Filtern
Dokumenttyp
- Zeitschriftenartikel (19)
- Vortrag (2)
- Beitrag zu einem Tagungsband (1)
Sprache
- Englisch (19)
- Deutsch (2)
- Mehrsprachig (1)
Schlagworte
- Tribofilm (6)
- Ball milling (3)
- Nanoparticles (3)
- TEM (3)
- Nanocomposite (2)
- Number density (2)
- Pin-on-disc test (2)
- STEM/TEM imaging (2)
- Volume fraction (2)
- (Mn,Ga) As crystallites (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (2)
Mn0.75Ga0.25As crystallites, partially embedded on and fully embedded within a single crystalline matrix of GaAs formed during metal organic vapor phase epitaxy (MOVPE) of Mn-rich (Mn,Ga)As on (001) oriented GaAs wafers. Phase and orientation analysis of these crystallites were performed with scanning nano beam electron diffraction (SNBED). The investigation of plan-view specimens using a liquid nitrogen cooling stage enabled the phase and orientation analysis of partially embedded ferromagnetic a-phase particles. In all specimens the following two orientation relationships (O) between the a-phase particles and the GaAs matrix were determined:
O1:
[1-2.0] Mn0.75Ga0.25As || [110] GaAs and
[10.2] Mn0.75Ga0.25As || [-110] GaAs
O2:
[10.2] Mn0.75Ga0.25As || [110] GaAs and
[1-2.0] Mn0.75Ga0.25As || [-110] GaAs.
The study of cross-sectional specimens enabled the analysis of fully embedded crystallites. It could be unambiguously detected that a fully embedded crystallite has the structure of the atomically ordered monoclinic β' phase. The β' phase crystallite consists of two domains which are related in twin positions to each other. The orientation relations of the different particles are illustrated by color coded stereographic projections.
Volume fraction determination of discretely oriented disc-shaped precipitates in transmission mode
(2017)
In der vorliegenden Arbeit wurde eine Formel zur Berechnung des Volumenantei ls dis kret orientierter scheibenförmiger Phasen für die Untersuchung im Transmissionsmodus hergeleitet, validiert und mit bereits veröffent lichen Formeln verglichen. Bei diesem Ver gleich konnte gezeigt werden,dass die in zahl reichen Veröffentlichungen benutzte Formel von E. E. Underwood für die Volumenanteils bestimmungbeidiskret orientierten Ausschei dungsphasen nicht benutzt werden sollte, da sie den Volumenanteil deutlich unterschätzt.
Die Ursache liegt in der von E.E. Underwood getroffenen Annahme, dass die kreisförmigen Scheiben regellos angeordnet und nicht aus gerichtet sind, was in Al-Legierungen in der Regel nicht der Fall ist.
The method of movable cellular automata (MCA) was applied to simulate the stress-strain behavior of a nano composite consisting of an epoxy matrix and 6 vol. % silica nano particles. The size of the elements used for modelling was fixed at 10 nm, corresponding approximately to the diameter of the filler particles. Since not only the stress-strain response of the two constituents but also debonding of neighboring particles and granular flow was taken into account, plastic deformation as well as crack initiation and propagation could be simulated with the model. Modelling results were compared with tensile test results of both, pure epoxy as well as the epoxy-6 vol. % SiO2 composite. Since assuming bulk properties of the two constituents did not yield satisfactory results, slight modifications of the nanoparticle response functions and nanostructures were tested numerically. Finally, it was observed that only the assumption of slightly increased strength properties of the epoxy yielded good correlation between experimental and modelling results. This was attributed to an increased cross linking of the epoxy caused by the presence of silica nano particles.
Excellent tribological properties of an advanced polymer matrix composite were obtained by a combination of micro- and nano-sized fillers. Surface features and the nanostructure of tribofilms were characterized by advanced microscopic techniques, and correlated with the macroscopic behavior in terms of wear rate and friction evolution. A model based on movable cellular automata was applied for obtaining a better understanding of the sliding behavior of the nanostructured tribofilms. The failure of the conventional composite without silica nanoparticles could be attributed to severe oxidational wear after degradation of an initially formed polymer transfer film. The hybrid composite preserves its antiwear and antifriction properties because flash temperatures at micron-sized carbon fibers, lead to polymer degradation and subsequent release of nanoparticles. It has been shown that the released particles are mixed with other wear products and form stable films at the disc surface thus preventing further severe oxidational wear. Furthermore, the released wear product also is embedding carbon fibers at the composite surface thus preventing fiber fragmentation and subsequent third body abrasion. With nanoscale modelling we were able to show that low friction and wear can be expected if the nanostructured silica films contain at least 10 vol.% of a soft ingredient.
A model system was used to simulate the properties of tribofilms which form during automotive braking. The model system was prepared by ball milling of a blend of 70 vol.% iron oxides, 15 vol.% molybdenum disulfide and 15 vol.% graphite. The resulting mixture was characterized by X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and various transmission electron microscopic (TEM) methods, including energy dispersive X-ray spectroscopy (EDXS), high resolution investigations (HRTEM) with corresponding simulation of the HRTEM images, diffraction methods such as scanning nano-beam electron diffraction (SNBED) and selected area electron diffraction (SAED). It could be shown that the ball milling caused a reduction of the grain size of the initial components to the nanometer range. Sometimes even amorphization or partial break-down of the crystal structure was observed for MoS2 and graphite. Moreover, chemical reactions lead to a formation of surface coverings of the nanoparticles by amorphous material, molybdenum oxides, and iron sulfates as derived from XPS.
Metal organic vapor phase epitaxy (MOVPE) of Mn-rich (Mn,Ga)As on (001) oriented GaAs wafers resulted in atomically ordered (Mn,Ga)As crystallites of two morphological kinds, partially embedded on the wafer surface and fully embedded within the single crystalline matrix. While the former were apparently free of defects (other than unavoidable point defects), the latter contained two domains separated by a grain boundary. Since atomic ordering can be modeled by space group symmetry descent considerations (Bärnighausen trees) that start with the space group of the known crystallographic phases of random (Mn,Ga)As alloys with specified chemical compositions, reasonable structure hypotheses have been derived for two atomically ordered Mn0.75Ga0.25As phases that we call the trigonal α' and the monoclinic β' phases. The implications of these structure hypotheses are in agreement with the results of a range of scanning transmission electron microscopy (STEM) and parallel illumination electron diffraction (ED) studies that include quantitative energy dispersive X-ray spectroscopy, X-ray spectroscopic imaging, as well nanobeam diffraction and high angle precession ED. The coexistence of two domains within the fully embedded crystallites is predicted by the corresponding Bärnighausen tree and observed experimentally for the fully embedded crystallites.
Formation and function mechanisms of nanostructured tribofilms of epoxy-based hybrid nanocomposites
(2015)
The nanostructures and properties of the tribofilms of epoxy (EP) composites filled with short carbon fibers (SCF) and different volume fractions of monodisperse silica nanoparticles were investigated. When the conventional composite filled only with SCF was considered under a high pv condition, an iron oxide layer is formed on the steel counterface. The addition of even only 0.05 vol% nano-silica leads to a significant change of the tribofilm's structure and the tribological behavior of the composite. With increasing silica content, the oxidation layer on the steel surface is gradually replaced by a silica-based tribofilm. A close relationship between the tribofilms structure and the tribological behavior of the composites was identified. Mixing, possible reactions and tribo-sintering of silica nanoparticles with other wear products are deemed to be main mechanisms inducing the formation and the lubricity of the silica-based tribofilm.
The primary crystallite size of titania powder relates to its properties in a number of applications. Transmission electron microscopy was used in this interlaboratory comparison (ILC) to measure primary crystallite size and shape distributions for a commercial aggregated titania powder. Data of four size descriptors and two shape descriptors were evaluated across nine laboratories. Data repeatability and reproducibility was evaluated by analysis of variance. One-third of the laboratory pairs had similar size descriptor data, but 83% of the pairs had similar aspect ratio data. Scale descriptor distributions were generally unimodal and were well-described by lognormal reference models. Shape descriptor distributions were multi-modal but data visualization plots demonstrated that the Weibull distribution was preferred to the normal distribution. For the equivalent circular diameter size descriptor, measurement uncertainties of the lognormal distribution scale and width parameters were 9.5% and 22%, respectively. For the aspect ratio shape descriptor, the measurement uncertainties of the Weibull distribution scale and width parameters were 7.0% and 26%, respectively. Both measurement uncertainty estimates and data visualizations should be used to analyze size and shape distributions of particles on the nanoscale.
The age hardening response of a high-purity Al–4Cu–1Li–0.25Mn alloy (wt. %) during isothermal aging without and with an applied external load was investigated. Plate shaped nanometer size T1 (Al2CuLi) and θ′ (Al2Cu) hardening phases were formed. The precipitates were analyzed with respect to the development of their structure, size, number density, volume fraction and associated transformation strains by conducting transmission electron microscopy (TEM) and scanning transmission electron microscopy (STEM) studies in combination with geometrical Phase analysis (GPA). Special attention was paid to the thickening of T1 phase. Two elementary types of single-layer T1 precipitate, one with a Li-rich (Type 1) and another with an Al-rich (Defect Type 1) central layer, were identified. The results show that the Defect Type 1 structure can act as a precursor for the Type 1 structure. The thickening of T1 precipitates occurs by alternative stacking of These two elementary structures. The thickening mechanism was analyzed based on the magnitude of strain associated with the precipitation transformation normal to its habit plane. Long-term aging and aging under load resulted in thicker and structurally defected T1 precipitates. Several types of defected precipitates were characterized and discussed. For θ′ precipitates, a ledge mechanism of
thickening was observed. Compared to the normal aging, an external load applied to the peak aged state leads to small variations in the average sizes and volume fractions of the precipitates.