Peculiarities of the process of orbital laser-arc welding of thick-walled large-diameter pipes
(2010)
Peculiarities of the process of orbital laser-arc welding of thick-walled large-diameter pipes
(2010)
Full penetration 15 kW Yb fibre laser butt welding of thick AlMg3 (AW 5754) plates was performed in PA position. A contactless inductive electromagnetic weld pool support system was used to prevent gravity dropout of the melt. The welding speed needed to achieve 20 mm penetration was ~0·5 m min-1. An ac power supply of ~244 W at 460 Hz was necessary to completely suppress gravity dropout of the melt and eliminate sagging of the weld pool root side surface. The oscillating magnetic field can suppress the Marangoni convection in the lower part of the weld pool. The system was also successfully used in the full penetration welding of 30 mm thick AlMg3 plates.
New brilliant high-power lasers such as disc laser and fibre laser open up new fields of applications for laser-hybrid welding, e.g. power generation, shipbuilding and pipeline construction. For the use of laser-hybrid welding in pipe laying, insensibility towards tolerances and the possibility of orbital welding are very important factors in addition to the weld seam quality.
Within the scope of a basic research project, first promising results for laser-hybrid welding of thick materials could be demonstrated. As base material, the typical pipeline steel API 5L X65 was selected. With the help of a 20 kW fibre laser in combination with an arc-welding process it was possible to produce high-quality welds in plates of up to 20 mm thickness in a single pass and of up to 32 mm in three to five passes, both welded in position PA. Various joint preparations were examined to weld 20 mm thick plates in one pass. Besides different welding positions, gap bridgeability and misalignment were studied. Results for microhardness and Charpy toughness are presented to proof the applicability of laser-hybrid welding for joining in pipe laying.