Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (44)
- Beitrag zu einem Tagungsband (34)
- Vortrag (15)
- Posterpräsentation (2)
- Buchkapitel (1)
Sprache
- Englisch (73)
- Deutsch (21)
- Mehrsprachig (1)
- Spanisch (1)
Schlagworte
- Additive manufacturing (19)
- Laser implantation (18)
- Laser powder bed fusion (17)
- Additive Fertigung (11)
- Additive Manufacturing (9)
- Laser beam welding (9)
- TiB2 (9)
- Surface structuring (7)
- Surface texturing (7)
- AISI D2 (6)
Organisationseinheit der BAM
- 9 Komponentensicherheit (81)
- 9.6 Additive Fertigung metallischer Komponenten (42)
- 9.3 Schweißtechnische Fertigungsverfahren (39)
- 8 Zerstörungsfreie Prüfung (20)
- 8.0 Abteilungsleitung und andere (15)
- 8.5 Röntgenbildgebung (9)
- 9.4 Integrität von Schweißverbindungen (9)
- 5 Werkstofftechnik (6)
- 5.1 Mikrostruktur Design und Degradation (5)
- 4 Material und Umwelt (3)
Eingeladener Vortrag
- nein (15)
Micrometric surface topologies are required for a wide range of technical applications. While lowered surface features have been used for many years to improve the tribological behavior of contacting surfaces, there are also other fields of application, where the potential of elevated surface features is known, e. g. for metal forming tools. However, the demand for a high wear resistance of these structures often inhibits an industrial application. A solution is offered by structuring techniques that use additional material. A promising approach is the localized dispersing of hard ceramic particles by pulsed laser radiation, the so-called laser implantation. This paper describes the potential to adjust the geometry as well as the mechanical properties of laser implanted surfaces by means of microstructural and topological investigations. Afterwards, results of a wear test are given. It can be shown that dome-shaped or ring-shaped structures on a micrometric scale can be produced with high hardness and wear resistance.
Skin-pass rolling is a substantial process step in the production line of sheet material for automotive applications. Textured rolls are used to emboss an immaterial surface structure on sheets for improving their formability in subsequent deep drawing operations. In this paper, state of the art techniques for texturing skin-pass rolls are discussed in order to assess their ability to meet optimal tribological parameters. Two main problems are identified: firstly, structured rolls are affected by ongoing wear limiting the operating time and necessitates perpetual maintenance. Secondly, state of the art techniques are not able to exploit the theoretically known potential of immaterial surface structures for enabling micro-lubrication mechanisms due to geometrical inadequacies.
Based on these findings, a new approach for texturing of skin-pass rolls is introduced. The technique uses a localised dispersing of hard ceramic particles by use of pulsed laser radiation. It is shown in this paper that this technique allows the creation of elevated structures with high hardness on the surface of 1.2379 cold-working steel. The wear behaviour of such textured rolls was investigated in a lubricated twin-disc-test. The experiments show that no significant wear of the laser produced structures occur during the test duration. The observed results lead to the assumption that the proposed technique allows the creation of skin-pass roll structures with significantly higher durability.
This article is an outcome of a workshop on Fatigue of Additive Manufactured Metallic Components jointly organized by the Federal Institute for Materials Research and Testing (BAM) Berlin, Germany and the National Institute of Standards and Technology (NIST) Boulder, CO, U.S.A. The aim of the workshop was a comprehensive discussion of the specific aspects of additively manufactured (AM) components in regard to failure under cyclic loading. Undoubtedly, a better understanding and the further development of approaches for damage tolerant component design of AM parts are among the most significant challenges currently facing the use of these new technologies.
This article presents a thorough overview of the workshop discussions. It aims to provide a review of the parameters affecting the damage tolerance of AM parts with special emphasis on the process parameters intrinsic to the AM technologies, the resulting defects and residual stresses. Based on these aspects, concepts for damage tolerant component design for AM are reviewed and critically discussed.
The safe fatigue design of metallic components fabricated by additive manufacturing (AM) is still a largely unsolved problem. This is primarily due to (a) a significant inhomogeneity of the material properties across the component; (b) defects such as porosity and lack of fusion as well as pronounced surface roughness of the asuilt components; and (c) residual stresses, which are very often present in the as‐built parts and need to be removed by post‐fabrication treatments. Such morphological and microstructural features are very different than in conventionally manufactured parts and play a much bigger role in determining the fatigue life. The above problems require specific solutions with respect to the identification of the critical (failure) sites in AM fabricated components. Moreover, the generation of representative test specimens characterized by similar temperature cycles needs to be guaranteed if one wants to reproducibly identify the critical sites and establish fatigue assessment methods taking into account the effect of defects on crack initiation and early propagation. The latter requires fracture mechanics‐based approaches which, unlike common methodologies, cover the specific characteristics of so‐called short fatigue cracks. This paper provides a discussion of all these aspects with special focus on components manufactured by laser powder bed fusion (L‐PBF). It shows how to adapt existing solutions, identifies fields where there are still gaps, and discusses proposals for potential improvement of the damage tolerance design of L‐PBF components
Additively manufactured components are characterized by heterogeneous mechanical properties due to variations of the microstructure, flaws and residual stresses resulting from the inhomogeneous fabrication process. The large number of influencing factors poses a further challenge in understanding the correlation between material properties, process parameters and component geometry. Therefore, the qualification of components based on witness specimens produced within the same job is questionable. This work aims to present a new strategy for the characterization of PBF-LB/M components based on representative specimens. The key assumption is the feasibility of a transfer of the thermal history from a component to a specimen. It is assumed that similar material properties are determined for components and specimens produced adopting a similar thermal history. After the definition of a region of interest in the component, a combination of thermal analyses by means of finite elements and in-situ experimental determination of the thermal history through infrared thermography is used to produce test coupons with a similar thermal history. The effectiveness of the procedure is demonstrated on a pressure vessel for applications in the chemical industry.
For the wide acceptance of the use of additive manufacturing (AM), it is required to provide reliable testing methods to ensure the safety of the additively manufactured parts. A possible solution could be the deployment of in-situ monitoring during the build process. However, for laser powder bed fusion using metal powders (PBF-LB/M) only a few in-situ monitoring techniques are commercially available (optical tomography, melt pool monitoring), which have not been researched to an extent that allows to guarantee the adherence to strict quality and safety standards.
In this contribution, we present results of a study of PBF-LB/M printed parts made of the nickel-based superalloy Haynes 282. The formation of defects was provoked by local variations of the process parameters and monitored by thermography, optical tomography and melt pool monitoring. Afterwards, the defects were characterized by computed tomography (CT) to identify the detection limits of the used in-situ techniques.
The present paper investigates the electromagnetic porosity reduction in partial penetration laser beam welding of 6 mm aluminum die casting AlSi9MnMg. Applying an electromagnetic field, a significant reduction of the porosity as well as smoothing of the surface of aluminum die casting can be observed. Starting from the reference case without an electromagnetic support, the porosity was reduced by 76 %. Especially big pores can be removed from the weld pool effectively due to their beneficial volume-to-area ratio whereas very small metallurgical pores tend to remain within the weld pool even when higher magnetic flux densities are applied.
Additive manufacturing processes are increasingly being used in industrial applications. Especially powder bed fusion processes are of high interest due to their capability to economically produce individual, highly complex and functionally integrated components in small batches.
However, the quality assurance of these components remains a challenge. Internal defects and undesirable microstructures and surface conditions can deteriorate the mechanical properties. Especially for use in safety-relevant applications, new design and inspection concepts are needed that take these factors into account.
This talk presents typical defects and microstructure phenomena resulting from the laser powder bed fusion process and identifies challenges and opportunities for non-destructive testing from a manufacturing engineering perspective. In particular, the possibility of a process-integrated quality control is shown based on current research results.
Safety-critical applications of products manufactured by laser powder bed fusion (PBF-LB/M) are still limited to date. This is mainly due to a lack of knowledge regarding the complex relationship between process, structure, and resulting properties. The assurance of homogeneity of the microstructure and homogeneity of the occurrence and distribution of defects within complexly shaped geometries is still challenging. Unexpected and unpredicted local inhomogeneities may cause catastrophic failures. The identification of material specific and machine specific process parameter windows for production of fully dense simple laboratory specimens is state of the art. However, the incorporation of changing thermal conditions that a complexly shaped component can be faced with during the manufacturing process is often neglected at the stage of a process window determination. This study demonstrates the tremendous effect of changing part temperatures on the defect occurrence for the broadly used stainless steel alloy AISI 316L. Process intrinsic variations of the surface temperature are caused by heat accumulation which was measured by use of a temperature adjusted mid-wavelength infrared (MWIR) camera. Heat accumulation was triggered by simple yet effective temporal and geometrical restrictions of heat dissipation. This was realized by a variation of inter layer times and reduced cross section areas of the specimens. Differences in surface temperature of up to 800 K were measured. A severe development of keyhole porosity resulted from these distinct intrinsic preheating temperatures, revealing a shift of the process window towards unstable melting conditions. The presented results may serve as a warning to not solely rely on process parameter optimization without considering the actual process conditions a real component is faced with during the manufacturing process. Additionally, it motivates the development of representative test specimens.
Among additive manufacturing (AM) technologies, the laser powder bed fusion (L-PBF) is one of the most important technologies to produce metallic components. The layer-wise build-up of components and the complex process conditions increase the probability of the occurrence of defects. However, due to the iterative nature of its manufacturing process and in contrast to conventional manufacturing technologies such as casting, L-PBF offers unique opportunities for in-situ monitoring. In this study, two cameras were successfully tested simultaneously as a machine manufacturer independent process monitoring setup: a high-frequency infrared camera and a camera for long time exposure, working in the visible and infrared spectrum and equipped with a near infrared filter. An AISI 316L stainless steel specimen with integrated artificial defects has been monitored during the build. The acquired camera data was compared to data obtained by computed tomography. A promising and easy to use examination method for data analysis was developed and correlations between measured signals and defects were identified. Moreover, sources of possible data misinterpretation were specified. Lastly, attempts for automatic data analysis by data Integration are presented.