Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (56)
- Vortrag (27)
- Beitrag zu einem Tagungsband (26)
- Monografie (3)
- Beitrag zu einem Sammelband (2)
- Buchkapitel (1)
- Posterpräsentation (1)
- Forschungsbericht (1)
Schlagworte
- Fatigue strength (17)
- Fracture mechanics (16)
- Bruchmechanik (11)
- Cyclic R-curve (11)
- Schwingfestigkeit (11)
- Weldments (11)
- Additive Manufacturing (8)
- Fatigue crack propagation threshold (8)
- Short cracks (8)
- Additive manufacturing (7)
Organisationseinheit der BAM
- 9 Komponentensicherheit (68)
- 9.4 Integrität von Schweißverbindungen (66)
- 8 Zerstörungsfreie Prüfung (11)
- 8.5 Röntgenbildgebung (10)
- 9.6 Additive Fertigung metallischer Komponenten (9)
- 9.0 Abteilungsleitung und andere (6)
- 5 Werkstofftechnik (5)
- 5.1 Mikrostruktur Design und Degradation (4)
- 5.5 Materialmodellierung (1)
- 8.3 Thermografische Verfahren (1)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (27)
In order to find a resource efficient approach for the fatigue lifetime prediction of laser powder bed fusion (L-PBF) processed AlSi10Mg material, results of tensile and fatigue tests were compared. The specimens were manufactured with three different L-PBF machines and studied in different heat treatment conditions (as-built, annealed, T6 heat treated). The investigations showed that the high attainable tensile strength properties after the manufacturing process are not beneficial in the high cycle fatigue (HCF) regime. In contrast, the applied heat treatments, which lead typically to a decrease of ultimate tensile strength, improved dramatically the fatigue behavior. Additionally, a clear correlation between the elongation at fracture and HCF resistance has been found for individual heat treatment conditions. This empiric relationship provides an estimation of the fatigue resistance in the presence of material defects and can be implemented in part and process approvals.
Se presenta una guía completa del procedimiento experimental para la determinación del valor umbral ΔKth intrínseco y caracterización de curvas FCGR sobre el acero de alta resistencia S960QL empleando probetas de pequeña escala. El análisis se realiza comparando probetas SENB de diferentes geometrías, distinguiendo entre “convencionales” y “miniatura”. Las primeras con espesor (B) de 6 mm y anchura (W) de 19, y las segundas con B = 3 y dos valores distintos de W, 4 y 6 mm. A fin de identificar el valor umbral ΔKth intrínseco, la relación de cargas (R) aplicada en todos los ensayos fue 0,8. La técnica de caída de potencial (DCPD) se utilizó para la monitorización del tamaño de grieta a lo largo de los ensayos.
La evaluación de los resultados experimentales confirma la equiparación de resultados entre las distintas geometrías y configuraciones de ensayo practicadas, así como la viabilidad de emplear probetas de pequeña escala en la determinación del valor umbral ΔKth intrínseco. Esto abre nuevas perspectivas en lo relativo al empleo de probetas de reducidas dimensiones en la caracterización de materiales a fatiga. A su vez, permite ofrecer una serie de recomendaciones para reproducir con éxito ensayos semejantes utilizando probetas de pequeñas dimensiones de acero y otros materiales metálicos.
The largest percentage of component life under fatigue loading conditions is spent in the short crack regime and in the initial phase of long cracks. The use of Fracture Mechanics in the characterization of fatigue crack growth rate curves has proven to be a useful and adequate tool in the prediction of fatigue lifetimes as long as certain conditions are satisfied. All the above implies the need for a methodical and accurate procedure of assessment of the material response in order to achieve a reliable prediction of lifetime in components under safe conditions, based on the damage tolerance approach. It also highlights the need to analyse the response of increasingly reduced thicknesses, which, as time goes by, show greater differences with respect to those commonly studied and defined in standards and design guidelines, as well as to the experimental studies that can be found in the literature at present. Some examples of thin-walled components are turbine blades or certain additively manufactured parts where, additionally, variations in material properties can occur locally and should also be examined.
This article is an outcome of a workshop on Fatigue of Additive Manufactured Metallic Components jointly organized by the Federal Institute for Materials Research and Testing (BAM) Berlin, Germany and the National Institute of Standards and Technology (NIST) Boulder, CO, U.S.A. The aim of the workshop was a comprehensive discussion of the specific aspects of additively manufactured (AM) components in regard to failure under cyclic loading. Undoubtedly, a better understanding and the further development of approaches for damage tolerant component design of AM parts are among the most significant challenges currently facing the use of these new technologies.
This article presents a thorough overview of the workshop discussions. It aims to provide a review of the parameters affecting the damage tolerance of AM parts with special emphasis on the process parameters intrinsic to the AM technologies, the resulting defects and residual stresses. Based on these aspects, concepts for damage tolerant component design for AM are reviewed and critically discussed.
The safe fatigue design of metallic components fabricated by additive manufacturing (AM) is still a largely unsolved problem. This is primarily due to (a) a significant inhomogeneity of the material properties across the component; (b) defects such as porosity and lack of fusion as well as pronounced surface roughness of the asuilt components; and (c) residual stresses, which are very often present in the as‐built parts and need to be removed by post‐fabrication treatments. Such morphological and microstructural features are very different than in conventionally manufactured parts and play a much bigger role in determining the fatigue life. The above problems require specific solutions with respect to the identification of the critical (failure) sites in AM fabricated components. Moreover, the generation of representative test specimens characterized by similar temperature cycles needs to be guaranteed if one wants to reproducibly identify the critical sites and establish fatigue assessment methods taking into account the effect of defects on crack initiation and early propagation. The latter requires fracture mechanics‐based approaches which, unlike common methodologies, cover the specific characteristics of so‐called short fatigue cracks. This paper provides a discussion of all these aspects with special focus on components manufactured by laser powder bed fusion (L‐PBF). It shows how to adapt existing solutions, identifies fields where there are still gaps, and discusses proposals for potential improvement of the damage tolerance design of L‐PBF components
Additively manufactured components are characterized by heterogeneous mechanical properties due to variations of the microstructure, flaws and residual stresses resulting from the inhomogeneous fabrication process. The large number of influencing factors poses a further challenge in understanding the correlation between material properties, process parameters and component geometry. Therefore, the qualification of components based on witness specimens produced within the same job is questionable. This work aims to present a new strategy for the characterization of PBF-LB/M components based on representative specimens. The key assumption is the feasibility of a transfer of the thermal history from a component to a specimen. It is assumed that similar material properties are determined for components and specimens produced adopting a similar thermal history. After the definition of a region of interest in the component, a combination of thermal analyses by means of finite elements and in-situ experimental determination of the thermal history through infrared thermography is used to produce test coupons with a similar thermal history. The effectiveness of the procedure is demonstrated on a pressure vessel for applications in the chemical industry.
La tecnología de fabricación aditiva (AM) continúan progresando y permitiendo alcanzar diseños cada vez más complejos y optimizados. La industria química es uno de los sectores donde componentes AM han adquirido un gran interés. La falta hasta la fecha de una directiva europea que regule la inspección, certificación y aceptación de equipos sometidos a presión hace necesario progresar en esta línea. El objetivo que se persigue en este trabajo es el de desarrollar una metodología de diseño sobre componentes fabricados aditivamente basada en la estimación de vida a fatiga de las zonas más susceptibles de sufrir dicho tipo de fallo. El estudio comprende diversas facetas de análisis, simulaciones numéricas, análisis de la microestructura del material y una extensa campaña experimental. La evaluación de la integridad estructural se realiza aplicando mecánica de fractura. La historia térmica a lo largo del proceso de fabricación determina la microestructura del componente en cada región y, por ende, influye en las propiedades mecánicas en cada una. Se presentan los resultados preliminares de un proyecto de investigación en curso dirigido a la caracterización de propiedades mecánicas en recipientes de presión producidos por fusión láser en lecho de polvo (L-PBF, por sus siglas en inglés) de acero inoxidable 316L. Se detallan los resultados preliminares en términos de velocidad de crecimiento de grietas por fatiga (FCGR), y se comparan los resultados de probetas extraídas de diferentes regiones de los depósitos.