A bottom-up approach is presented for the production of arrays of indium islands on a molybdenum layer on glass, which can serve as micro-sized precursors for indium compounds such as copper-indium-gallium-diselenide used in photovoltaics. Femtosecond laser ablation of glass and a subsequent deposition of a molybdenum film or direct laser processing of the molybdenum film both allow the preferential nucleation and growth of indium islands at the predefined locations in a following indium-based physical vapor deposition (PVD) process. A proper choice of laser and deposition parameters ensures the controlled growth of indium islands exclusively at the laser ablated spots. Based on a statistical analysis, these results are compared to the non-structured molybdenum surface, leading to randomly grown indium islands after PVD.
A procedure to fabricate CuInSe2 (CISe) micro-absorbers and solar cells for concentrator applications is presented. The micro-absorbers are developed from indium precursor islands, which are deposited on a molybdenum coated glass substrate (back contact), followed by deposition of copper on top and subsequent selenization as well as selective etching of copper selenides. In order to compare the properties of the locally grown absorbers to those of conventional large area CISe films, we systematically examine the compositional and morphological homogeneity of the micro absorbers and carry out photoluminescence measurements. Preliminary devices for micro-concentrator solar cell applications are fabricated by optimizing the copper to indium ratio and the size of the indium precursor islands. The resulting micro solar cells provide a characteristic I–V curve under standard illumination conditions (1 sun).
The Spray Ion Layer Gas Reaction (Spray-ILGAR) technique is a new variation on the ILGAR technique used to prepare chalcogenide thin films. High quality indium sulfide thin films were produced by Spray-ILGAR with an indirect bandgap of 2.2 eV and a high suitability for use as buffer layers in chalcopyrite solar cells. The process involves the cyclical spray deposition of an indium containing precursor layer followed by its conversion to sulfide using hydrogen sulfide gas. Analysis of the deposition reveals that the indium chloride based precursor is transported via the vapour phase from the spray droplets to the substrate surface.
Ultra-thin In(OH)x Sy/Pb(OH)x Sy heterostructures were formed by the wet chemical SILAR (successive ion layer adsorption and reaction) technique. ERDA (elastic recoil detection analysis) was used for stoichiometry analysis. The heterocontacts were conditioned by joint annealing of the two layers at different low temperatures in air. The charge selectivity was demonstrated with various small area solar cell structures. The results are discussed on the base of formation of bonds between sulphide clusters and passivation of defects with hydrogen containing species in hydroxy-sulphides.