle size distribution of fine powders in wet dispersion by laser diffraction. In this proficiency test 32 participants from four countries took part. They utilized 13 different devices from 7 manufacturers.
Three commercial powders (glass spheres and two silicon carbide powders) showing a median diameter of about 30, 10 and 1 µm (volume distribution), respectively, were chosen for the procedure. A homogeneity study was carried out after the units had been separated and bottled.
All participants received their test samples including a description of the standard operating procedures based on ISO 13320:2009 – to ensure that experiments were performed in a consistent manner. Results were calculated using the Mie Theory. The general means and the precision of the results were estimated in accordance with ISO 5725-2:2002.
The evaluation showed excellent values of repeatability standard deviation. Values of 4 to 21?% of the reproducibility standard deviation of the results were found in the particle size range above 1 µm. Much larger deviation between the labs was detected in the case of smaller particles. Differences in the design of the analyzers were unambiguously identified as the main reason for the large deviations.
Resolution of capacitive sensors can be improved enormously by replacement of the dielectric material between the capacitor plates (e.g. air-dielectric) by a dielectric fluid with high permittivity. High dielectric liquid dispersions of ceramic micro and nano powders should be qualified as dielectric fluid with longtime shelf life.
For this purpose it was necessary to produce stabilized ceramic suspensions with high particle concentration and to investigate sedimentation processes of the particles. Characterization of particles was done by use of zeta potential measurement, gas adsorption measurements (BET), density measurement with gas pycnometer as well as particle sizing by ultrasound spectroscopy and by use of an optical centrifuge.
Shelf life of optimized electrostatic and steric stabilized ceramic suspension was investigated by use of an optical centrifuge, a LUMISizer 651 MW (LUM Ltd.) with STEP technology and front tracking analysis. Two different wave lengths – NIR (865 nm) and blue light (470 nm) were available for examination. Centrifugation measurements with different rotation speed were used to study the rheological behavior and the sedimentation process. By this way it was possible to achieve accelerated stability determination. Measured values could be used to simulate the sedimentation process under gravity acceleration and to predict shelf life for suspensions with different dispersants.