- nein (3)
We have studied the integration of Ni-Cu-Zn ferrite spinels as well as substituted hexagonal Co2Y-and M-type ferrites into LTCC (Low Temperature Ceramic Co-firing) modules. The cofiring behavior and the magnetic properties of these materials were investigated and evaluated for multilayer applications. Ni-Cu-Zn ferrites exhibit permeabilities of µ=300–500 for operating frequencies in the MHz range. Cu-substituted Y-type ferrites Ba2Co2-x-yZnxCuyFe12O22 in combination with sintering additives display sufficient shrinkage and densification at 900°C. A permeability of µ=10 is observed; however, substituted Co2Y-type ferrites do not exhibit long-term stability at 900°C. Co/Ti-substituted M-type ferrites BaFe12-2yCoyTiyO19 (y=1.2) with planar magneto-crystalline anisotropy exhibit excellent soft magnetic behavior. Using sintering additives, complete densification is reached at 900°C and a permeability of µ=15 and a resonance frequency of larger than 1?GHz are observed. Integration of ferrite multilayer inductor components into LTCC modules using free and constrained cofiring technologies is demonstrated.
LTCC-modules with integrated ferrite layers - Strategies for material development and co-sintering
(2008)
Silver in LTCC - Interfacial reactions, transport processes and influence on properties of ceramics
(2009)
LTCC-Modules with integrated ferrite layers - Strategies for material development and co-sintering
(2009)
The integration of passive components (resistors, capacitors, inductors) into LTCC modules is a challenging task in multilayer ceramics technology. We report on multilayer assemblies consisting of combined layers of ferrite and dielectric LTCC tapes. Ni-Cu-Zn ferrites with maximum shrinkage at 900°C were processed to green tapes and laminated with dielectric LTCC tapes. Cosintering at 900°C led to multilayers with different defects such as incomplete densification of the ferrite layers, cracks, and warpage. Since ferrite tapes do not really allow compositional changes without deterioration of magnetic properties, the dielectric tape was modified with the following objectives: (i) matching of the shrinkage curves of dielectric and ferrite materials, (ii) adjusting the coefficients of thermal expansion to avoid cracking during cooling, and (iii) controlling of interface reactions. Using this concept we fabricated dense and defect-free multilayers consisting of dielectric and ferrite layers. However, compositional changes of the individual ferrite tapes require the development of a specific dielectric tape material with tailored properties.
Integration of magnetic functional components in LTCC Circuit boards calls for co-firing of dielectric and ferrite tapes. Ni-Cu-Zn ferrites with permeability of p=900 were developed which can be fully densified at the Standard LTCC sintering temperature of 900 °C. Successful co-firing of this ferrite with dielectric tapes requires the adaptation of the shrinkage behavior of the materials as well as the thermal expansion during the cooling period - especially in the temperature range below the transformation point of the glassy phase of the dielectric tape. To match these preconditions, a new dielectric LTCC material with steep sintering curve and high thermal expansion coefficient was designed. Sintered multilayer composed of Ni-Cu-Zn ferrite and tailored dielectric tapes are free of cracks and possess no open porosity. No significant interdiffusion between the ferrite and dielectric tapes was found by EDX measurements. Compared to pure ferrite laminates the permeability of co-sintered Ni-Cu-Zn ferrite layers is drastically reduced to 400, i.e. a decrease of more than 50 %.
To investigate the origin of this permeability reduction, Ni-Cu-Zn ferrite laminates were sintered separately, and in combination with alumina release tapes or dielectric tapes, respectively. SEM and EDX analysis of co-fired laminates reveal differences in the ferrite grain growth behavior. Ferrite laminates with homogeneous microstructure and grain size up to 50 pm exhibit large permeability. However, growth of ferrite grains does not take place near the interface between ferrite and release or dielectric tapes. There is a strong correlation between high permeability and volume fraction of large ferrite grains. Regions of fine and coarse grains inside the ferrite layers show different bismuth concentration; the Bi-content is larger in regions of fine ferrite grains.