Schlagworte
- MOUSE (2) (entfernen)
Organisationseinheit der BAM
- 6 Materialchemie (2) (entfernen)
Large, ink-bottle-shaped pores in mesocellular foams (MCFs) are desired for various applications requiring enhanced mass transfer or the immobilization of larger compounds. Hence, the cylindrical pores of COK-12, an ordered mesoporous silica structurally comparable to SBA-15 but synthesized at room-temperature at quasi-neutral pH, are chemically swollen into ink-bottle pores. Therefore, p-xylene is used as a more sustainable swelling agent compared to popular alternatives. Its high boiling point allows for an additional thermal aging step to amplify the mesostructure enlargement without needing additional chemicals. For COK-12, the MCFs obtained at room temperature reach an unprecedented plateau for the modal mesopore cell and window diameter of 19.9 and 5.5 nm, respectively, with an underlying broad pore size distribution and distorted hexagonal lattice up to 14.5 nm, involving hexagonal and spherical structures. The combined chemical and thermal swelling resulted in the selective enlargement of the window diameter to more than 200% and a slightly increased cell diameter, pore size distribution, and hexagonal lattice distortion in comparison to the room temperature synthesis. Such materials are thought to be promising alternatives to SBA-15-based MCFs, often utilizing toxic catalysts during synthesis. The presented results pave the way for enhanced adsorptive, catalytic, and drug delivery performances for COK-12-based materials.
Hierarchically porous, high‐surface‐area silica materials are excellent candidates for multiple applications like catalysis and environmental remediation. Shaping these materials with additive manufacturing (AM) techniques, like robocasting, could enable their use with the benefit of on‐demand, customized shaping and maximizing performance. Herein, ordered mesoporous silica COK‐12 slurries were robocasted into monoliths, containing different ratios of uncalcined COK‐12 and sodium bentonite (0–25 wt.%). The rheology of the mixed slurries is characterized by lower flow indexes (0.69 vs. 0.32) and higher yield stresses (96 vs. 259 Pa) compared to pure COK‐12 ones. Monoliths were printed in woodpile structures and calcined at 600°C. Micro‐CT measurements showed a linear shrinkage of 25% after calcination. Mechanical characterization showed increased uniaxial strength (0.20 ± 0.07 to 1.0 ± 0.3 MPa) with increasing binder/solids ratio from 13 to 25%. The amorphous, mesoporous structure of COK‐12 was retained. The structures exhibited open porosities of 52 ± 4% and showed higher specific mesopore volumes, and increased average mesopore size (6 vs. 8 nm) compared to COK‐12. Small‐angle x‐ray scattering analysis revealed an increased lattice parameter (10.3 vs. 11.0 nm) and reduced wall thickness (3.1 nm vs. 4.1 nm) of the COK‐12 in the monoliths. These properties indicate suitability for their application as porous supports and adsorbents.