The material properties of recycled concrete aggregates (RCA) are
correlated to the sorting accuracy of the former demolition waste. Impurities like
wood, clay bricks or gypsum can lead to inferior building material properties. Harmful
substances like heavy metals or organic pollutants should be minimised as well.
Hence the non-concrete materials have to be separated from the concrete material
stream. This can be done during the demolition process by using selective
dismantling techniques. Alternatively a variety sorting and classifying techniques to
purify the crushed concrete can be utilized.
A research project, funded by the Federal Ministry for the Environment, Nature
Conservation and Nuclear Safety, investigated the possibilities of gaining recycled
concrete aggregates of a high quality for the reuse in the production of concrete. The
work focuses especially on how gypsum respectively sulphates in the crushed
concrete can be reduced. Sulphates can impair the setting behaviour of concrete
and also damage set concrete by causing expansion. Therefore the content of
sulphates in RCA is restricted by guidelines and standards in Germany.
Generally, gypsum in construction waste originates from interior fittings like gypsum
walls, floor screeds, plaster boards and also plaster. Most of these materials can be
reconstructed using selective dismantling techniques. This can be achieved either by
manual labour or by using mechanical equipment e.g. to remove floor screeds by
milling. Depending on the specific deconstruction site it can be more effective and/or
more environmentally compatible to remove sulphates by treating the crushed
concrete. Applicable treatments for sulphate reduction include dry processes like
manual sorting of gypsum wall blocks as well as wet treatments e.g. jigging.
In addition this research project an environmental performance evaluation was
undertaken to assess different techniques for reducing sulphates in recycled
concrete aggregates.
Concrete is one of the most widely used construction materials and, accordingly, the concrete industry is an important stakeholder in the field of sustainable construction. Therefore various approaches have been implemented to increase the sustainability of concrete. Besides reducing CO2-emissions during cement production, increasing the energy efficiency of buildings and extending their life span, the end-of-life performance of concrete is also an essential aspect of sustainability. Reusing concrete as a secondary building material meets the requirements of sustainability in several ways: the extended time availability of primary raw materials and, thereby, the protection of natural resources as well as conserving landfill site. Furthermore, the production of recycled concrete aggregates (RCA) is a good example for closed-loop recycling.
However, regarding the use of RCA as a substitute for natural aggregates in concrete, attention must be paid to all issues of sustainability: this means that environmental, economic and social aspects have to be considered. Since RCA generally have inferior building material properties, such as higher porosity and lower density, the implementation of closed-loop recycling of concrete only makes sense if the technical quality assurance is secured. This paper focusses on the implementation of techniques for the deconstruction/demolition of buildings and the subsequent treatment of concrete rubble in order to improve the building material properties of RCA with regard to the requirements of sustainability and also technical rules and standards.
Concrete is one of the most widely used construction materials and, accordingly, the concrete industry is an important stakeholder in the field of sustainable construction. Therefore various approaches have been implemented to increase the sustainability of concrete. Besides reducing CO2-emissions during cement production, increasing the energy efficiency of buildings and extending their life span, the end-of-life performance of concrete is also an essential aspect of sustainability. Reusing concrete as a secondary building material meets the requirements of sustainability in several ways: the extended time availability of primary raw materials and, thereby, the protection of natural resources as well as conserving landfill site. Furthermore, the production of recycled concrete aggregates (RCA) is a good example for closed-loop recycling.
However, regarding the use of RCA as a substitute for natural aggregates in concrete, attention must be paid to all issues of sustainability: this means that environmental, economic and social aspects have to be considered. Since RCA generally have inferior building material properties, such as higher porosity and lower density, the implementation of closed-loop recycling of concrete only makes sense if the technical quality assurance is secured. This paper focusses on the implementation of techniques for the deconstruction/demolition of buildings and the subsequent treatment of concrete rubble in order to improve the building material properties of RCA with regard to the requirements of sustainability and also technical rules and standards.
Due to the large quantities of construction and demolition waste (CDW) in Europe, its reuse or recycling is of particular importance. Although several countries already recycle high amounts of CDW, the use as secondary raw materials is often limited by inferior building material properties. Specific characteristics, like high porosity and low density are caused by hardened cement paste in crushed concrete and the content of mortar and plaster in brick debris. Impurities like wood or gypsum and also harmful substances like organic pollutants may be a major problem for a reuse and should be minimized. Therefore unwanted materials and impairing substances have to be separated from the secondary building material stream. This can be done during the demolition process by using techniques for selective dismantling or during the subsequent treatment of the resulting rubble. Since almost all processing steps are associated with environmental impacts, the benefits of saving natural resources by applying secondary building materials should be weighed carefully. An environmental performance evaluation was undertaken to assess different techniques for reducing gypsum in recycled concrete aggregates, aiming at a minimization of elutable sulfates. These results were compared to the environmental impacts of the extraction of natural aggregates for concrete.
Advantages of recycling gypsum plaster boards
During the last decades the material composition of buildings has become increasingly diverse. However, largely sorted material flows are needed for generating high quality secondary building materials. The use of secondary building materials can meet the requirements of sustainability in several ways: the extended time availability of primary raw materials and, thereby, the preservation of natural resources as well as the conservation of landfill sites.
Recycling of gypsum (calcium sulfate) can be a good example for the environmental benefits of closed-loop recycling. The content of sulfates in other secondary building materials, in particular in recycled concrete aggregates, should be minimized for quality reasons. In contrast, separated gypsum can also be used in gypsum production if the high quality requirements for the recycled gypsum are met. Since almost all processing steps in the recycling process are associated with environmental impacts, an environmental evaluation of the use of recycled gypsum as a substitute in gypsum production has to be carefully conducted.
This paper focusses on the techniques for generating recycled gypsum from gypsum plasterboards, the related quality requirements and a comprehensive environmental evaluation of the complete process.
During the last decades the material composition of buildings has become increasingly diverse. However, largely sorted material flows are needed for generating high quality secondary building materials. The use of secondary building materials can meet the requirements of sustainability in several ways: the extended time availability of primary raw materials and, thereby, the preservation of natural resources as well as the conservation of landfill sites.
Recycling of gypsum (calcium sulfate) can be a good example for the environmental benefits of closed-loop recycling. The content of sulfates in other secondary building materials, in particular in recycled concrete aggregates, should be minimized for quality reasons. In contrast, separated gypsum can also be used in gypsum production if the high quality requirements for the recycled gypsum are met. Since almost all processing steps in the recycling process are associated with environmental impacts, an environmental evaluation of the use of recycled gypsum as a substitute in gypsum production has to be carefully conducted.
This paper focusses on the techniques for generating recycled gypsum from gypsum plasterboards, the related quality requirements and a comprehensive environmental evaluation of the complete process.
The use of secondary building materials can meet the requirements of sustainability in several ways: the extended time availability of primary raw materials and, thereby, the protection of natural ressources as well as the conservation of landfill sites. Regarding the predicted decrease of gypsum supply in Germany, particularly the recycling of gypsum (calcium sulfate) is of growing importance. Currently, the gypsum demand is fulfilled (at least 60%) by gypsum as side product from coal-fired power plants (FGD Gypsum). Germany’s natural gypsum deposits fulfil the remaining gypsum demand. Due to national climate protection goals the gypsum supply from coal power plants will decrease significantly in the future.
In addition, the content of sulfates in other secondary building materials, in particular in recycled concrete aggregates, should be minimized for quality reasons. Separated gypsum can be used in gypsum production if the high quality requirements for recycled gypsum are met. Accordingly, there have been significant advancements in the processing of gypsum residues in the last years. Since almost all processing steps in the recycling process are associated with environmental impacts, an evironmental evaluation of the use of recycled gypsum as a substitute in gypsum production has to be carefully conducted.
The presentation focusses on the techniques for generating recycled gypsum from gypsum plaster boards, the related quality requirements and a comprehensive environmental evaluation of the complete process.
Here, we show that calcium sulfate dihydrate (gypsum) can be directly, rapidly and reversibly converted to calcium sulfate hemihydrate (bassanite) in high salinity solutions (brines). The optimum conditions for the efficient production of bassanite in a short time (<5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the better-known behaviour of the bassanite phase in low-salt environments. In low-salinity aqueous solutions, bassanite is considered to be metastable with respect to gypsum and anhydrite, and therefore gypsum-to-bassanite conversion does not occur in pure water. Interestingly, the high-salinity transformation of gypsum-to-bassanite has been reported by many authors and used in practice for several decades, although its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures was inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline phase for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios.