Most of the previous studies on reinforced concrete columns with elastically restrained thermal elongation were carried out on square, rectangular or ‘+’-shaped cross sections. The fire resistance of these columns is probably more compromised than in circular columns due to the phenomenon of concrete detachment in the corners of the cross-section. In order to examine the influence of several parameters on the behaviour in fire of circular reinforced concrete columns with restrained thermal elongation, several fire resistance tests were carried out. The parameters tested were load, restraint level, slenderness of the column and the longitudinal reinforcement ratio. In the fire resistance tests the specimens were exposed to the ISO 834 Standard fire curve and the critical time and temperature and failure modes were determined. The test results mainly indicated that the spalling phenomenon may also occur in circular columns and so reducing its fire resistance. The restrained level might not so much relevant concerning the fire resistance of circular reinforced concrete columns.
Most of the previous studies on reinforced concrete columns with elastically restrained thermal elongation were carried out on square, rectangular or '+'-shaped cross sections. The number of fire resistance tests on circular reinforced concrete columns with elastically restrained thermal elongation is still very small. In order to examine the influence of several parameters on the behaviour in fire of this type of columns several fire resistance tests were carried out. The parameters tested were the load and restraint level, slenderness of the column and longitudinal reinforcement ratio. In the fire resistance tests the specimens were exposed to the ISO 834 standard fire curve and the critical time (fire resistance) and temperature and failure modes were determined. The test results showed that the spalling phenomenon may occur in circular columns and so reducing its fire resistance. The increasing of the load level led to a reduction while the increasing of the longitudinal reinforcement ratio or the decreasing of the slenderness of the columns led to an increasing of their fire resistance. The restraint level might not be much relevant on the fire resistance of circular reinforced concrete columns.
Engineering Modelling
(2019)
This chapter presents the most commonly used approach to analyse the
thermo-mechanical behaviour of concrete structures subjected to high temperatures as in the case of fire loading. Prescriptions of the Eurocode are detailed for the thermal as well as the mechanical analysis. Finally, recommendations from two national (Austrian and German) guidelines give some improvements for Underground infrastructure.
Advanced Modelling
(2019)
The recommendation is based on the coauthors’ work organized by the RILEM TC 256-SPF ‘‘Spalling of concrete due to fire: testing and modelling’’. The Committee has defined two types of screening tests for characterization of concrete propensity to fire spalling: Material screening tests and Product screening tests. Definitions of both types of tests are given in the paper. The following recommendations apply to Material screening tests. The material screening tests described in these recommendations are a set of minimum requirements to test concrete spalling propensity (for example, the minimal specimen size). This document covers the aspects of concrete characterization, specimen geometries, storage conditions, test methods and measured parameters.
The recommendation is based on the co-authors’ work organized by the RILEM TC 256-SPF “Spalling of concrete due to fire: testing and modelling”. It aims to provide useful information, guidance and best practices in fire spalling assessment to laboratories that perform large-scale tests based on fire resistance test standards. It provides guidance on the spalling observation techniques during testing, as well as post-test spalling quantification/assessment methods. This document is intended to be used in conjunction with the fire resistance test standards, e.g. EN 1363-1 and ISO 834-1.