Eingeladener Vortrag (wissenschaftliche Konferenzen)
- nein (5)
Epoxy composites used for high-end structural applications are typically cured under the influence of temperature and pressure causing a number of complex chemical and physical transformations. On heating a mould, temperature gradients will occur through the component which will depend largely on the thermophysical properties of the specific composite. The crosslinking reaction is exothermic leading to additional heat release, thus complicating heat transportation models. If such effects are not accounted for, it can lead to variations in resin flow, poor fibre wetting causing voiding and inhomogeneous cure, leading to shrinkage and unfavourable variations in moulded part geometry. Limited information is available for thermal models used in the manufacture of reinforced thermosets. Autoclave [1, 2] and laser or infra-red curing processes [3, 4] typically use constant values determined on fully cured parts. In this work, the variation in thermal conductivity (K) (W/(m K)), thermal diffusivity (a) (m(2)/s) and specific heat capacity at constant pressure (c(p)) (J/(g K) is determined for a carbon fibre prepreg during cure. It is the intention to improve understanding of how these parameters are related to chemical or physical transformations occurring during cure, and where estimates or shortcuts may be used for heat transfer models
Das Fließ-Härtungs-Verhalten von Duroplastformmassen wird gegenwärtig nur
unvollständig durch empirische Größen beschrieben. Diese ungenauen und
unsicheren Angaben können zu Schwierigkeiten bei der optimalen Einstellung
der Fertigungsmaschinen des Verarbeiters führen. Insbesondere Veränderungen
der Formmasseeigenschaften während des Transportes und der Lagerung stören
die Produktion. Das vorgestellte Messverfahren mit Ultraschall-sensoren ermöglicht
die schnelle und vollständige Erfassung des Fließ-Härtungs-Verhaltens, auch
während des technologischen Prozesses. Experimentelle Ergebnisse zu
Alterungs-erscheinungen dieser Formmassen illustrieren den Nutzen des
Verfahrens für Formmasse-produzenten und -verarbeiter.
The technique normally used to measure Cp during isothermal cure is Temperature Modulated - Dynamic Scanning Calorimetry TM-DSC. It is however not standardised, experimentally complicated and quite time intensive. As will be shown, Cp may also be estimated during isothermal cure just from using dynamic heating experiments on a fully cured sample. Such values are often sufficient for isothermal heat transfer models that otherwise employ a constant Cp value obtained from the fully cured epoxy. Secondly, the results from dynamic heating experiments provide a quick means, in comparison to isothermal TMDSC measurements, of estimating Cp variation during cure as well as providing a good estimate value for Cp towards the end of isothermal cure. As will be shown, such values obtained from a standardised measurement procedure are very helpful in setting up TMDSC experiments that are more sensitive to experimental error influenced by factors such as sample weight and geometry.
The DSC results illustrate that the measured heat capacity Cp for a fully cured epoxy over a temperature range are very similar to values for samples partially cured at corresponding isothermal temperatures, under the prerequisite that vitrification takes place. In such cases the primary influence on Cp is specific measurement temperature and not degree of cure. For isothermal cure temperatures investigated between 150 and 200 °C, the total change of Cp during cure is nearly constant and correlates well with values published by authors on other epoxy based systems. Taking Cp variation as constant, it is possible from just dynamic heating experiments on the cured epoxy to estimate Cp for the uncured epoxy system at specific cure temperatures. The next step would be to estimate the full Cp profile during isothermal cure, however, in such cases, the time to vitrification would also be needed as additional information.
Ultrasound on-line NDT methods have been demonstrated as a useful tool for monitoring the curing reaction of thermosets. In order to achieve this ultrasound sensors are incorporated into compression, injection and RTM (resin transfer) mould. For many commercial products imprints or any surface markings upon the moulded product are undesirable. Due to its physical properties ultrasound has a large advantage over other techniques for similar applications. The sound wave can pass through the wall of the mould and direct contact with the moulded part is not required. In this particular case one fundamental problem is a good coupling of the sensors to the mould wall. Several mediums came into question but because of the high technical (e. g. temperature and long time stability) and practical demands, it was decided that dry (non-fluid) coupling would be the most promising candidate. A handful of coupling foils suitable also at high temperatures and for long time application under industrial conditions were tested and are presented in this paper.