We studied sintering of LTCC-type glass matrix composites (GMCs) consisting of small glass and alumina particles of equal size. Primarily, crystals act as rigid inclusions, decelerating the densification rate. In later stages, they also dissolve, partially increasing the viscosity. Release of alumina finally induces crystallization of alumosilicates, which enables post-firing stability. To study both effects, two model GMCs were prepared: an α-Al2O3 + barium alumoborosilicate glass (BABS)GMC, which shows neither significant dissolution nor crystallization, and an α-Al2O3 + calcium alumoborosilicate glass (CABS)GMC, which dissolves readily and promotes crystallization. The kinetics of shrinkage for both GMC were modeled by utilizing Frenkel theory for the early stage and MackenzieShuttleworth theory for the late stage, assuming that sintering is superimposed by the weighted contributions of triparticle glasscrystal clusters, their random occurrence (ideal mixing), and a shrinkage rate controlled by the GMC effective viscosity. In agreement with modeling, the experimental results showed that the shrinkage rate of BABSGMC decreases progressively for crystal volume fractions Φ > 0.15. The attainable shrinkage is reduced by up to 8% for Φ = 0.45. For the CABSGMC with Φ = 0.25, a reduction of Φ to 0.20 was evident due to partial α-Al2O3 dissolution. This effect was found able to increase the sintering temperature by ~5060 K.
The sintering of Low Temperature Co-fired Ceramics prepared from alumoborosilicate
glass- and Al2O3 powders of similar small particle size was studied by dilatometry, heating microscopy,
microstructure analysis, glass- and effective viscosity measurements. The steric effect of
Al3O3 inclusions was studied using a gnon-reactiveh model composite. With increasing Al3O3 volume
fraction (Φ ≤ 0.45), sintering decelerates and its final stage shifts to higher temperature. The
attainable shrinkage is reduced as Al2O3 particle clusters bearing residual pores become more frequent.
The kinetics of sintering could be described formally superposing the weighed contributions
of differentially sized and randomly composed glass-crystal particle clusters and assuming a sintering
rate controlled by the effective matrix viscosity, which increases with Φ and with progressive
wetting of Al2O3 particles during densification. The "reactive" model composite shows significant
dissolution of Al2O3 into the glass, which has two opposed effects on sintering: reducing Φ and increasing
glass viscosity. For the present case (Φ = 0.25), the latter effect dominates and sintering is
retarded by Al2O3 dissolution. Crystallization of wollastonite starts after full densification. Dissolution
of Al2O3 was found to promote the subsequent growth of anorthite.