Laser Plasma Hybrid Welding of Austenitic Stainless Steels - Phenomena of Process Instability
(2007)
Laser plasma hybrid welding has been proved to be a very stable hybrid welding process and
welds of high quality can be produced, especially if high surface quality and low spattering is
demanded such as in welding fabrication of high alloyed austenitic stainless steels.
In particular cases, even though welds display high outer quality, X-ray examinations
revealed weld defects which may range from low porosity to blowhole-like cavities. The
phenomena and the main influencing parameters such as arc current, welding speed and
focal point position are discussed. Parameter fields will be suggested for welding plates of
different austenitic stainless steel grades with thicknesses ranging from 3 to 8 mm. The
results are based on welding experiments carried out using a 4.4 kW diode pumped Nd:YAGlaser.
Thus, also the influence of the feeding fibre diameter has been investigated and it was found
that the resulting beam shape has a major effect on the welding performance.
Al-Mg-Si alloys are known to be highly susceptible to solidification cracking except when using an appropriate filler metal (e.g., 4343 or 5356), although the amount of dilution required to avoid cracking has never been a well-defined quantity. The aim of the present study is to determine a relationship between filler metal dilution, local strain rate conditions, and cracking susceptibility. Making use of the controlled tensile weldability (CTW) test and local strain extensometer measurements, a boundary has been established between crack and non-crack conditions for different local strain rates and dilution amounts, holding all other welding parameters constant. This boundary, presented in the form of critical strain rate-dilution map, defines the critical amount of 4043 filler metal required to avoid solidification cracking when arc welding 6060 aluminium, depending upon local strain rate.