Ti/TiN multilayer coatings with multilayer periods in the range 550 nm and a final thickness of 2 µm were deposited on steel substrates by cyclic modulation of nitrogen gas flow into the chamber of a PVD sputtering device. Coating characterization was performed by cross-sectional transmission electron microscopy, glancing-angle X-ray diffraction and instrumental indentation testing. Individual a-titanium and titanium nitride layers were always observed, although for the finer microstructures, the TiN layers were thicker than the Ti layers by a factor three. The plastic hardness of the films increased steadily with decreasing layer spacing, following a HallPetch relationship. Finally, a hardness value of 42 GPa was reached, which is similar to that of a thick TiN monolayer, prepared under the same coating conditions.
Durch faseroptische Sensoren können Bauteile im Einsatz kontinuierlich überwacht und frühzeitig Informationen über Materialveränderungen gewonnen werden. Mittels einer magnetostriktiven Aktorschicht, welche den Sensor umhüllt, kann nun auch die korrekte Sensorfunktion jederzeit kontrolliert werden. Als Aktorschicht eignet sich galvanisch abgeschiedenes reines Nickel oder Nickel-Eisen in der Zusammensetzung 50:50. Um diese haftfest mit dem Sensor zu verbinden wurde ein ECD/PVD-Kombinationsschichtsystem entwickelt. Die mechanischen Eigenschaften der ECD-Schicht können sowohl mit einer auf die Fasergeometrie angepassten instrumentierten Eindringprüfung als auch einem 2-Punkt-Biegeversuch bestimmt werden.
Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms.