CCQM-K143 is a key comparison that assesses participants’ ability to prepare single element calibration solutions. Preparing calibration solutions properly is the cornerstone of establishing a traceability link to the International System of Units (SI), and therefore should be tested in order to confirm the validity of CCQM comparisons of more complex materials. CCQM-K143 consisted of participants each preparing a single copper calibration solution at 10 g/kg copper mass fraction and shipping 10 bottled aliquots of that solution to the coordinating laboratory, the National Institute of Standards and Technology (NIST). The masses and mass fraction for the prepared solutions were documented with the submitted samples.
The solutions prepared by all participants were measured at NIST by high performance inductively coupled plasma optical emission spectroscopy (HP-ICP-OES). The intensity measurements for copper were not mapped onto values of mass fraction via calibration. Instead, ratios were computed between the measurements for copper and simultaneous measurements for manganese, the internal standard, and all subsequent data reductions, including the computation of the KCRV and the degrees of equivalence, were based on these ratios. Other than for two participants whose measurement results appeared to suffer
from calculation or preparation errors, all unilateral degrees of equivalence showed that the measured values did not differ significantly from the KCRV. These results were confirmed by a second set of ICP-OES measurements performed by the Physikalisch-Technische Bundesanstalt (PTB). CCQM-K143 showed that participants are capable of preparing calibration solutions starting from high purity, assayed copper metal.
Similar steps are involved when preparing solutions for other elements, so it seems safe to infer that similar capabilities should prevail when preparing many different, single-element solutions.
The CCQM-K88 key comparison was organized by the Inorganic Analysis Working Group of CCQM to test the abilities of the national metrology institutes to measure the mass fraction of lead in lead-free solder containing silver and copper. National Metrology Institute of Japan (NMIJ), National Institute of Metrology of China (NIM) and Korea Research Institute of Standards and Science (KRISS) acted as the coordinating laboratories. The participants used different measurement methods, though most of them used inductively coupled plasma optical emission spectrometry (ICP-OES) or isotope-dilution inductively coupled plasma mass spectrometry (ID-ICP-MS). Accounting for relative expanded uncertainty, comparability of measurement results was successfully demonstrated by the participating NMIs for the measurement of the mass fraction of lead in lead-free solder at the level of 200 mg/kg.
It is expected that metals at mass fractions greater than approximately 100 mg/kg in lead-free solder containing silver and copper can be determined by each participant using the same technique(s) employed for this key comparison to achieve similar uncertainties mentioned in the present report.
Ultra-thin In(OH)x Sy/Pb(OH)x Sy heterostructures were formed by the wet chemical SILAR (successive ion layer adsorption and reaction) technique. ERDA (elastic recoil detection analysis) was used for stoichiometry analysis. The heterocontacts were conditioned by joint annealing of the two layers at different low temperatures in air. The charge selectivity was demonstrated with various small area solar cell structures. The results are discussed on the base of formation of bonds between sulphide clusters and passivation of defects with hydrogen containing species in hydroxy-sulphides.
The solubility of carbon dioxide in three ionic liquids (ILs) under supercritical fluid condition was measured at pressures up to 32 MPa and at temperatures of 313.15, 323.15, and 333.15 K in a high-pressure view cell. The imidazolium-derivative ionic liquids 1-butyl-3-methylimidazolium hexafluorophosphate ([bmim][PF6]), 1-butyl-3-methylimidazolium tetrafluoroborate ([bmim][BF4]), and 1-octyl-3-methylimidazolium tetrafluoroborate ([omim][BF4]) were employed in this research. The effects of pressure, temperature, nature of anion and cation as well as the water content on the solubility of CO2 in the ILs were investigated experimentally. The solubility of CO2 in the IL was higher for the ILs with longer cationic alkyl group and for the ILs with lower anion polarity. The lower the water content or the lower the temperature as well as the higher the pressure, the higher was the solubility of CO2.