Filtern
Erscheinungsjahr
Dokumenttyp
- Posterpräsentation (36)
- Vortrag (30)
- Zeitschriftenartikel (20)
- Beitrag zu einem Sammelband (16)
- Beitrag zu einem Tagungsband (14)
- Forschungsbericht (7)
- Sonstiges (4)
- Buchkapitel (1)
Sprache
- Deutsch (97)
- Englisch (29)
- Mehrsprachig (2)
Schlagworte
- Kulturguterhaltung (14)
- Glasmalerei (13)
- Restaurierung (13)
- Glasanalysen (7)
- Klimamessungen (6)
- Umweltsimulation (5)
- Emission (4)
- Fenster (4)
- Glaszusammensetzung (4)
- Protective glazing (4)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (30)
The initial focus of this research was on the development of a general workflow for the documentation and monitoring of historical stained glass windows using structured light scanning. Therefore windows from different churches, time periods and with different corrosion and damage phenomena were scanned before and after conservation measures. To evaluate the execution of the restoration measures the data was compared using 3D inspection software to examine the differences in geometry between the two scans. Various problems had to be solved, for example, how to deal with heavily reflective surfaces and the extreme contrast between light and dark surfaces, as seen in the borders between ‘Schwarzlot’ painting and plain glass. The application of materials for matting the surfaces, such as Cyclododecane spray, was impossible due to the high accuracy of the surface measurement required for 3D inspection. Regarding the contrast differences of the surfaces, the creation of exposure fusions and the use of polarization filters to reduce reflections were tested. In addition to the general problems encountered when recording translucent surfaces, the historical glasses caused additional problems in calculating surface comparisons. For example, the windows have to be moved and turned around several times, both during the conservation process and while scanning, causing deformations of the geometry due to the flexible lead rods allowing a certain degree of movement.
To improve the adhesives used for restoring stained glass windows, various adhesives were tested and modified. Stained glass windows often show gaps that are too wide to be glued with conventional adhesives, and complementing the gap with spare glass is very time-consuming.
To solve this problem, a filler with improved adhesive strength was developed to bridge wider gaps and cracks. The new filler combines glass adhesives with specially treated glass powder.
Three different glass adhesives were selected and mixed with the specially treated glass powder. The adhesive – glass powder mixture developed was then subjected to accelerated aging and analysed with Fourier transform infrared analysis, scanning electron microscopy, colourimetry, and bending and tensile tests. The results were excellent and the mixture was subsequently used to restore glass windows from four 19th-century churches and chapels. The restoration process was described in conjunction with the advantages of using this approach.
This new adhesive – glass powder mixture provides an adhesive process that can be adapted to the special needs of any object being restored and thus provides a ready answer to the specific damage of each object.
Nach 1850 wurde zur weiteren Herabsetzung der Einbrenntemperatur von Glasmalfarben Borax (Na2B4O7 · 10 H2O) zugesetzt. Das Verhältnis war nun 1 Teil SiO2, 3 Teile PbO und 0,5 Teile Borax. Der analytische Nachweis von Bor in eingebrannten Malschichten war bisher jedoch nicht möglich.Daher wurden in Laborversuchen Glasmalfarben mit unterschiedlichem Gehalt an Borax auf Modellgläser aufgetragen, eingebrannt und anschließend unter simulierten Umweltbedingungen zeitraffend im Klimaschrank bewittert.
Mit Hilfe von elektronenmikroskopischen Untersuchungen können Malschichten charakterisiert werden und somit Hinweise auf mögliche Schadensursachen liefern. Erste Versuche zum Nachweis von Bor erfolgten mit Hilfe von LIBS-Messungen (Laser Induced Breakdown Spectroscopy) an im Labor hergestellten Glasmalfarben mit unterschiedlichem Boraxgehalt.
Nach 1850 wurde zur weiteren Herabsetzung der Einbrenntemperatur von Glasmalfarben Borax (Na2B4O7 · 10 H2O) zugesetzt. Das Verhältnis war nun 1 Teil SiO2, 3 Teile PbO und 0,5 Teile Borax. Der analytische Nachweis von Bor in eingebrannten Malschichten war bisher jedoch nicht möglich.
In Laborversuchen wurden Glasmalfarben mit unterschiedlichem Gehalt an Borax auf Modellgläser aufgetragen, eingebrannt und anschließend unter simulierten Umweltbedingungen zeitraffend im Klimaschrank bewittert. Mit Hilfe von elektronenmikroskopischen Untersuchungen können Malschichten charakterisiert werden und somit Hinweise auf mögliche Schadensursachen liefern. Der Nachweis von Bor erfolgte mit Hilfe von LIBS-Messungen (Laser Induced Breakdown Spectroscopy) an im Labor hergestellten Glasmalfarben mit unterschiedlichem Boraxgehalt.