Decay resistance of pine sapwood treated with titanium alkoxide solutions was tested against the brown-rot fungi Coniophora puteana and Poria placenta for exposure times of 10 and 16 wk. In practice, wood-specimens were vacuum-impregnated by alcoholic solutions of titanium alkoxide with concentrations in the range of 5–16 mass % (solid content in solution) and subsequently cured under different humidity conditions. Results reveal that treated wood degraded up to 5% in comparison to untreated one that deteriorated 38% and 50%, respectively against both wood-decay fungi. Even full protection (mass loss below 3%) was achieved against brown rot with titanium alkoxide solution containing solid content of around 5 mass% with a weight percentage gain (WPG) of 9 mass%. With increased concentration, fungal resistance decreased slightly which was associated with more cracks and imperfections formed in the deposited layers of titanium dioxide in the adjacent wood matrix. Thermal analysis verified that a considerable amount of precursor remained in the wood structure as un-hydrolyzed organic residues. These organics, being bioactive, had the tendency to induce similar fungicidal effects as those of conventional fungicides. The amount of organic residues is correlated with the decay resistance of the tested samples. In a prolonged decay test, mass losses of 16-wk incubated samples do not show behavior different from that of the wood samples incubated for 10 wk. This result implies that the decay protection is permanent and confirms further the fungicidal activity of titanium-alkoxide-treated wood.
The metabolism of moulds results in the formation of various microbial volatile organic compounds (MVOCs). These substances can be used as an indicator for the presence of moulds in the indoor environment. Three different mould strains were cultivated on culture media and IMS spectra of gaseous mould metabolites were recorded using a portable mini system with a tritium source and a 5 cm drift cell. The headspace spectra are characteristic for mould species and their age. Typical gaseous components of the metabolites were identified and compared with results obtained from gas chromatography using a mass spectrometer detector. It was observed that the MVOCs formation depends on mould species and their growing stage with a maximum of MVOCs emission occurring during the first 10 days. These preliminary results show that IMS can be applied to detect MVOCs in indoor environment and indicate hidden mould growth.
The antileaching efficacy of sol-gel-derived TiO2- and SiO2-based precursors has been evaluated through laboratory leaching trials with pine sapwood in two different ways. In a one-step process, wood was vacuum impregnated by the precursor solutions containing CuCl2. The copper (Cu) emission rates of the sol-gel-based impregnated woods were up to 70% lower than that of wood treated with pure CuCl2 solution at the same level of concentration. More improvement (80%) could be achieved in a two-step process, in which sol-gel precursors were introduced into an already CuCl2-treated wood. The refinement was attributed to several effects. In the one-step approach, Cu was embedded in the TiO2/SiO2 gels formed in the wood texture. During a two-step impregnation, gel layers that were formed in the wooden interior acted as an effective diffusion barrier. The sol-gel impregnations made wood more hydrophobic; therefore, the low amount of water that penetrated the cell wall was less efficient to leach out Cu.
Improved Durability of Wood Treated with Nano Metal Fluorides against Brown-Rot and White-Rot Fungi
(2022)
Low-water soluble metal fluorides such as magnesium fluoride (MgF2) and calcium Fluoride (CaF2) were evaluated for decay protection of wood. Initially, the biocidal efficacy of nano metal fluorides (NMFs) against wood destroying fungi was assessed with an in-vitro agar test. The results from the test showed that agar medium containing MgF2 and CaF2 was more efficient in preventing fungal decay than stand-alone MgF2 or CaF2. These metal fluorides, in their nanoscopic form synthesized using fluorolytic sol-gel synthesis, were introduced into the sapwood of Scots pine and beech wood and then subjected to accelerated ageing by leaching (EN 84). MAS 19F NMR and X-ray micro CT images showed that metal fluorides were present in treated wood, unleached and leached. Decay resistance of Scots pine and beech wood treated with NMFs was tested against Wood destroying fungi Rhodonia placenta and Trametes versicolor in accordance with EN 113. Results revealed that mass losses were reduced to below 3% in wood treated with the combination of MgF2 and CaF2.
It is concluded that NMFs provide full protection to wood even after it has been leached and can be used as wood preservatives in outdoor environments.
During their growth on wood many fungi produce characteristic volatile organic compounds as secondary metabolites. These microbial volatile organic compounds (MVOCs) can be used as indicators of fungal growth even when such growth is concealed. In order to investigate the formation of these volatile metabolites on building materials, specimens of pine sapwood on agar media colonized by the dry-rot fungus Serpula lacrymans and a mixture of six moulds were examined. MVOCs from this fungal growth were studied over a period of up to half a year by ion mobility spectrometry (IMS) headspace analysis using a sensitive, portable IMS mini-device. The IMS headspace spectra from the growing fungal specimens obtained during this time span are differed from non-incubated wood specimens and indicate the presence of a mixture of MVOCs. The composition and amount of volatile metabolites of the fungi changed during cultivation. This was confirmed by a principal component analysis (PCA). Identification of different MVOCs in the headspace according to drift time and the mobility of ionized gaseous species in reference to GC-MS investigations were proposed. It was concluded that IMS can be used as a rapid and sensitive on-site method to indicate actively growing fungi concealed within wood.