Filtern
Erscheinungsjahr
Dokumenttyp
Sprache
- Englisch (16)
- Deutsch (5)
- Mehrsprachig (1)
Schlagworte
- Durability (3)
- Weathering (3)
- Bundesoberbehörden (2)
- Concrete (2)
- Flame retardant (2)
- Forschungsstrategie (2)
- LIBS (2)
- Nano (2)
- 3-dimensional microscopy (1)
- Aluminum hydroxide (ATH) (1)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (5)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (5)
- 8 Zerstörungsfreie Prüfung (4)
- 8.0 Abteilungsleitung und andere (3)
- 1 Analytische Chemie; Referenzmaterialien (2)
- 5 Werkstofftechnik (2)
- 5.3 Polymere Verbundwerkstoffe (2)
- 1.3 Instrumentelle Analytik (1)
- 1.4 Prozessanalytik (1)
- 4 Material und Umwelt (1)
Aufbereitungsuntersuchungen an schwermetallbelastetem Baggergut aus dem ältesten Kanal Deutschlands
(2000)
Das Basisanliegen - Einleitung
Mit der zunehmenden Zahl akkreditierter ZfP-Firmen und zunehmender Anwendung risikobasierender Konzepte ergibt sich die Notwendigkeit, internationale Standards wie die DIN EN ISO 17025 und darüber hinausgehende Richtlinien bei der Verfahrensauswahl in der ZfP zu berücksichtigen. Dieser Aufsatz soll aufzeigen, welche internationalen Aktivitäten gegenwärtig für die Zuverlässigkeitsbetrachtungen von Bedeutung sind (siehe auch [1]). In Übereinstimmung mit den Vereinbarungen und Definitionen der European-American Workshops zur Zuverlässigkeit [2, 3] gilt: Das Basisanliegen der Zuverlässigkeitsuntersuchungen beliebiger diagnostischer Systeme besteht darin, den Grad festzustellen mit dem das Prüfsystem in der Lage ist, seinen vorgesehenen Zweck zu erfüllen. Im Falle der ZfP besteht dieser Zweck zumeist in der Aufgabe, Bauteildefekte aufzufinden und zu beschreiben bzw. die Defektfreiheit von Bauteilen zu bestätigen, sowie Wanddicken zu messen oder Material zu charakterisieren.
Das Basisanliegen der Zuverlässigkeitsuntersuchungen findet seinen Niederschlag bei folgenden international relevanten Aktivitäten:
neue ISO 17025 als Notwendigkeit mit variablen Möglichkeiten der Verfahrensvalidierung
als Kettenglied in RBLM (Risk Based Life Time Management) (r) EPERC-Initiative
CEN/TC138/WG9 "Qualifizierung von ZfP-Verfahren"
Six-Sigma Strategie: als notwendiger Bestandteil
ASNT-Initiative: Standing Committee on NDE Reliability: als Arbeitspaket
Produkthaftung: als notwendige Voraussetzung für die Handhabung
Turbine components from conventionally cast nickel-base alloy René 80 show different hot cracking susceptibilities depending on their heat treatment conditions leading to slightly different microstructures. Electron probe micro-analysis, focused ion beam technique and analytical transmission electron microscopy were applied to reveal and identify grain boundary precipitates and the γγ'-microstructure. The distribution of borides along grain boundaries was evaluated statistically by quantitative metallography. The following features could be correlated with an increase of cracking susceptibility: i) Increasing grain size, ii) increasing fraction of grain boundaries with densely spaced borides, iii) lack of secondary γ'-particles in matrix channels between the coarse cuboidal γ'-precipitates. The latter feature seems to be responsible for linking-up of cracked grain boundary precipitates which occurred as an additional cracking mechanism after one heat treatment, whereas decohesion at the boride-matrix-interface in the heat affected zone of laser-drilled holes was observed for both heat treatments.
The interest in repair technologies for polymer composites has increased significantly over the last decades, due to the growing use of these materials in structural applications. In this study, poly (ethylene-co-methacrylic acid) (EMAA) was used as self-healing agent to glass fiber/epoxy composite. Materials with EMAA contents of 2 wt% and 5 wt% were manufactured using Resin Transfer Molding (RTM) and the effects of the healing agent on the properties were investigated using tensile tests and Dynamic Mechanical Analysis (DMA). Results show slight variation of properties, which was more pronounced as the content of EMAA increased. In addition, the healing efficiency was investigated through fatigue tests and the addition of higher content of EMAA increased the number of cycles to failure after the healing activation cycle.
Large-language models (LLMs) such as GPT-4 caught the interest of many scientists. Recent studies suggested that these models could be useful in chemistry and materials science. To explore these possibilities, we organized a hackathon. This article chronicles the projects built as part of this hackathon. Participants employed LLMs for various applications, including predicting properties of molecules and materials, designing novel interfaces for tools, extracting knowledge from unstructured data, and developing new educational applications. The diverse topics and the fact that working prototypes could be generated in less than two days highlight that LLMs will profoundly impact the future of our fields. The rich collection of ideas and projects also indicates that the applications of LLMs are not limited to materials science and chemistry but offer potential benefits to a wide range of scientific disciplines.
We report the selective ring opening copolymerisation (ROCOP) of
oxetane and phthalic thioanhydride by a heterobimetallic Cr(III)K
catalyst precisely yielding semi-crystalline alternating poly(esteralt-
thioesters) which show improved degradability due to the
thioester links in the polymer backbone.
Mit einer langfristigen Forschungsstrategie begleiten die für die Sicherheit von Mensch und Umwelt zuständigen Bundesoberbehörden (Umweltbundesamt, Bundesinstitut für Risikobe-wertung, Bundesanstalt für Arbeitsschutz und Arbeitsmedizin, Bundesanstalt für Materialfor-schung und -prüfung und Physikalisch-Technische Bundesanstalt) die rasch voranschreiten-de Entwicklung neuer Materialien unter den Gesichtspunkten des Arbeits-, Verbraucher- und Umweltschutzes. Die Strategie steht daher in enger Verbindung zu den öffentlichen Förder-programmen für Nanomaterialien und andere innovative Werkstoffe, z. B. des BMBF („Vom Material zur Innovation“) und der EU („Horizon 2020“).
Die Forschungsstrategie baut auf den bisherigen Ergebnissen der 2008 begonnenen und 2013 erstmals bilanzierten gemeinsamen Forschungsstrategie der Bundesoberbehörden „Nanotechnologie - Gesundheits- und Umweltrisiken von Nanomaterialien"1 auf und erweitert den Blickwinkel auch auf andere Materialinnovationen, bei denen vergleichbare Risiken für Mensch und Umwelt bestehen oder abgeklärt werden müssen. Darüber hinaus greift sie die Idee „anwendungssichere chemische Produkte“2 aus der Initiative „Neue Qualität der Arbeit“ (INQA) des Bundesministeriums für Arbeit und Soziales (BMAS) und das Konzept der nach-haltigen Chemie3 auf, das vom Bundesministerium für Umwelt, Naturschutz, Bau und Reak-torsicherheit (BMUB) unterstützt wird. Durch eine anwendungssichere und umweltverträgli-che Gestaltung innovativer Materialien und ihrer Folgeprodukte sollen nicht akzeptable Risi-ken für Mensch und Umwelt von Anfang an weitgehend ausgeschlossen werden. Dies kann erreicht werden durch
1.
die Verwendung sicherer Materialien ohne Gefahreneigenschaften für Mensch und Umwelt (direkte Anwendungssicherheit) oder
2.
eine Produktgestaltung, die über den gesamten Lebenszyklus emissionsarm und umweltverträglich ist (integrierte Anwendungssicherheit) oder
3.
eine Unterstützung des Anwenders (product stewardship) durch den Hersteller bei technischen, organisatorischen und persönlichen Schutzmaßnahmen zur sicheren Verwendung und Entsorgung des Produktes (unterstützte Anwendungssicherheit).
Die Fortschreibung der Forschungsstrategie soll als Bestandteil des Nanoaktionsplans 2020 der Bundesregierung Beiträge der Ressortforschung zu folgenden Schwerpunkten leisten:
•
Charakterisierung und Bewertung der Risiken von Materialinnovationen
•
Unterstützung von Forschungseinrichtungen und Unternehmen
•
Fortschreiben von Rechtsvorschriften und Praxisempfehlungen
1
http://www.baua.de/nn_47716/de/Themen-von-A-Z/Gefahrstoffe/Nanotechnologie/pdf/Forschungsstrategie.pdf
2 http://www.baua.de/de/Themen-von-A-Z/Gefahrstoffe/Nachhaltige-Chemie/Nachhaltige-Chemie.html
3
http://www.umweltbundesamt.de/themen/chemikalien/chemikalien-management/nachhaltige-chemie
2
•
Gesellschaftliche Akzeptanz
Die Forschungsstrategie soll mit Projekten und anderen forschungsnahen Aktivitäten umge-setzt werden. Dies umfasst die eigene Forschung der Häuser, die extramurale Ausschrei-bung und Vergabe von Forschungsdienstleistungen sowie die Beteiligung an vorwiegend öffentlich geförderten Drittmittelprojekten. Hinzu kommen Aktivitäten im Rahmen der Politik-beratung und der hoheitlichen Aufgaben. Mit inter- und transdisziplinären Ansätzen soll die Risiko- und Sicherheitsforschung enger mit der Innovationsforschung und Materialentwick-lung verknüpft werden. Die Forschungsstrategie ist aufgrund der raschen Entwicklungen auf diesem Gebiet für den Zeitraum bis 2020 angelegt. Die Forschungsziele adressieren die in diesem Zeitraum voraussichtlich umsetzbaren Forschungsansätze. Die Forschungsstrategie wird durch einen Arbeitskreis begleitet und spätestens mit Ablauf des Nanoaktionsplans 2020 evaluiert und angepasst.
Fire stability of glass-fibre sandwich panels: The influence of core materials and flame retardants
(2017)
Fire resistance has become a key property for structural lightweight sandwich components in aviation, shipping, railway vehicles, and construction. The development of future composite materials and components demands adequate test procedures for simultaneous application of compression and fully developed fire. Therefore an intermediate-scale approach (specimen size = 500 mm x 500 mm) is applied with compressive loads (up to 1 MN) and direct application of a burner to one side of the specimens, as established in aviation for severe burn-through tests. The influence of different core structures (polyvinylchloride foam, polyisocyanorate foam reinforced by stitched glass bridges, and balsa wood) was investigated for glass-fibre-reinforced sandwich specimens with and without flame retardants applied on the fabrics, in the matrix, and on surface for each specimen at the same time. Times to failure were increased up to a factor of 4. The intumescent coating prolongs the time to failure significantly.
What is more, using the intrinsic potential of the front skin together with the core to protect a load bearing back skin in sandwich panels, the design of the core – here using the wood core – is the most promising approach.
The site of Schöningen (Germany), dated to ca. 300,000 years ago, yielded the earliest large-scale record of humanly-made wooden tools. These include wooden spears and shorter double-pointed sticks, discovered in association with herbivores that were hunted and butchered along a lakeshore. Wooden tools have not been systematically analysed to the same standard as other Palaeolithic technologies, such as lithic or bone tools. Our multianalytical study includes micro-CT scanning, 3-dimensional microscopy, and Fourier transform infrared spectroscopy, supporting a systematic technological and taphonomic analysis, thus setting a new standard for wooden tool analysis. In illustrating the biography of one of Schöningen’s double-pointed sticks, we demonstrate new human behaviours for this time period, including sophisticated woodworking techniques. The hominins selected a spruce branch which they then debarked and shaped into an aerodynamic and ergonomic tool. They likely seasoned the wood to avoid cracking and warping. After a long period of use, it was probably lost while hunting, and was then rapidly buried in mud. Taphonomic alterations include damage from trampling, fungal attack, root damage and compression. Through our detailed analysis we show that Middle Pleistocene humans had a rich awareness of raw material properties, and possessed sophisticated woodworking skills. Alongside new detailed morphometrics of the object, an ethnographic review supports a primary function as a throwing stick for hunting, indicating potential hunting strategies and social contexts including for communal hunts involving children. The Schöningen throwing sticks may have been used to strategically disadvantage larger ungulates, potentially from distances of up to 30 metres. They also demonstrate that the hominins were technologically capable of capturing smaller fast prey and avian fauna, a behaviour evidenced at contemporaneous Middle Pleistocene archaeological sites.
Concrete structures experience severe damage during service, for example due to pitting corrosion of rebars caused by the ingress of chlorine (Cl) into the porous concrete structure. The ingress can be monitored using laser-induced breakdown spectroscopy (LIBS), a recently introduced civil engineering technique used to detect Cl in concrete structures in addition to conventional wet chemistry methods. The key advantages of LIBS are high spatial resolution, which is important when analyzing heterogeneous concrete samples, as well as the almost complete absence of sample preparation. To assess LIBS as a reliable analytical method, its accuracy and robustness must be carefully tested. This paper presents the results of an interlaboratory comparison on the analysis of Cl in cement paste samples conducted by 12 laboratories in 10 countries. Two sets of samples were prepared with Cl content ranging from 0.06 to 1.95 wt% in the training set and 0.23–1.51 wt% in the test set, with additional variations in the type of cement and Cl source (salt type). The overall result shows that LIBS is suitable for the quantification of the studied samples: the average relative error was generally below 15%. The results demonstrate the true status quo of the LIBS method for this type of analysis, given that the laboratories were not instructed on how to perform the analysis or how to process the data.
In a joint project of partners from industry and research, the automated recycling of construction and demolition waste (CDW) is investigated and tested by combing laser-induced breakdown spectroscopy (LIBS) and near-infrared (NIR) spectroscopy. Joint processing of information (data fusion) is expected to significantly improve the sorting quality of various materials like concrete, main masonry building materials, organic components, etc., and may enable the detection and separation of impurities such as SO3-cotaining building materials (gypsum, aerated concrete, etc.). The project focuses primarily on the Berlin site to analyze the entire value chain, minimize economic/technological barriers and obstacles at the cluster level, and sustainably increase recovery and recycling rates. First measurements with LIBS and NIR spectroscopy show promising results in distinguishing various material types and indicate the potential for a successful combination. In addition, X-ray fluorescence (XRF) spectroscopy is being performed to obtain more information about the quantitative elemental composition of the different building materials. Future work will apply the developed sorting methodology in a fully automated measurement setup with CDW on a conveyor belt.
Scientific publications addressing the durability of the flame retardance of cables during their long-term application are rare and our understanding lacks. Three commercial flame retardants, aluminum hydroxide, aluminum diethyl phosphinate (AlPi-Et), and intumescent flame retardant based on ammonium polyphosphate, applied in ethylene-vinyl acetate copolymer (EVA) model cables, are investigated. Different artificial aging scenarios were applied: accelerated weathering (UV-irradiation/temperature/rain phases), humidity exposure (elevated temperature/humidity), and salt spray exposure. The deterioration of cables’ surface and flame retardancy were monitored through imaging, color measurements, attenuated total reflectance Fourier transform infrared spectroscopy, and cone calorimeter investigations. Significant degradation of the materials’ surface occurred. The flame retardant EVA cables are most sensitive to humidity exposure; the cable with AlPi-Et is the most sensitive to the artificial aging scenarios. Nevertheless, substantial flame retardance persisted after being subjected for 2000 h, which indicates that the equivalent influence of natural exposure is limited for several years, but less so for long-term use.
The durability of flame retardancy is a challenge for cables over long lifetimes. The degradation of flame retardance is investigated in two kinds of exposures, artificial weathering and humidity. In this basic study, typical mineral flame retardants in two polymers frequently used in cable jackets are investigated to get the fundamental picture. Aluminum hydroxide (ATH) and magnesium hydroxide (MDH) are compared in ethylene‐vinyl acetate (EVA), and further in EVA and linear low‐density polyethylene (LLDPE) cables containing the same ATH. The changes in chemical structure at the surface are studied through attenuated total reflectance Fourier transform infrared spectroscopy (ATR‐FTIR), the formation of cracks, and changes in color are investigated. The cone calorimeter and a bench scale fire testing cable module are utilized to evaluate the fire behavior of the cables. Although the flame retardancy deteriorated slightly, it survived harsh exposure conditions for 2000 h. Compared to EVA/MDH and LLDPE/ATH, the fire behavior of EVA/ATH is the least sensitive. Taken together, all of the results converge to estimate that there will be no problem with flame retardancy performance, for materials subjected to natural exposure for several years; the durability of fire retardancy is questionable for longer periods, and thus requires further investigation.
The OECD test guidelines (TGs) for testing chemicals have been widely used for regulatory purposes all over the world since the establishment of the Mutual Acceptance of Data (MAD) principle in 1984. This MAD principle ensures that, if a chemical is tested under the Good Laboratory Practice (GLP) conditions accordingly to an OECD TG, the data should be accepted in all OECD countries. The TGs have been developed, harmonized, internationally validated (round robin tests) and adopted by OECD countries to be used for the physical-chemical characterisation, fate estimation, and hazard identification for risk assessment of various chemicals. In addition to the TGs, OECD Guidance Documents (GDs) usually provide guidance on how to use TGs and how to interpret the results. These GDs do not have to be fully experimentally validated, and hence they are not under MAD, but they are based on relevant published scientific research.
But are the existing TGs and the related GDs applicable and adequate for the regulatory testing of nanomaterials? In general, for nanomaterials it is accepted that most of the "endpoints" or more precisely measurement variables are applicable. However, for some endpoints new or amended TGs are needed. In addition, several GDs are needed to give more precise advice on the test performance in order to gain regulatory relevant data on nanomaterials.
The heterogeneous mesostructure of concreted causes local stress concentrations. Stress dependent phenomena like damage and creep as well as their interactions are effected by those stress
concentrations. Therefore a material model’s macroscopic behavior will differ whether the mesoscale structure is considered or not. The differences between the mesoscale approach and an homogeneous approach will be presented. The results are discussed with focus on the true materials behavior.
Die Erwartungen der Prozessindustrie an die NAMUR Open Architecture sind groß, schließlich soll das Konzept der Garant für die digitale Transformation der Branche sein. Im atp-Interview warnt Dr. Michael Maiwald, Fachbereichsleiter „Prozessanalytik“ an der Bundesanstalt für Materialforschung und -prüfung (BAM), allerdings davor, NOA als Allheilmittel zu betrachten.
With 8% of man-made CO2 emissions, cement production is an important driver of the climate crisis. By using alkali-activated binders, part of the energy-intensive clinker production process can be dispensed. However, as numerous raw materials are involved in the manufacturing process here, the complexity of the materials increases by orders of magnitude. Finding a properly balanced binder formulation is like looking for a needle in a haystack. We have shown for the first time that artificial intelligence (AI)-based optimization of alkali-activated binder formulations can significantly accelerate research.
The "Sequential Learning App for Materials Discovery" (SLAMD) aims to accelerate practice transfer. With SLAMD, materials scientists have low-threshold access to AI through interactive and intuitive user interfaces. The value added by AI can be determined directly. For example, the CO2 emissions saved per ton of cement can be determined for each development cycle: the more efficient the AI optimization, the greater the savings.
Our material database already includes more than 120,000 data points of alternative binders and is constantly being expanded with new parameters. We are currently driving the enrichment of the data with a life cycle analysis of the building materials.
Based on a case study we show how intuitive access to AI can drive the adoption of techniques that make a real contribution to the development of resource-efficient and sustainable building materials of the future and make it easy to identify when classical experiments are more efficient.
Assessing the structural integrity of carbon-fibre sandwich panels in fire: Bench-scale approach
(2019)
The fire resistance of lightweight sandwich panels (SW) with carbon fibre/epoxy skins and a poly(methacryl imide) (PMI) foam core is investigated in compression under direct application of a severe flame (heat flux=200 kW m−2). A bench-scale test procedure was used, with the sample held vertically. The epoxy decomposition temperature was quickly exceeded, with rapid flash-over and progressive core softening and decomposition.
There is a change in failure mode depending on whether the load is greater or less than 50% of the unexposed failure load, or in other words if one or two skins carry the load. At high loads, failure involved both skins with a single clear linear separation across each face. There is an inflection in the failure time relationship in the ∼50% load region, corresponding to the time taken for heat to be transmitted to the rear face, along with a change in the rear skin failure mode from separation to the formation of a plastic hinge. The integrity of the carbon front face, even with the resin burnt out, and the low thermal diffusivity of the core, both play key roles in prolonging rear face integrity, something to be borne in mind for future panel design. Intumescent coatings prolong the period before failure occurs. The ratio of times to failure with and without protection is proposed as a measure of their effectiveness. Apart from insulation properties, their adhesion and stability under severe fire impact play a key role.