Substrukturtechnik - eine hybride Prüfmethode ; Überblick mit Anwendung im Brandingenieurwesen
(1999)
For the evaluation of the fire resistance time of structural elements thermal and mechanical loadings are applied to the specimen. Up to now the monitored data is represented in tabular form and simple plots. In the following a visualization system to show the data in its geometrical context is discussed.
Monitoring of fire damage processes in concrete by pore pressure and acoustic emission measurements
(2011)
This paper presents the combined use of acoustic emission (AE), gas pore pressure and temperature measurements (PT). The simultaneous application of both techniques represents a new methodology in the context of fire spalling and contributes to a better understanding of the mechanisms of fire spalling, particular with regard to the interaction of micro cracking and pore pressure evolution. The study presents fire tests on normal strength concrete specimens with and without reinforcement at ISO Standard fire and at hydrocarbon (HC) fire. Supported by AE-analysis, it can be shown that due to the higher heating rate of the HC-fire in comparison to the ISO Standard fire the damage processes inside the concrete during the exposure are increased combined with augmenting the concrete permeability. As a consequence lower pore pressures were measured. However, despite the lower pore pressures, explosive spalling was observed.
An intermediate-scale fire testing approach on the structural integrity of lightweight materials
(2013)
Carbon or glass über composites and Sandwich structures, the lightweight materials of choice for aviation, naval, offshore and construction show an enormous energy saving potential. Their combination of excellent specific mechanical properties, high corrosive resistance and thermal insulation properties in combination with various adoptable fabrication techniques leading to mass and fuel cost reduction. The most limiting single factor for a wider use of fibre reinforced plastics (FRP) in particular as elements for structural application is believed to be their fire behaviour (Mouritz and Gibson, 2006). FRPs promote burning by themselves consuming the stabilizing polymeric matrix while embedded fibers (glass, carbon) persisting the flame (Mouritz et ah, 2006). Already at elevated temperatures (100 - 200 °C) the matrix softens with a loss in mechanical properties (Perret et al., 2011, Mouritz and Gibson, 2006). For this reason the stability of the structural component is decreased severely. Fire behavior becomes the major hazard to worry about, increasingly demanding targetoriented investigation, suitable testing and tailored development.
Experimental approaches in the bench-scale have been proposed to investigate the structural integrity in the past (La Delfa et al., 2009, Gibson et al., 2010, Seggewiß, 2011, Mouritz and Gardiner, 2002, Schartel et al.). Ascribed to the small-scale neither the mechanical properties nor the effects of fire may be represented satisfactorily. Flence, the task is to perform more realistic investigations under adequate compressive loads in fully developed fires, based on suitable specimen sizes. Also (La Delfa et al., 2009)) have announced that it is evident that larger scale test of composites are needed. The aim of this study is to present a developed intermediate-scale test setup to perform more realistic investigations (Hörold et al.). Mechanical loading is generated by a column furnace in terms of compression due to a more severe response of specimens in fire tests (Seggewiß, 2011, Gibson et al., 2012, Feih et al., 2008, Feih et al., 2007). An oil burner used to determine the burnthrough resistance of thermal/acoustic insulation materials provides fire directly onto one side of the specimen (Federal Aviation Administration, 2003). Generating a fully developed fire the NexGen burner offers a homogenous heat flux of ~ 180 kW/m2. The intermediate-scale is addressed by specimen sizes either 500 x 500 mm or 1000 x 500 mm with a maximum thickness of 50 mm. The specimen attachment is realized by a compression device that was designed to apply the compressive loads, figure 1. The test setup for specimens with component like dimensions allows realistic investigations up to structural failure in absence and presence of fire load. A first test series was carried out with different levels of loading while the fire remained unchanged. Failure mechanisms, temperature distributions, diversity of FRPs regarding fiber, matrix, lay-up and core as well as flame retardant Systems are in the scope of investigation.