The potential of lowered surface features as well as the application of wear resistant coatings have been known for many years to improve the tribological behavior of forming tools. More recent studies also discuss the capability of protruded microfeatures for adjusting the tribological behavior between contacting surfaces. The demand for a high wear resistance of such structures as well as their economical and reliable production, however, often limits the industrial application. The laser implantation process can overcome these limitations. In contrast to conventional cw-laser dispersing processes, where the formation of uniform metal matrix composite layers is intended, this surface engineering technique aims to improve the tribological behavior of contacting surfaces by a localized dispersing of pre-placed hard ceramic particles. This enables the formation of deterministic textures composed of separated wear resistant dome- or ring-shaped microstructures (implants).
Since TaC shows very promising material properties for improving the wear resistance of tools exposed to severe operating conditions, this paper analyzes its suitability for pulsed laser implantation on X38CrMoV5-3 tool steel for the first time. In the experiments, the influence of the particles and the laser parameters (pulse power, pulse duration and focal diameter) on the material properties of the localized dispersed zones was studied by optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy and X-ray diffraction. The composite´s (micro-) hardness was measured and calculated by using a rule of mixture. Additionally, the influence of the laser parameters and the TaC particles on the geometrical properties of the implants was studied by optical microscopy and white light interferometry.
The results showed that defect-free implants with hardness values of ~900 HV1 can be obtained at the focal spot, since a localized dispersing of the TaC particles is possible using a pulsed millisecond laser. However, in dependence of the laser intensity, also a partial dissolution of the initial particles occurs. This leads to the precipitation of new dendritic TaC nanoparticles and to varying contents of retained austenite in the matrix. Both effects have a strong influence on the implant hardness and must be considert by the rule of mixture. Regarding the geometrical response it was pointed out that protruded microfeatures with heights up to 10 µm can be created. In comparison to laser remelted zones, the implanted zones showed significantly altered weld pool profiles due to the influence of the particles on the melt convection. A transition of the implant shape from predominantly dome-shaped to predominantly ring-shaped was observed for intensities >1.7∙106 W/cm2 due to the onset of the keyhole effect.
The paper describes a systematic investigation of the EM influenced laser beam welding of the aluminum die casting alloy AlSi12(Fe) in comparison to a reference material, a wrought aluminum alloy AlMg3. By using of a face centred CCD test plan, the influencing variables laser power, welding velocity and magnetic flux density are varied with regard to their influence on the remaining porosity. The global pore fraction of the weld seams was analyzed by X-ray images with ImageJ. This enabled a qualitatively very good regression model to be derived for the respective material, which identifies the dominant influencing variables. The results prove, statistically verified, for the investigated parameter range, that
- the magnetic flux density is the main cause for the porosity reduction,
- the porosity rises with increasing laser power the porosity in the weld seams rises,
- the influence of the welding velocity is negligible,
- the pore quantity in wrought alloy is more strongly minimized by the magnetic flux density than in die casting,
- the porosity decreases due to the EM influence by approx. 70 % compared to the unaffected welds. This effect is emphasized by the contour line charts, which illustrate the relationship between laser power and magnetic flux density.
With the exception of the quadratic influence of B at the wrought alloy, the statistical correlation shows a linear development of the respective influence variables for both aluminum alloys. In order to investigate these deviations, further simulations with a focus on weld pool geometry and weld pool flow are to be performed. In addition, the welding results can be classified in accordance with DIN EN ISO 13919-2 in the highest evaluation group B for AlMg3 and in evaluation group C for AlSi12(Fe) by applying a magnetic flux density of 350 mT. The analysis of the CT images at constant laser power and welding velocity allows a direct comparison both between the two alloys and also as a function of the magnetic flux density with regard to the number and size of pores. An increase in the magnetic flux density leads to a significant decrease in the number and volume of pores, which can be seen more clearly in wrought alloy than in die casting. Very acceptable results can be achieved for both materials and different welding parameters. This successfully demonstrates the desired process robustness and functionality of the EM system for practical applications. For subsequent investigations of overlap joints, the lowest possible laser power and a high magnetic flux density are recommended.
Localized laser surface treatments are able to produce tailor-made surface properties to fulfill requirements of a variety of technical applications. Especially micrometric surface topologies can be beneficial for optimizing tribological contact situations. Structures with lowered surface features are already utilized for bearings or cylinders of combustion engines. There are also other fields of application, where the potential of protruding surface features is known, e. g. for metal forming tools.
A promising approach for a tailored surface treatment working in the microsecond range is the localized dispersing of hard ceramic particles by pulsed laser radiation, the so-called laser implantation. This technique is able to produce micrometric surface structures and to improve simultaneously the wear resistance by creating metal matrix composites.
In this talk, the laser implantation technique is described and compared to the state of the art. The potential to adjust the geometry as well as the mechanical properties of laser implanted surfaces is demonstrated by means of microstructural and topographical investigations of different ceramic materials and steel substrates. Finally, results of research projects are presented aiming on the application of such structured surfaces. Their capability to change and optimize friction and wear are demonstrated for fully lubricated contacts, tools for hot sheet metal forming and tools for cold rolling of sheets for automotive applications.
The laser implantation–named technique aims to address the tribological problems frequently seen on tool surfaces during hot stamping. It is based on the creation of elevated dome- or ring-shaped hard structures on the surface of tool steels by a localized dispersing of hard particles. Therefore, a combination of the two distinct approaches that are normally used in surface Technology for optimizing friction and wear, i.e., surface texturing and surface material optimization, are realized in one processing step. In experimental studies, a localized dispersing of TiB2 particles in the surface layer of the hot work tool steel X38CrMoV5-3 was considered and compared with punctual laser–remelted textures. The structures (micro-) hardness was measured at top- and cross-sections. With the aid of a scanning electron microscope, energy dispersive X-ray spectroscopy and X-ray diffraction the interaction between the hard particles and the substrate material were studied. From the results, an optimal parameter range was identified for laser implantation. To the investigation’s end, the implant geometry was measured by optical microscopy and White light microscopy. Furthermore, a mathematic model was introduced, which allows a prediction of the implant geometry as a response to the laser parameters. It was shown that the implantation of TiB2 particles leads to a significant hardness increase up to 1600 HV1 due to the dispersion of initial particles and an in situ precipitation of new titanium-rich phases. It was possible to create defect-free dome- and ring-shaped microstructures on the surfaces. It was also shown that the implants geometry highly depends on the applied laser parameters. The applied central composite design shows a good agreement with the experimental results.
The laser implantation technique bases on a localized dispersing of ceramic particles in metallic surface layers for changing their micro geometry as well as their material properties. Using TiB2 and NbC hard particles, tailored microtextures consisting of elevated dome-, ring-, or line-shaped Features can be manufactured. Especially TiB2 implants feature high hardness values up to 1800 HV1 and ceramic particle contents up to 55 %, indicating superior wear resistant properties.
In this paper, titanium-di-boride is dispersed on a cold-working tool steel by use of a pulsed fiber laser with high beam quality to produce separated and elevated surface features. The potential to adjust the geometry as well as the mechanical properties of the produced structures in dependence on the process parameters (pulse power, pulse duration) is described by means of metallographic and topographical investigations. It can be ascertained that very hard (hardness > 1000 HV1) surface features of different shape (spots and short lines) can be produced. They are characterized by a fine-grained microstructure resulting from a rapid solidification and finely dispersed TiB2 particles. Finally, the paper proposes different applications for this structuring technique.
In this paper, titanium-di-boride is dispersed on a cold-working tool steel by use of a pulsed fiber laser with high beam quality to produce separated and elevated surface features. The potential to adjust the geometry as well as the mechanical properties of the produced structures in dependence on the process parameters (pulse power, pulse duration) is described by means of metallographic and topographical investigations. It can be ascertained that very hard (hardness > 1000 HV1) surface features of different shape (spots and short lines) can be produced. They are characterized by a fine-grained microstructure resulting from a rapid solidification and finely dispersed TiB2 particles. Finally, the paper proposes different applications for this structuring technique.
AISI D2 is one of the most applied cold-working tool steel for deep drawing operations, due to the materials good toughness and high wear resistance. However, since the lubricant-free deep drawing as well as the processing of high strength and ultra-high strength steel sheets remaining ongoing trends in the automotive industry, the tool surfaces need to be improved regarding their friction and wear behavior. For this purpose elevated micro textures can be applied. Since protruded micro features are predominantly affected by wear, a structuring process enabling the formation of suitable textures with high wear resistance is needed.
In this paper surface texturing at microscale was conducted by laser implantation. This technique allows the fabrication of highly wear resistant, separated and elevated features (implants) on steel surfaces via a discontinuous dispersing of ceramic particles by pulsed laser radiation. The aim of this study was to investigate the techniques potential for the creation of wear resistant elevated micro features on AISI D2 tool steel surfaces by the application of TiB2 particles. The laser parameters (pulse power and length) were varied and a comparative material analysis on AISI D2 laser remelted spots and TiB2 localized dispersed zones was examined. High-speed camera recordings allowed the description of the particle insertion mechanism from pre-coatings during laser processing. Mechanical properties were analyzed by (micro-) hardness measurements at top and cross sections. The microstructure was investigated by optical microscopy, scanning electron microscopy (SEM), energy dispersive Xray
spectroscopy (EDX) and X-ray diffraction (XRD). The implants geometrical properties (diameter, height, depth) were investigated by white light interferometry and optical microscopy. The experiments reveal that a pulsed laser remelting of AISI D2 leads to a significant hardness drop due to high retained austenite (γR) contents. Contrary, a localized dispersing of TiB2 particles leads to defect free dome- or ring-shaped elevated features with hardness values up to 1800 HV1. The high hardness values result from the dispersed TiB2 particles and an in-situ precipitation of new hard particle phases, which lead to a reduction of the γR content within the matrix.