Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (28)
- Beitrag zu einem Sammelband (7)
- Beitrag zu einem Tagungsband (2)
- Posterpräsentation (2)
- Vortrag (1)
Schlagworte
- Glass (7)
- LTCC (6)
- Viscosity (5)
- Inclusions (4)
- Water content (4)
- Glass matrix composites (3)
- Internal friction (3)
- Sintering (3)
- Sintering kinetics (3)
- Sintern (3)
Organisationseinheit der BAM
- 5 Werkstofftechnik (16)
- 5.6 Glas (16)
- 5.0 Abteilungsleitung und andere (1)
Eingeladener Vortrag
- nein (1)
Glass-ceramics are noted for their unusual combination of properties and manifold commercialized products for consumer and specialized markets. Evolution of novel glass and ceramic processing routes, a plethora of new compositions, and unique exotic nano- and microstructures over the past 60 years led us to review the Definition of glass-ceramics. Well-established and emerging processing methods, such as co-firing, additive manufacturing, and laser patterning are analyzed concerning the core requirements of processing glass-ceramics and the Performance of the final products. In this communication, we propose a revised, updated definition of glass-ceramics, which reads “Glass-ceramics are inorganic, non-metallic materials prepared by controlled crystallization of glasses via different processing methods. They contain at least one type of functional crystalline phase and a residual glass. The volume fraction crystallized may vary from ppm to almost 100%”.
Lithium disilicate, leucite and apatite glass-ceramics have become state-of-the-art framework materials in the fabrication of all-ceramic dental restorative materials. The goal of this study was to examine the crack propagation behaviour of these three known glass-ceramic materials after they have been subjected to Vickers indentation and to characterize their crack opening profiles (δmeas vs. (a-r)). For this purpose, various methods of optical examination were employed. Optical microscopy investigations were performed to examine the crack phenomena at a macroscopic level, while high-resolution techniques, such as scanning electron microscopy (SEM) and atomic force microscopy (AFM), were employed to investigate the crack phenomena at a microscopic level. The crack patterns of the three glass-ceramics vary from fairly straightforward to more complex, depending on the amount of residual glass matrix present in the material. The high-strength lithium disilicate crystals feature a high degree of crosslinking, thereby preventing crack propagation. In this material, the crack propagates only through the residual glass phase, which constitutes 30%40% by volume. Having a high glass content of more than 65% by volume, the leucite and apatite glass-ceramics show far more complex crack patterns. Cracks in the leucite glass-ceramic propagate through both the glass and crystal phase. The apatite glass-ceramic shows a similar crack behaviour as an inorganicorganic composite material containing nanoscale fillers, which are pulled out in the surroundings of the crack tip. The observed crack behaviour and the calculated View the MathML source values of the three types of glass-ceramics were compared to the Kkic values determined according to the SEVNB method.
We studied sintering of LTCC-type glass matrix composites (GMCs) consisting of small glass and alumina particles of equal size. Primarily, crystals act as rigid inclusions, decelerating the densification rate. In later stages, they also dissolve, partially increasing the viscosity. Release of alumina finally induces crystallization of alumosilicates, which enables post-firing stability. To study both effects, two model GMCs were prepared: an α-Al2O3 + barium alumoborosilicate glass (BABS)GMC, which shows neither significant dissolution nor crystallization, and an α-Al2O3 + calcium alumoborosilicate glass (CABS)GMC, which dissolves readily and promotes crystallization. The kinetics of shrinkage for both GMC were modeled by utilizing Frenkel theory for the early stage and MackenzieShuttleworth theory for the late stage, assuming that sintering is superimposed by the weighted contributions of triparticle glasscrystal clusters, their random occurrence (ideal mixing), and a shrinkage rate controlled by the GMC effective viscosity. In agreement with modeling, the experimental results showed that the shrinkage rate of BABSGMC decreases progressively for crystal volume fractions Φ > 0.15. The attainable shrinkage is reduced by up to 8% for Φ = 0.45. For the CABSGMC with Φ = 0.25, a reduction of Φ to 0.20 was evident due to partial α-Al2O3 dissolution. This effect was found able to increase the sintering temperature by ~5060 K.
The sintering of Low Temperature Co-fired Ceramics prepared from alumoborosilicate
glass- and Al2O3 powders of similar small particle size was studied by dilatometry, heating microscopy,
microstructure analysis, glass- and effective viscosity measurements. The steric effect of
Al3O3 inclusions was studied using a gnon-reactiveh model composite. With increasing Al3O3 volume
fraction (Φ ≤ 0.45), sintering decelerates and its final stage shifts to higher temperature. The
attainable shrinkage is reduced as Al2O3 particle clusters bearing residual pores become more frequent.
The kinetics of sintering could be described formally superposing the weighed contributions
of differentially sized and randomly composed glass-crystal particle clusters and assuming a sintering
rate controlled by the effective matrix viscosity, which increases with Φ and with progressive
wetting of Al2O3 particles during densification. The "reactive" model composite shows significant
dissolution of Al2O3 into the glass, which has two opposed effects on sintering: reducing Φ and increasing
glass viscosity. For the present case (Φ = 0.25), the latter effect dominates and sintering is
retarded by Al2O3 dissolution. Crystallization of wollastonite starts after full densification. Dissolution
of Al2O3 was found to promote the subsequent growth of anorthite.