A three-phase transport model for high-temperature concrete simulations validated with X-ray CT data
(2021)
Concrete exposure to high temperatures induces thermo-hygral phenomena, causing water phase changes, buildup of pore pressure and vulnerability to spalling. In order to predict these phenomena under various conditions, a three-phase transport model is proposed. The model is validated on X-ray CT data up to 320 ◦C, showing good agreement of the temperature profiles and moisture changes. A dehydration description, traditionally derived from thermogravimetric analysis, was replaced by a formulation based on data from neutron radiography. In addition, treating porosity and dehydration evolution as independent processes, previous approaches do not fulfil the solid mass balance. As a consequence, a new formulation is proposed that introduces the porosity as an independent variable, ensuring the latter condition.
Numerical simulators, such as finite element models, have become increasingly capable of predicting the behaviour of structures and components owing to more sophisticated underlying mathematical models and advanced computing power. A common challenge lies, however, in calibrating these models in terms of their unknown/uncertain parameters. When measurements exist, this can be achieved by comparing the model response against measured data. Besides uncertain model parameters, phenomena like damage can give rise to further uncertainties; in particular, quasi-brittle materials, like concrete, experience damage in a heterogeneous manner due to various imperfections, e.g. in geometry and boundary conditions. This hardens an accurate prediction of the damaged behaviour of real structures that comprise such materials.
In this study, which draws from a data-driven approach, we use the force-version of the finite element model updating method (FEMU-F) to incorporate measured displacements into the identification of the damage parameters, in order to cope with heterogeneity. In this method, instead of conducting a forward evaluation of the model and comparing the model response (displacements) against the data, we impose displacements to the model and compare the resulting force residuals with measured reaction forces. To account for uncertainties in the measurement of displacements, we endow this approach with a penalty term, which reflects the discrepancy between measured and imposed displacements, where the latter is assumed as unknown random variables to be identified as well. A Variational Bayesian approach is used as an approximating tool for computing posterior parameters. The underlying damage model considered in this work is a gradient-enhanced damage model.
We first establish the identification procedure through two virtual examples, where synthetic data (displacements) are generated over a certain spatially-dense set of points over the domain. The procedure is then validated on an experimental case-study; namely a 3-point bending experiment with displacement measurements resulting from a digital image correlation (DIC) analysis.
Concrete is a complex material. Its properties evolve over time, especially at early age, and are dependent on environmental conditions, i.e. temperature and moisture conditions, as well as the composition of the material.
This leads to a variety of macroscopic phenomena such as hydration/solidification/hardening, creep and shrinkage, thermal strains, damage and inelastic deformations. Most of these phenomena are characterized by specific set of model assumptions and often an additive decomposition of strains into elastic, plastic, shrinkage and creep components is performed. Each of these phenomena are investigated separately and a number of respective independent models have been designed. The interactions are then accounted for by adding appropriate correction factors or additional models for the particular interaction. This paper discusses the importance of reconsider even in the experimental phase the model assumptions required to generalize the experimental data into models used in design codes. It is especially underlined that the complex macroscopic behaviour of concrete is strongly influenced by its multiscale and multiphyscis nature and two examples (shrinkage and fatigue) of interacting phenomena are discussed.
Concrete is a complex material. Its properties evolve over time, especially at early age, and are dependent on environmental conditions, i.e. temperature and moisture conditions, as well as the composition of the material.
This leads to a variety of macroscopic phenomena such as hydration/solidification/hardening, creep and shrinkage, thermal strains, damage and inelastic deformations. Most of these phenomena are characterized by specific set of model assumptions and often an additive decomposition of strains into elastic, plastic, shrinkage and creep components is performed. Each of these phenomena are investigated separately and a number of respective independent models have been designed. The interactions are then accounted for by adding appropriate correction factors or additional models for the particular interaction. This paper discusses the importance of reconsider even in the experimental phase the model assumptions required to generalize the experimental data into models used in design codes. It is especially underlined that the complex macroscopic behaviour of concrete is strongly influenced by its multiscale and multiphyscis nature and two examples (shrinkage and fatigue) of interacting phenomena are discussed.
The durability of concrete structures and its performance over the lifetime is strongly influenced by many interacting phenomena such as e.g. mechanical degradation due to fatigue loading, loss of prestress, degradation due to chemical reactions or creep and shrinkage. Failure due to cyclic loading is generally not instantaneous, but characterized by a steady damage accumulation.
Many constitutive models for concrete are currently available, which are applicable for specific loading regimes, different time scales and different resolution scales. A key limitation is that the models often do not address issues related to fatigue on a structural level. Very few models can be found in the literature that reproduce deterioration of concrete under repeated loading-unloading cycles.
The objective of this paper is the presentation of numerical methods for the simulation of concrete under fatigue loading using a temporal multiscale method.
First, a continuum damage model for concrete is developed with a focus on fatigue under compressive stresses. This includes the possibility to model stress redistributions and capture size effects. In contrast to cycle based approaches, where damage is accumulated based on the number of full stress cycles, a strain based approach is developed that can capture cyclic degradation under variable loading cycles including different amplitudes and loading frequencies. Second, a multiscale approach in time is presented to enable structural computations of fatigue failure with a reduced computational effort. The damage rate within the short time scale corresponding to a single cycle is computed based on a Fourier based approach. This evolution equation is then solved on the long time scale using different time integration schemes.
Lifetime aspects including fatigue failure of concrete structures were traditionally only of minor importance. Because of the growing interest in maxing out the capacities of concrete, its fatigue failure under compression has become an issue. A variety of interacting phenomena such as e.g. loss of prestress, degradation due to chemical reactions or creep and shrinkage influence the fatigue resistance. Failure due to cyclic loads is generally not instantaneous, but characterized by a steady damage accumulation. Therefore, a reliable numerical model to predict the performance of concrete over its lifetime is required, which accurately captures order effects and full three-dimensional stress states.
Many constitutive models for concrete are currently available, which are applicable for specific loading regimes, different time scales and different resolution scales.
However, a key limitation of those models is that they generally do not address issues related to fatigue on a structural level. Very few models can be found in the literature that reproduce deterioration of concrete under repeated loading-unloading cycles. This is due to the computational effort necessary to explicitly resolve every cycle which exceeds the currently available computational resources. The limitation can only be overcome by the application of multiscale methods in time.
The objective of the paper is the development of numerical methods for the simulation of concrete under fatigue loading using temporal multiscale methods.
First, a continuum damage model for concrete is developed with a focus on fatigue under compressive stresses [1]. This includes the possibility to model stress redistributions and capture size effects. In contrast to cycle based approaches, where damage is accumulated based on the number of full stress cycles, a strain based approach is developed that can capture cyclic degradation under variable loading cycles including different amplitudes and loading frequencies. The model is designed to represent failure under static loading as a particular case of fatigue failure after a single loading cycle. As a consequence, most of the material parameters can be deduced from static tests. Only a limit set of additional constitutive parameters is required to accurately describe the evolution under fatigue loading. Another advantage of the proposed model is the possibility to directly incorporate other multi-physics effects such as creep and shrinkage or thermal loading on the constitutive level.
Second, a multiscale approach in time is presented to enable structural computations of fatigue failure with a reduced computational effort. The damage rate within the short time scale corresponding to a single cycle is computed based on a Fourier based approach [2]. This evolution equation is then solved on the long time scale using different implicit and explicit time integration schemes. Their performance and some limitations for specific loading regimes is discussed.
Finally, the developed methods will be validated and compared to experimental data.
[1] Vitaliy Kindrachuk, Marc Thiele, Jörg F. Unger. Constitutive modeling of creep-fatigue interaction for normal strength concrete under compression, International Journal of Fatigue, 78:81-94, 2015
[2] Vitaliy Kindrachuk, Jörg F. Unger. A Fourier transformation-based temporal integration scheme for viscoplastic solids subjected to fatigue deterioration, International Journal of Fatigue, 100:215-228, 2017
Lifetime aspects including fatigue failure of concrete structures were traditionally only of minor importance. Because of the growing interest in maxing out the capacities of concrete, its fatigue failure under compression has become an issue. A variety of interacting phenomena such as e.g. loss of prestress, degradation due to chemical reactions or creep and shrinkage influence the fatigue resistance. Failure due to cyclic loads is generally not instantaneous, but characterized by a steady damage accumulation. Therefore, a reliable numerical model to predict the performance of concrete over its lifetime is required, which accurately captures order effects and full three-dimensional stress states.
Many constitutive models for concrete are currently available, which are applicable for specific loading regimes, different time scales and different resolution scales.
However, a key limitation of those models is that they generally do not address issues related to fatigue on a structural level. Very few models can be found in the literature that reproduce deterioration of concrete under repeated loading-unloading cycles. This is due to the computational effort necessary to explicitly resolve every cycle which exceeds the currently available computational resources. The limitation can only be overcome by the application of multiscale methods in time.
The objective of the paper is the development of numerical methods for the simulation of concrete under fatigue loading using temporal multiscale methods.
First, a continuum damage model for concrete is developed with a focus on fatigue under compressive stresses. This includes the possibility to model stress redistributions and capture size effects. In contrast to cycle based approaches, where damage is accumulated based on the number of full stress cycles, a strain based approach is developed that can capture cyclic degradation under variable loading cycles including different amplitudes and loading frequencies. The model is designed to represent failure under static loading as a particular case of fatigue failure after a single loading cycle. As a consequence, most of the material parameters can be deduced from static tests. Only a limit set of additional constitutive parameters is required to accurately describe the evolution under fatigue loading. Another advantage of the proposed model is the possibility to directly incorporate other multi-physics effects such as creep and shrinkage or thermal loading on the constitutive level.
Second, a multiscale approach in time is presented to enable structural computations of fatigue failure with a reduced computational effort. The damage rate within the short time scale corresponding to a single cycle is computed based on a Fourier based approach. This evolution equation is then solved on the long time scale using different implicit and explicit time integration schemes. Their performance and some limitations for specific loading regimes is discussed.
Finally, the developed methods will be validated and compared to experimental data.