Filtern
Erscheinungsjahr
Dokumenttyp
Sprache
- Englisch (53)
- Deutsch (11)
- Mehrsprachig (3)
Schlagworte
- TEM (10)
- Alumina (4)
- Transmission electron microscopy (4)
- Alumina coatings (3)
- Alumosol (3)
- Coatings (3)
- Corrosion protection (3)
- Nanoparticles (3)
- Oxidation (3)
- Sol-gel (3)
Organisationseinheit der BAM
- 5 Werkstofftechnik (7)
- 5.1 Mikrostruktur Design und Degradation (7)
- 5.6 Glas (3)
- 6 Materialchemie (3)
- 6.7 Materialsynthese und Design (3)
- 6.1 Oberflächen- und Dünnschichtanalyse (2)
- 6.3 Strukturanalytik (2)
- 9 Komponentensicherheit (2)
- 9.5 Tribologie und Verschleißschutz (2)
- 6.2 Material- und Oberflächentechnologien (1)
Future coal power plants will in case of oxyfuel combustion be operated with altered atmospheres. Hence, corrosion attack might become more severe and steels have to be protected. An alumina-sol was used to coat X20CrMoV12-1 (X20) with alumina to test the protection. Testing was performed at 600 °C in flowing H2O–CO2–O2 and static laboratory air for 1000 h. Oxidation under air is minor compared to exposure in oxyfuel atmosphere. In both cases a multilayered oxide (hematite, magnetite, spinel) was formed on uncoated steels. Carburization appeared on uncoated X20 in H2O–CO2–O2. The coating demonstrates a high protection.
Up to ~ 3 µm thick alumina coatings on corundum ceramic, sodalimesilica glass and Inconel718 were produced from mixtures of boehmite sols and corundum suspensions.
Transmission electron micrographs in combination with electron diffraction and energy dispersive X-ray spectroscopy served to identify crystallographic phases and to characterize the microstructure of the coatings. Using corundum ceramic as substrate the initially deposited boehmite transforms via transition aluminas to corundum while heating to 1200 °C. In the cases of glass and Inconel718 thermal treatments up to 520 °C and 1100 °C, respectively, cause diffusion of ions from the substrates into the coatings. Thus additional oxide phases were formed.
All coatings are free of cracks or delaminations and do not show any directed crystal growth.
Modified Yoldas sols can be used to prepare crack-free well adherent layers on different substrate materials such as sodalime glass, corundum and metal (IN-718). These layers having thicknesses of 0.6 µm are strain tolerant and withstand thermal cycling between 810 °C and room temperature. Introducing alpha-Al2O3 filler particles into modified Yoldas sols allows the preparation of thicker layers of 1.6 µm, which as well can be thermally cycled without noticeable delaminations. Chemical bonding seems to be the predominant layer bonding mechanism.
Alumina coatings with differing phase compositions were deposited on Inconel-718 (IN-718) Ni-base
superalloy substrates using solgel processing. Mass gain measurements served for studying the oxidation
behavior of coated metal surfaces if exposed to 800°C and 900°C for up to 4000 h in static air. Itwas found, that
alumina coatings significantly reduce the oxidation related mass gain of IN-718 even after heating to 900°C
for 4000 h. Transmission electron microscopy (TEM) studies revealed diffusion of elements from the metal
substrate (IN-718) into the alumina coatings and to a much lower degree from the coating into the
substrate. These diffusion processes are greatly influenced by the phase composition of the coatings, especially
by the presence of alpha-alumina.
Alumosols in combination with well dispersed corundum were successfully used to form up to 2.5 ìm thick coatings on the Ni-base alloy SC16. These coatings withstood heat treatments at 700 °C in a water vapour containing atmosphere. The heat treatment caused formation of delta-alumina in the coating and diffusion of chromium and titanium into the coating.
Weld metal microstructure for alloy 6060 aluminum welds, made using the gas-tungsten arc process and alloy 4043 filler metal, has been characterized using optical metallography, EPMA microprobe analysis, SEM/EBSD and STEM/EDX electron microscopy, and single-sensor differential thermal analysis (SS-DTA). In addition, alloy 6060 castings were solidified at variable cooling rates approaching that of welding, to provide a reference for comparison with weld microstructure. It was found that a major change in cast microstructure occurs at cooling rates higher than 27 K/s resulting in a structure similar to that observed in weld metal. Rapid cooling is believed to favor low temperature solidification reactions that normally would be achieved only at higher silicon content. Accordingly, additions of 4043 filler metal that increase the weld metal silicon content have only limited affect on weld solidification range and microstructure. This has direct implications regarding how 4043 filler additions improve weldability and weld quality.
Diffusion of Cr, Fe, and Ti ions from Ni-base alloy inconel-718 into a transition alumina coating
(2012)
Heat treating metals at high temperatures trigger diffusion processes which may lead to the formation of oxide layers. In this work the diffusion of Cr, Fe and Ti into an alumina coating applied to Inconel-718 is being investigated. Mass gain measurements, UV–vis spectroscopy and transmission electron microscopy were applied in order to study the evolution of the diffusion process. It was found that mainly Cr as well as minor amounts of Fe and Ti are being incorporated into the alumina coating upon prolonged heat treatment at 700 °C. It could be shown that alumina coatings being void of Cr have the same oxidation related mass gain as uncoated samples. However, incorporation of Cr into the alumina coating decreased their mass gain below that of uncoated substrates forming a Cr oxide scale only.