In fire resistance tests, building elements are considered as stand-alone elements without interaction with the surrounding building. As a contribution to overcome the situation, the application of the substructuring method has been adopted to fire engineering. The paper gives some remarks on the aforementioned experimental method. The analysis is based on the results of two built-in column fire resistance tests, i.e. one test with an unprotected column at the ground floor of the 8-storey steel framed building at Cardington and another test at BAM with an unprotected column and simulated axial restraining stiffness by the substructuring method.
Fire stability of glass-fibre sandwich panels: The influence of core materials and flame retardants
(2017)
Fire resistance has become a key property for structural lightweight sandwich components in aviation, shipping, railway vehicles, and construction. The development of future composite materials and components demands adequate test procedures for simultaneous application of compression and fully developed fire. Therefore an intermediate-scale approach (specimen size = 500 mm x 500 mm) is applied with compressive loads (up to 1 MN) and direct application of a burner to one side of the specimens, as established in aviation for severe burn-through tests. The influence of different core structures (polyvinylchloride foam, polyisocyanorate foam reinforced by stitched glass bridges, and balsa wood) was investigated for glass-fibre-reinforced sandwich specimens with and without flame retardants applied on the fabrics, in the matrix, and on surface for each specimen at the same time. Times to failure were increased up to a factor of 4. The intumescent coating prolongs the time to failure significantly.
What is more, using the intrinsic potential of the front skin together with the core to protect a load bearing back skin in sandwich panels, the design of the core – here using the wood core – is the most promising approach.
In this study, a nonlinear three-dimensional finite element (FE) model was developed and validated to investigate the response of concrete filled tube (CFT) columns subjected to post-earthquake fires. Three steps were considered successively in the modelling, namely, cyclic, thermal and structural analyses. Outputs from the cyclic loading including residual deformationswere imposed as an initial condition to the thermal-stress model, imitating the seismic response of the column. Subsequently, a nonlinear sequentially thermal-stress analysis was conducted to simulate the fire response of column after the earthquake. The proposed FE model was validated by comparing the simulation resultswith the observations of full-scale fire and cyclic tests available in the literature.
The validated numericalmodelwas then used to study the behavior of CFT columns under the combined action of earthquake and fire as a multi-hazard event. Three probable seismic damage scenarios were considered in the column, namely, middle length, bottom and top end region damages. The level of damage was assumed as a high damage level, presuming that the column reached 50% of its lateral resistance while still maintaining ist overall stability after the earthquake. The results showed that the top and bottom end region damages have not significantly influence the fire response of the damaged column. Besides, the column with the middle span damage performed a lesser fire resistance time owing to the coincidence of damage location to that of onset of global buckling.
The composite steel and concrete columns are known to have enhanced fire behaviour when compared with bare steel columns. However there are still aspects that must be clarified, as the influence of the building surrounding structure on the fire resistance of the columns. In this paper, the results of fire resistance tests on partially encased steel columns carried out with two different experimental systems are compared. In one of the experimental systems, the building surrounding structure is materialised by a steel restraining frame, and in the other is performed by the so-called substructuring method. Due to the concept of hybrid substructuring, the entire building is decomposed in two parts: one is represented by the building element under test, whereas the remaining building is simulated numerically in a computer. The main conclusion drawn from this work was that the surrounding structure has a major influence in the development of axial forces in the test columns. Moreover, it was observed that the higher the non-dimensional axial restraint ratio the lower the critical time of the columns.
Thermal restraint effects on the fire resistance of steel and composite steel and concrete columns
(2009)
A systematic approach was used to investigate the weathering-induced degradation of a common water–based intumescent coating. In this study, the coatings are intended for humid indoor applications on steel substrates. The coating contains ammonium polyphosphate, pentaerythritol, melamine, and polyvinyl acetate. By replacing each ingredient with a less water-soluble substance, the most vulnerable substances, polyvinyl acetate and pentaerythritol, were identified. Furthermore, the weathering resistance of the system was improved by exchanging the ingredients. The coatings were stressed by artificial weathering tests and evaluated by fire tests. Thermogravimetry and Fourier-transform infrared spectroscopy were used to study the thermal decomposition. This study lays the foundation for the development of a new generation of water-based intumescent coatings.