Up to ~ 3 µm thick alumina coatings on corundum ceramic, sodalimesilica glass and Inconel718 were produced from mixtures of boehmite sols and corundum suspensions.
Transmission electron micrographs in combination with electron diffraction and energy dispersive X-ray spectroscopy served to identify crystallographic phases and to characterize the microstructure of the coatings. Using corundum ceramic as substrate the initially deposited boehmite transforms via transition aluminas to corundum while heating to 1200 °C. In the cases of glass and Inconel718 thermal treatments up to 520 °C and 1100 °C, respectively, cause diffusion of ions from the substrates into the coatings. Thus additional oxide phases were formed.
All coatings are free of cracks or delaminations and do not show any directed crystal growth.
Aluminas resulting from sols prepared via a modified Yoldas procedure were studied with differential thermal analysis (DTA), differential thermal gravimetrie (DTG), 27Al nuclear magnetic resonance (27Al MAS NMR) and X-ray diffraction (XRD) concerning their thermal properties, aluminum speciation and phase content.
Hydrolysis of aluminum-sec-butoxide in aluminum nitrate solutions allowed to prepare stable sols with varying NO3-/Al molar ratios, solids contents and pH values. Resulting sols contained different aluminum species including also Al13 polycations. Sol preparation conditions also determined aluminum speciation in solid products obtained after thermal treatments of gels obtained from these sols. Al13 polycations and AlO5 species were found to play an important role for thermally induced transformation from amorphous products via eta-Al2O3 to alpha-Al2O3. Intermediately formed eta-Al2O3 promotes the phase transformation to alpha-Al2O3.
The need for a more efficient coal power plant generation (e.g. oxyfuel technology) results in modified process parameters and enhanced corrosion. To reach the necessary service life of high temperature parts protective coatings may be a sufficient technical solution. A modified Yoldas sol (Al2O3 based) was used to coat X20CrMoV12-1 by spin coating. After appropriate heat treatments transition alumina coatings being about 400 nm thick were obtained. Oxidation studies were carried out in laboratory air at temperatures up to 650 °C for up to 500 h exposure time. In case of the uncoated sample a rough oxide layer formed on the surface and a remarkable weight gain (2.62 mg/cm²) were detected. The sol–gel alumina layer (mainly δ-Al2O3) demonstrated a high protection, i.e. a very low weight gain (0.05 mg/cm²). Diffusion of alloying elements into the coating was observed. No indication of spallation of the coating occurred. Local defects (2 µm–30 µm) in the coating led to the formation of iron-oxide islands.
This work compares thin layers (films) and monoliths prepared from alumina sols with respect to their microstructure, thermal evolution, porosity and specific surface area. After heat treatment at similar temperatures, films and monoliths showed the same qualitative changes in porosity and specific surface area. However, some marked quantitative differences were detected. Film fragments had a lower open porosity, a lower specific surface area and a narrower pore size distribution. Furthermore, the thermal evolution showed a markedly different burnout of organic components between films and monoliths. The observed differences between films and monolith can be explained by the ageing history of the sols during sample preparation.