Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (155)
- Vortrag (51)
- Beitrag zu einem Tagungsband (42)
- Beitrag zu einem Sammelband (31)
- Posterpräsentation (13)
- Buchkapitel (12)
Schlagworte
- Femtosecond laser (28)
- Laser-induced periodic surface structures (LIPSS) (25)
- Femtosecond laser ablation (24)
- Laser ablation (23)
- Laser processing (14)
- Radiation protection (12)
- Silicon (11)
- Laser cleaning (10)
- Ablation (9)
- Materialbearbeitung (9)
Organisationseinheit der BAM
- 6 Materialchemie (55)
- 6.2 Material- und Oberflächentechnologien (55)
- 9 Komponentensicherheit (4)
- 9.5 Tribologie und Verschleißschutz (4)
- 6.7 Materialsynthese und Design (3)
- 4 Material und Umwelt (2)
- 4.1 Biologische Materialschädigung und Referenzorganismen (2)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.2 Gefahrguttanks und Unfallmechanik (1)
- 5 Werkstofftechnik (1)
Paper des Monats
- ja (1)
Biofilm formation poses high risks in multiple industrial and medical settings. However, the robust nature of biofilms makes them also attractive for industrial applications where cell biocatalysts are increasingly in use. Since tailoring material properties that affect bacterial growth or its inhibition is gaining attention, here we focus on the effects of femtosecond laser produced nanostructures on bacterial adhesion. Large area periodic surface structures were generated on steel surfaces using 30-fs laser pulses at 790 nm wavelength. Two types of steel exhibiting a different corrosion resistance were used, i.e., a plain structural steel (corrodible) and a stainless steel (resistant to corrosion). Homogeneous fields of laser-induced periodic surface structures (LIPSS) were realized utilizing laser fluences close to the ablation threshold while scanning the sample under the focused laser beam in a multi-pulse regime. The nanostructures were characterized with optical and scanning electron microscopy. For each type of steel, more than ten identical samples were laser-processed. Subsequently, the samples were subjected to microbial adhesion tests. Bacteria of different shape and adhesion behavior (Escherichia coli and Staphylococcus aureus) were exposed to laser structures and to polished reference surfaces. Our results indicate that E. coli preferentially avoids adhesion to the LIPSS-covered areas, whereas S. aureus favors these areas for colonization.
Titanium and its alloys are known to allow the straightforward laser-based manufacturing of ordered surface nanostructures, so-called high spatial frequency laser-induced periodic surface structures (HSFL). These structures exhibit sub-100 nm spatial periods – far below the optical diffraction limit. The resulting surface functionalities are usually enabled by both, topographic and chemical alterations of the nanostructured surfaces. For exploring these effects, multi-method characterizations were performed here for HSFL processed on Ti–6Al–4V alloy upon irradiation with near-infrared ps-laser pulses (1030 nm, ≈1 ps pulse duration, 1–400 kHz) under different laser scan processing conditions, i.e., by systematically varying the pulse repetition frequency and the number of laser irradiation passes. The sample characterization involved morphological and topographical investigations by scanning electron microscopy (SEM), atomic force microscopy (AFM), tactile stylus profilometry, as well as near-surface chemical analyses hard X-ray photoelectron spectroscopy (HAXPES) and depth-profiling time-of-flight secondary ion mass spectrometry (ToF-SIMS). This provides a quantification of the laser ablation depth, the geometrical HSFL characteristics and enables new insights into the depth extent and the nature of the non-ablative laser-induced near-surface oxidation accompanying these nanostructures. This allows to answer the questions how the processing of HSFL can be industrially scaled up, and whether the latter is limited by heat-accumulation effects.
Micromachining experiments were performed with Ti:sapphire laser pulses (130 fs - 150 fs, 800 nm, approximately 10 Hz) in air. Employing the direct focusing technique, highly absorbing titanium nitride (TiN) and weakly absorbing polyimide (PI) and polymethylmethacrylate (PMMA) served as target materials. The lateral and vertical precision of the laser ablation and morphological features were characterized by scanning force (SFM), scanning electron (SEM) and optical microscopy. For TiN, incubation can be observed, i.e. the single-pulse surface damage threshold (0.26 J/cm2) is by a factor of two greater than the threshold for 100 pulses. Ablation rates below 10 nm per pulse can be achieved. The evolution of sub-wavelength ripples is presented in dependence on pulse number and laser fluence, respectively. The incubation behavior of the polymers can be described by an accumulation model as for TiN. Experiments on PI with varying focal lengths result in the same modification thresholds. Different polarization states of light (linear, circular) lead to a variation of the ablation rate and to various morphological patterns in the ablation craters (wavelength ripples, cones). Swelling of PMMA occurred at fluences below the ablation threshold.
Zusammenfassung
The surface chemical modification of polyurethane (PU) films was performed by an UV laser-induced chemical reaction in a polysaccharide solution. This process may be applicable as hydrophilic packaging of implantable medical devices and in vivo sensors. When a PU film in contact with an aqueous alginic acid (AAC) solution was irradiated with a XeCl laser, the PU film turned hydrophilic. Contact angles of water on the film were reduced from 110° to 60°. Since light absorption of the AAC solution at 308 nm was negligibly small, reactive sites were generated solely on the PU surface. There, AAC could be immobilized by chemical bonds thus allowing for a nanometer-scaled grafting of this biomolecule. The mechanism was investigated by surface analyses with Fourier-transform infrared spectroscopy (FT-IR), dye staining, ultraviolet-visible (UV-VIS) spectroscopy, and scanning electron microscopy (SEM) techniques. A one-photon photochemical process could beidentified.
Ablation of indium phosphide wafers in air was performed with 130 fs laser pulses at a wavelength of 800 nm at a low repetition rate of 10 Hz. In order to evaluate the role of the incubation effects, the relationship between the number of laser pulses used for the ablation and the threshold fluence was studied. Particular attention was paid to the chemical composition, surface morphology and structural variations of the ablated area.
Summary form only given. Machining investigations of crystalline silicon have been performed with laser pulses at a wavelength of 780 nm in the range between 5 fs and 400 fs. Applying 100 pulses per spot, surface damage thresholds were determined by the measurement of the damage diameter. In this pulse duration regime, the threshold fluences were nearly constant. Single-pulse investigations with 5 fs pulses yielded a value of about 0.15 J cm-2 identical to the multi-pulse experiment. This is in contradiction to the behaviour of dielectrics where incubation effects alter the optical properties down to the 5 fs pulse regime. Employing laser pulses with a duration of 130 fs at a wavelength of 800 nm, single-pulse ablation thresholds of 0.23 J cm-2 and 0.16 J cm-2 were determined for Si and InP in air, respectively. The threshold fluence was calculated from the linear relation between the square of the diameters versus the logarithm of the laser fluences.
Optical filters and fabrics are important parts of laser safety equipment such as goggles and curtains. A choice of these materials with varying absorption spectra is investigated with respect to their resistance to Ti:sapphire femtosecond laser radiation (800 nm wavelength, 1 kHz repetition rate). Pulse durations down to 30 fs and multiple-pulse irradiation conditions are employed to evaluate technically relevant damage thresholds. The ablation threshold fluences of the absorbing filters are comparable to those observed for transparent materials with 30-fs-pulses. These investigations together with scanning electron microscopy of the surface morphology after laser treatment provide insight into the interaction mechanism of the short pulses with the materials.
The removal and accelerated corrosion monitoring of metal coating systems is of general interest in materials science
and engineering technology. The femtosecond and nanosecond laser ablation and delamination at 800 nm and 532 nm,
respectively, of anodic oxide layers on aluminium alloys in electrolyte contact were investigated. Laser-induced
modifications of the oxide layer resulted in an ionic contact between electrolyte and metal, which produced a current
transient and thus allowed the in-situ electrochemical monitoring of the modification. Oxide coatings with different
optical properties, almost transparent and opaque, were examined. The transparent anodic oxides showed contrasting
ablation mechanisms in the nanosecond and femtosecond pulse duration regime: nanosecond pulses caused spallation,
whereas femtosecond treatment led to ablation. Current signals measured in the transparent film were consistent with
light absorption below the metal-oxide interface and with film spallation. Irradiation of the opaque coating yielded ionic
current transients within the so-called shock-affected-zone of the oxide layer. This investigation provided insight into the
role of the penetration depth of light and the heat-affected zone, the extent of the shock-affected zone, and the defect
formation in the coating and at the solid-solid interface between metal and oxide.