The residual post-fire mechanical properties of fiber-reinforced epoxy composites are influenced by their fire residues after burning. This study uses intumescent/low-melting glass flame retardants to tailor fire residues in epoxy resin. Processibility of prepregs and their quality are analysed for transfer of the flame-retardant epoxy resins to layered glass-fiber reinforced composites. Minimal effects were found on the pre-fire flexural strengths of the composites due to low loading of the flame retardants. However, when transferred to glass-fiber reinforced composites, the fire residues diminish significantly. Further studies are required to improve theoretical and experimental estimations of the post-fire mechanics of the composites.
Several investigation groups have studied the flame-retardancy modes of action and properties of epoxy resins in the past; nevertheless, the selection of suitable flame retardants for epoxy resins remains challenging, and the transfer to fiber composites is difficult. The addition of flame retardants and glass fibers (GFs) to a polymeric system in a fire scenario changes the polymer's pyrolytic path and burning characteristics, reduces the heat released in the combustion, and suppresses the modes of action in the condensed and gas phase. In this study, the thermal analysis, flammability, fire behavior, residue analysis, fire stability, and quantification of modes of action of three different systems with three halogen-free flame retardants (melamine polyphosphate (MPP), ammonium polyphosphate (APP), and silane ammonium polyphosphate (SiAPP)) and three different types of GFs (unidirectional (UD), bidirectional (BD), and woven roving (WR)) will be compared with pure epoxy resin as a reference.
Fire resistance of fiber-reinforced polymers (FRPs) has been an important area of research for many years since FRPs are mainly used in the transportation and construction sectors. This study presents the fire behavior, and mechanical performance between the flame retarded pure epoxy resin and flame retarded glass-fiber composites before, during, and after a fire event. This enables a deeper understanding of the transferability of flame retardants on composite materials.
The systematic transfer of solvent-free, additive flame retardant (FR) formulations from epoxy resins to glass fiber-reinforced epoxy composites (GFRECs) through prepregs is difficult. Additionally, obtaining data on their post-fire mechanics is often challenging. Utilizing melamine polyphosphate (MPP), ammonium polyphosphate (APP), and silane-coated ammonium polyphosphate (SiAPP) FRs with low-melting inorganic silicates (InSi) in an 8:2 proportion and 10% loading by weight in a diglycidyl ether of bisphenol A (DGEBA) resin, a systematic investigation of the processing properties, room-temperature mechanics, and temperature-based mechanics of the systems was performed. The resin was cured with a dicyandiamide hardener (DICY) and a urone accelerator. The results revealed no substantial impact of these FRs at the current loading on the resin's glass transition temperature or processability. However, the fire residues from cone calorimetry tests of the composites containing FRs were found to be only 15-20% of the thickness of the resins, implying a suppression of intumescence upon transfer. At room temperature, the decrease in the flexural modulus for the composites containing FRs was negligible. Exposure of the composites in a furnace at 400°C as a preliminary study before ignition tests was shown to cause significant flexural moduli reductions after 2.5 min of exposure and complete delamination after 3 min making further testing unviable. This study emphasizes the need for future research on recovering modes of action upon transfer of FR formulations from resins to composites. Based on the challenges outlined in this investigation, sample adaptation methods for post-fire analysis will be developed in a future study.
This study presents the processability, fire behavior, and mechanical performance between the flame retarded pure epoxy resin and flame retarded glass-fiber-reinforced plastic before, during, and after a fire event. This enables a deeper understanding of the transferability of flame retardants, modes of action, char enhancement, and flame inhibition on composite materials