Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (19)
Referierte Publikation
- ja (19) (entfernen)
Schlagworte
Organisationseinheit der BAM
- 4 Material und Umwelt (8)
- 4.1 Biologische Materialschädigung und Referenzorganismen (6)
- 4.0 Abteilungsleitung und andere (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.8 Umweltanalytik (1)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (1)
- 4.3 Schadstofftransfer und Umwelttechnologien (1)
Decay resistance of pine sapwood treated with titanium alkoxide solutions was tested against the brown-rot fungi Coniophora puteana and Poria placenta for exposure times of 10 and 16 wk. In practice, wood-specimens were vacuum-impregnated by alcoholic solutions of titanium alkoxide with concentrations in the range of 5–16 mass % (solid content in solution) and subsequently cured under different humidity conditions. Results reveal that treated wood degraded up to 5% in comparison to untreated one that deteriorated 38% and 50%, respectively against both wood-decay fungi. Even full protection (mass loss below 3%) was achieved against brown rot with titanium alkoxide solution containing solid content of around 5 mass% with a weight percentage gain (WPG) of 9 mass%. With increased concentration, fungal resistance decreased slightly which was associated with more cracks and imperfections formed in the deposited layers of titanium dioxide in the adjacent wood matrix. Thermal analysis verified that a considerable amount of precursor remained in the wood structure as un-hydrolyzed organic residues. These organics, being bioactive, had the tendency to induce similar fungicidal effects as those of conventional fungicides. The amount of organic residues is correlated with the decay resistance of the tested samples. In a prolonged decay test, mass losses of 16-wk incubated samples do not show behavior different from that of the wood samples incubated for 10 wk. This result implies that the decay protection is permanent and confirms further the fungicidal activity of titanium-alkoxide-treated wood.
Material performance testing of wood-plastic composites (WPC) requires adequate and time-efficient evaluation of the resistance against fungal colonisation and decay. This study investigates the effects of weathering on WPCs and subsequent material degradation by fungi. Weathering using UV radiation, water spray and repeated frost incidents caused micro- and macro-cracks. Fourier transform infrared spectroscopy (FTIR) demonstrated delignification of wood particles at the weathered WPC surface. Despite of increased surface area, accessibility for fungal hyphae and moisture content, weathering enhanced mass loss due to fungal decay only subtly but not significantly. These potentially enhancing effects for fungal decay are assumed to be outbalanced by delignification due to photo-oxidation and leaching of degradation products resulting in loss of nutrient sources essential for fungal growth.
The wood protection industry has refined their products from chrome-, copper-, and arsenate-based wood preservatives toward solely copper-based preservatives in combination with organic biocides. One of these is Cu-HDO, containing the chelation product of copper and N-cyclohexyldiazenium dioxide (HDO). In this study, the fate of isotope-labeled (13C) and nonlabeled (12C) Cu-HDO incorporated in wood sawdust mixed with soil was investigated. HDO concentration was monitored by high-pressure liquid chromatography. The total carbon and the δ13C content of respired CO2, as well as of the soil-wood-sawdust mixture, were determined with an elemental analyzer-isotopic ratio mass spectrometer. The concentration of HDO decreased significantly after 105 days of incubation, and after 24 days the 13CO2 concentration respired from soil increased steadily to a maximum after 64 days of incubation. Phospholipid fatty acid-stable isotope probing (PFA-SIP) analysis revealed that the dominant PFAs C19:0d8,9, C18:0, C18:1ω7, C18:2ω6,9, C17:1d7,8, C16:0, and C16:1ω7 were highly enriched in their δ13C content. Moreover, RNA-SIP identified members of the phylum Acidobacteria and the genera Phenylobacterium and Comamonas that were assimilating carbon from HDO exclusively. Cu-HDO as part of a wood preservative effectively decreased fungal wood decay and overall microbial respiration from soil. In turn, a defined bacterial community was stimulated that was able to metabolize HDO completely.
As the results of a 14 weeks outdoor exposure of a series of automotive coatings in South Florida, the panels were found to be overgrown with an almost closed layer of mildew. Pinholes remained as permanent surface damage after removing the mildew mycelium. The extent of the damage differed in dependence of the kind of the coating. By tracing the images and profiles of the coating surfaces systematically over all phases of weathering and the subsequent cleaning procedure, a connection between formation of pinholes and mildew growth could be found. Outdoor weathering tests in other regions of Florida as well as in Europe and Australia showed that pinholes caused by mildew attack could also be found in all other locations, but always to a lower extent than in South Florida. The standardised mildew tests EN ISO 846 and MIL-STD 810F for laboratory exposure failed to reproduce the formation of pinholes.
Flame retarded wood-plastic composites (WPCs) should allow safe application in areas of fire risk. Halogen-free flame retardants can contain high amounts of nitrogen, phosphorus or sulphur, which may serve as nutrition source for wood degrading fungi and accelerate wood decay. Therefore, the material resistance of WPCs with each of four flame retardants against both fire or fungal decay was examined in comparison to WPC without flame retardant. Expandable graphite showed the best performance against fire in cone calorimetry and radiant panel testing. Two ammonium polyphosphates and a third nitrogen-containing flame retardant were not as effective. Contrary to the possibility that flame retardants might enhance fungal decay of WPC, the opposite effect occurred in case of the wood-degrading fungi Trametes versicolor and Coniophora puteana according to determination of mass loss and decrease of bending modulus of elasticity. Only the surface mould Alternaria alternata slightly increased the degradation of WPCs with nitrogen-containing flame retardants compared to WPC without flame retardant according to mass loss data and FTIR-ATR analyses. Finally, WPC including expandable graphite as flame retardant was effective against both fire and fungal decay.
The antileaching efficacy of sol-gel-derived TiO2- and SiO2-based precursors has been evaluated through laboratory leaching trials with pine sapwood in two different ways. In a one-step process, wood was vacuum impregnated by the precursor solutions containing CuCl2. The copper (Cu) emission rates of the sol-gel-based impregnated woods were up to 70% lower than that of wood treated with pure CuCl2 solution at the same level of concentration. More improvement (80%) could be achieved in a two-step process, in which sol-gel precursors were introduced into an already CuCl2-treated wood. The refinement was attributed to several effects. In the one-step approach, Cu was embedded in the TiO2/SiO2 gels formed in the wood texture. During a two-step impregnation, gel layers that were formed in the wooden interior acted as an effective diffusion barrier. The sol-gel impregnations made wood more hydrophobic; therefore, the low amount of water that penetrated the cell wall was less efficient to leach out Cu.
Improved Durability of Wood Treated with Nano Metal Fluorides against Brown-Rot and White-Rot Fungi
(2022)
Low-water soluble metal fluorides such as magnesium fluoride (MgF2) and calcium Fluoride (CaF2) were evaluated for decay protection of wood. Initially, the biocidal efficacy of nano metal fluorides (NMFs) against wood destroying fungi was assessed with an in-vitro agar test. The results from the test showed that agar medium containing MgF2 and CaF2 was more efficient in preventing fungal decay than stand-alone MgF2 or CaF2. These metal fluorides, in their nanoscopic form synthesized using fluorolytic sol-gel synthesis, were introduced into the sapwood of Scots pine and beech wood and then subjected to accelerated ageing by leaching (EN 84). MAS 19F NMR and X-ray micro CT images showed that metal fluorides were present in treated wood, unleached and leached. Decay resistance of Scots pine and beech wood treated with NMFs was tested against Wood destroying fungi Rhodonia placenta and Trametes versicolor in accordance with EN 113. Results revealed that mass losses were reduced to below 3% in wood treated with the combination of MgF2 and CaF2.
It is concluded that NMFs provide full protection to wood even after it has been leached and can be used as wood preservatives in outdoor environments.
Materials that confer antimicrobial activity, be that by innate property, leaching of biocides or design features (e.g., non-adhesive materials) continue to gain popularity to combat the increasing and varied threats from microorganisms, e.g., replacing inert surfaces in hospitals with copper. To understand how efficacious these materials are at controlling microorganisms, data is usually collected via a standardised test method. However, standardised test methods vary, and often the characteristics and methodological choices can make it difficult to infer that any perceived antimicrobial activity demonstrated in the laboratory can be confidently assumed to an end-use setting. This review provides a critical analysis of standardised methodology used in academia and industry, and demonstrates how many key methodological choices (e.g., temperature, humidity/moisture, airflow, surface topography) may impact efficacy assessment, highlighting the need to carefully consider intended antimicrobial end-use of any product.
Numerous non-native tree species are given attention with respect to the reforestation of calamity areas in Europe. Among them, several species may form durable wood which can be used for outdoor applications, but differences in wood durability are expected between original and European growth sites. This study aimed at examining the biological durability against wooddestroying fungi and water permeability of German-grown Dawn redwood (Metasequoia glyptostroboides) and Port Orford cedar (Chamaecyparis lawsoniana). The heartwood of both wood species was assigned to durability class 4 (DC 4, less durable) in soil contact and DC 1–4 (very to less durable) against wood-destroying basidiomycetes. However, according to the Meyer-Veltrup model, their material resistance dose was notably higher compared to the reference species Norway spruce (Picea abies), and the resulting service life of above ground structures should be a multiple of the reference.