Low-κ dielectric LTCC was developed, to realize successful co-firing with NiCuZn ferrite tapes. A critical high-temperature process in the production of highly integrated LTCC modules is the migration of silver from inner conductors into the LTCC glass phase. Intensive silver migration causes strong deformation of LTCC multilayers during firing in air.
Silver migration into the LTCC glass phase depends on oxygen content of the sintering atmosphere and can be minimized by sintering in nitrogen atmosphere. However, partial decomposition of NiCuZn-ferrite and formation of cuprite was observed during sintering in nitrogen and, consequently, the permeability of the ferrite decreases. As shown by a combined XRD/thermogravimetric study the co-firing of LTCC modules with silver metallization and integrated ferrite layer demands precise adjustment of oxygen partial pressure.
The sintering behavior of sub-micron Ni0.30Cu0.20Zn0.52Fe1.98O3.99 ferrite with and without Bi2O3 addition was studied. Ferrites with 0.5 wt% Bi2O3 exhibit enhanced shrinkage at T < 900 °C with significant grain growth. Additive-free ferrite powders also sinter to high density at 900 °C, however, grain growth is very limited. Both ferrites exhibit a permeability of µ = 400–450. Multilayers consisting of ferrite and low-k dielectric LTCC layers were prepared by co-firing at 900–915 °C. The shrinkage and thermal expansion characteristics of ferrite and LTCC tapes are similar. However, the permeability of integrated ferrite layers, made from ferrite tapes with Bi2O3 additive, significantly drops after co-firing with LTCC layers compared to separately fired monolithic ferrite multilayers. Contrarily, the permeability of integrated, Bi2O3-free ferrite layers, co-fired with dielectric tapes, is identical to that of monolithic ferrite multilayers. This finding is an important step toward ferrite integration into complex LTCC multilayer architectures.
LTCC-modules with integrated ferrite layers - Strategies for material development and co-sintering
(2008)
Silver in LTCC - Interfacial reactions, transport processes and influence on properties of ceramics
(2009)
LTCC-Modules with integrated ferrite layers - Strategies for material development and co-sintering
(2009)
The integration of passive components (resistors, capacitors, inductors) into LTCC modules is a challenging task in multilayer ceramics technology. We report on multilayer assemblies consisting of combined layers of ferrite and dielectric LTCC tapes. Ni-Cu-Zn ferrites with maximum shrinkage at 900°C were processed to green tapes and laminated with dielectric LTCC tapes. Cosintering at 900°C led to multilayers with different defects such as incomplete densification of the ferrite layers, cracks, and warpage. Since ferrite tapes do not really allow compositional changes without deterioration of magnetic properties, the dielectric tape was modified with the following objectives: (i) matching of the shrinkage curves of dielectric and ferrite materials, (ii) adjusting the coefficients of thermal expansion to avoid cracking during cooling, and (iii) controlling of interface reactions. Using this concept we fabricated dense and defect-free multilayers consisting of dielectric and ferrite layers. However, compositional changes of the individual ferrite tapes require the development of a specific dielectric tape material with tailored properties.
Integration of magnetic functional components in LTCC Circuit boards calls for co-firing of dielectric and ferrite tapes. Ni-Cu-Zn ferrites with permeability of p=900 were developed which can be fully densified at the Standard LTCC sintering temperature of 900 °C. Successful co-firing of this ferrite with dielectric tapes requires the adaptation of the shrinkage behavior of the materials as well as the thermal expansion during the cooling period - especially in the temperature range below the transformation point of the glassy phase of the dielectric tape. To match these preconditions, a new dielectric LTCC material with steep sintering curve and high thermal expansion coefficient was designed. Sintered multilayer composed of Ni-Cu-Zn ferrite and tailored dielectric tapes are free of cracks and possess no open porosity. No significant interdiffusion between the ferrite and dielectric tapes was found by EDX measurements. Compared to pure ferrite laminates the permeability of co-sintered Ni-Cu-Zn ferrite layers is drastically reduced to 400, i.e. a decrease of more than 50 %.
To investigate the origin of this permeability reduction, Ni-Cu-Zn ferrite laminates were sintered separately, and in combination with alumina release tapes or dielectric tapes, respectively. SEM and EDX analysis of co-fired laminates reveal differences in the ferrite grain growth behavior. Ferrite laminates with homogeneous microstructure and grain size up to 50 pm exhibit large permeability. However, growth of ferrite grains does not take place near the interface between ferrite and release or dielectric tapes. There is a strong correlation between high permeability and volume fraction of large ferrite grains. Regions of fine and coarse grains inside the ferrite layers show different bismuth concentration; the Bi-content is larger in regions of fine ferrite grains.
Transformers couple two sections of a circuit by electromagnetic induction. They are widely used to either transform alternating voltage levels or to transmit power or signals across galvanic isolation. Both of these functions are essential for the operation of sensors and controllers. Covering all aspects from idea to circuit performance and from design to manufacture, this paper presents the first comprehensive description of the making of miniaturized, rugged, up-to-100W transformers for embedding into multilayer circuit boards. For circular coils, the well-manageable Ampere-Laplace law is shown to yield reliable designs, predicting correctly the performance of manufactured hardware. This enables fast design without lengthy finite element modelling. In the low-power linear regime, basic relations describe how the device’s characteristics evolve from the material properties and device structure. While scattering Parameters are useful for the analysis of isolated transformers with their intrinsic parasitics, the interaction with the components of the final circuit and the aspects of power and efficiency are addressed by chain matrixes.
While these design rules are similar for multilayer boards of different material (like epoxy, Teflon, ceramics), the manufacturing of ceramic board transformers is considered here in detail. Low-temperature-cofired ceramic (LTCC) boards being sintered at 900 °C are particularly suited for harsh environments with chemical or thermal stress as frequently found at sensor positions. The transformer performance usually benefits from or even requires an integrated ceramic core of higher permeability, a ferrite, to shape the magnetic flux. Methods to sinter ferrites inside a dielectric ceramic multilayerandto measure their performance are therefore described in detail.Asthe sintering behaviour of dielectricandmagnetic ceramics differs considerably, their simultaneous sintering is challenging.However, the sintering temperatures of the usefulMnZnand NiZnCu ferrites can be lowered to that of the dielectric material with only moderate loss of permeability by glass additives. Furthermore, thermal mismatch between materials causes catastrophic failure or at least stress and loss of magnetic performance during cooling to room temperature after sintering. This is avoidable by either adjusting the thermal expansion coefficient of the ferrite or by enclosing the ferrite between stressreleasing separation layers.We present the state of the art in materials development according to the first approach as well as fully functional devices made with the second technique.
Other applications not directly addressed but well related to this work are characterized by low load resistance in relation to the coil resistance of the transformer. Efficient power transmission then requires that technological solutions are applied to achieve the lowest possible resistive loss inside the coils by an enlarged conductor cross-section.
As this is particularly challenging for LTCC boards, a technique is discussed to fabricate conductor traces with a thickness larger than their width.